钢板表面纵向裂纹的金相检验和分析
METALLOGRAPHICAL EXAMINATION AND ANALYSIS OF LONGITUDINAL CRACK ON STEEL PLATE
摘 要
在连铸轧制的钢板表面有沿轧制方向的裂纹。采用化学成分分析，宏、微观检验等方法对裂纹进行了分析。结果表明,裂纹中存在氧化物及其脱碳等缺陷，这说明连铸坯表面在轧制前已存在裂纹并在轧前加热中裂纹内发生氧化和脱碳，导致轧制后的钢板表面出现裂纹。
金相检验
连铸板坯
The longitudinal surface carcks
Metallographical examination
Continuous casting slab
Abstract
There are some longitudinal surface cracks appear on the continuous casting slab and consequently on the rolling steel plate. By means of the chemical composition analysis, macro-scopic observation and microstructure examination, the results showed that there is oxide in the crack, and the decarburizing and the pit-oxide are exsited in the continuous casting and rolling process. All these factors caused the longitudinal surface cracks appeared on the steel plate after rolling.
中图分类号 TG335.5
所属栏目
基金项目
收稿日期 2006/3/14
修改稿日期
网络出版日期
作者单位点击查看
备注许庆太(1937-)，男，教授级高级工程师。
引用该论文: XU Qing-tai,WEI Bo,ZHAO Xiao-fei,SUN Wei. METALLOGRAPHICAL EXAMINATION AND ANALYSIS OF LONGITUDINAL CRACK ON STEEL PLATE[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(12): 634～636
许庆太,魏伯,赵晓飞,孙伟. 钢板表面纵向裂纹的金相检验和分析[J]. 理化检验－物理分册, 2006, 42(12): 634～636
被引情况:
【1】靳芳芳,刘守显,李朝辉,孙胜英, "高层建筑用Q345GJC钢板表面裂纹成因分析",理化检验－物理分册 46, 515-517(2010)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王广生编著.金属热处理缺陷分析及案例[M].北京:机械工业出版社, 2000,6:150-154.
【2】程饴萱.钢的相变显微组织[M].杭州:浙江大学出版社, 1989.206-210.
【3】杜 萍.板坯表面纵裂纹的原因分析及采取的措施[J].天津冶金, 2003,(3):27-29.
【4】蔡开科.连续铸钢愿理与工艺[M].北京:冶金工业出版社, 1994,12:310-320.
【5】李建科.板坯表面纵裂纹的成因与控制[J].连铸, 2005,(1):37-38.
【2】程饴萱.钢的相变显微组织[M].杭州:浙江大学出版社, 1989.206-210.
【3】杜 萍.板坯表面纵裂纹的原因分析及采取的措施[J].天津冶金, 2003,(3):27-29.
【4】蔡开科.连续铸钢愿理与工艺[M].北京:冶金工业出版社, 1994,12:310-320.
【5】李建科.板坯表面纵裂纹的成因与控制[J].连铸, 2005,(1):37-38.
相关信息