光电直读光谱法测定高温合金K18中的主量和杂质元素
Determination of Major and Impurity Elements in K18 Super Alloy by Photoelectric Direct-Reading Atomic Emission Spectrometry
摘 要
采用光电直读光谱法测定高温合金K18中主量和杂质元素。样品经过磨床的预处理,使得表面平整光滑,激发试样的边缘进行测定。采用一套内控标准样品建立了校准曲线,在此基础上采用控制试样法进行漂移校正。此方法的测定结果与电感耦合等离子体原子发射光谱法和高频感应加热-红外线吸收法的结果相吻合,测定值的相对标准偏差(n=11)在7.6%之内。
主量元素
杂质
高温合金K18
Photoelectric direct-reading atomic emission spectrometry
Major elements
Impurity
K18 super alloy
Abstract
Photoelectric direct-reading atomic emission spectrometry was applied to the determination of major and impurity elements in K18 super alloy. The sample was pretreated by a grinder to give a smooth surface. The edge of the sample was excited for the determination. Standard curves were established with a set of internal control standards. Drift correction was made by using the control sample method. The results obtained by the proposed method were in consistent with those obtained by ICP-AES and high-frequency induction heating-infrared absorption method and RSDs (n=11) were within 7.6%.
中图分类号 O657.31 DOI 10.11973/lhjy-hx201510004
所属栏目 试验与研究
基金项目
收稿日期 2014/9/14
修改稿日期
网络出版日期
作者单位点击查看
备注高颂(1978-),女,河南平顶山人,高级工程师,硕士,研究方向为航空用金属材料化学成分的检测。
引用该论文: GAO Song,PANG Xiao-hui,LIU Xi-shan,ZHAO Hai-yu,ZHANG Yan. Determination of Major and Impurity Elements in K18 Super Alloy by Photoelectric Direct-Reading Atomic Emission Spectrometry[J]. Physical Testing and Chemical Analysis part B:Chemical Analysis, 2015, 51(10): 1369～1372
高颂,庞晓辉,刘喜山,赵海燏,张艳. 光电直读光谱法测定高温合金K18中的主量和杂质元素[J]. 理化检验－化学分册, 2015, 51(10): 1369～1372
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李汉康,黄乾尧.高温合金［M］.北京:冶金工业出版研究和发展, 2000.
【2】师昌绪,仲增墉.我国高温合金的发展与创新［J］.金属学报, 2010,46(11):1281-1288.
【3】刘丽荣,金涛,孙晓峰,等.钛含量对一种镍基单晶高温合金长期时效后的组织影响［J］.材料工程, 2006(9):14-19.
【4】余竹,刘林,赵新宝,等.碳在镍基单晶高温合金中作用研究的进展［J］.铸造, 2009,58(9):918-924.
【5】ZHOU Peng-jie, YU Jin-jian, SUN Xiao-fen, et al. Roles of Zr and Y in cast microstructure of M951 nickel-based superalloy［J］.Rare Metal Letters, 2010,39(9):1541-1544.
【6】郑亮,谷臣清,张国庆.钽对低铬高钨铸造镍基高温合金显微组织的影响［J］.稀有金属材料与工程, 2005,34(2):191-198.
【7】管秀荣,魏健,刘恩泽,等.钛含量对镍基高温合金抗热腐蚀性能的影响［J］.稀有金属材料与工程, 2012,41(11):1990-1994.
【8】徐岩,郭守仁,卢德忠,等.微量元素B对铸造高温合金组织和性能的影响［J］.材料工程, 2001(增):14-18.
【9】马冲先,陈忠颖,芮琦.镍基高温合金中痕量元素分析方法研究的最新进展［J］.理化检验-化学分册, 2013,49(12):1522-1531.
【10】HB 5220-2008高温合金化学方法［S］.
【11】ASTM E 2594-09电感耦合等离子体法测定镍基合金含量分析方法［S］.
【12】张桂竹,李国华.电感耦合等离子体原子发射光谱法测定高温合金和耐热不锈钢中铌时钒、钛、铬的光谱干扰及校正［J］.冶金分析, 2013,3(8):43-48.
【13】童坚.ICP-OES法测定高温合金中的多种化学成分［J］.分析试验室, 2001,20(3):20-22.
【14】HB 5404-2005高温合金痕量元素分析方法［S］.
【15】蒋启翠.高频燃烧-红外吸收法测定钢铁中微量碳硫［J］.分析试验室, 2005,25(4):95-96.
【2】师昌绪,仲增墉.我国高温合金的发展与创新［J］.金属学报, 2010,46(11):1281-1288.
【3】刘丽荣,金涛,孙晓峰,等.钛含量对一种镍基单晶高温合金长期时效后的组织影响［J］.材料工程, 2006(9):14-19.
【4】余竹,刘林,赵新宝,等.碳在镍基单晶高温合金中作用研究的进展［J］.铸造, 2009,58(9):918-924.
【5】ZHOU Peng-jie, YU Jin-jian, SUN Xiao-fen, et al. Roles of Zr and Y in cast microstructure of M951 nickel-based superalloy［J］.Rare Metal Letters, 2010,39(9):1541-1544.
【6】郑亮,谷臣清,张国庆.钽对低铬高钨铸造镍基高温合金显微组织的影响［J］.稀有金属材料与工程, 2005,34(2):191-198.
【7】管秀荣,魏健,刘恩泽,等.钛含量对镍基高温合金抗热腐蚀性能的影响［J］.稀有金属材料与工程, 2012,41(11):1990-1994.
【8】徐岩,郭守仁,卢德忠,等.微量元素B对铸造高温合金组织和性能的影响［J］.材料工程, 2001(增):14-18.
【9】马冲先,陈忠颖,芮琦.镍基高温合金中痕量元素分析方法研究的最新进展［J］.理化检验-化学分册, 2013,49(12):1522-1531.
【10】HB 5220-2008高温合金化学方法［S］.
【11】ASTM E 2594-09电感耦合等离子体法测定镍基合金含量分析方法［S］.
【12】张桂竹,李国华.电感耦合等离子体原子发射光谱法测定高温合金和耐热不锈钢中铌时钒、钛、铬的光谱干扰及校正［J］.冶金分析, 2013,3(8):43-48.
【13】童坚.ICP-OES法测定高温合金中的多种化学成分［J］.分析试验室, 2001,20(3):20-22.
【14】HB 5404-2005高温合金痕量元素分析方法［S］.
【15】蒋启翠.高频燃烧-红外吸收法测定钢铁中微量碳硫［J］.分析试验室, 2005,25(4):95-96.
相关信息