18-8奥氏体不锈钢焊接接头晶间腐蚀的评定及控制

EVALUATION AND CONTROL OF THE AUSTENITIC 18-8 STAINLESS STEEL WELDED JOINT INTERGRANULAR CORROSION

林晓云

摘要

介绍了18-8奥氏体不锈钢焊接件焊接接头抗晶间腐蚀能力的检验和评定方法,对焊接接头晶间腐蚀的原因进行了分析,阐述了在焊接过程中的主要方面实施的有效控制方法,以提高不锈钢焊件抗晶间腐蚀的能力。

标签奥氏体不锈钢

焊接接头

晶间腐蚀

焊接

控制

Austenitic stainless steel

Welded joint

Intergranular corrosion

Weld

Control

Abstract

The examination and evaluation methods for property of the 18-8 Austenitic stainless steel welded joint resistant to intergranular corrosion were introduced. Reason caused welded joint intergranular corrosion was analyzed. The control process for welding to improve the quality of stainless steel intergranular corrosion resistant was proposed.

中图分类号 TG142.71

所属栏目试验技术与方法

基金项目

收稿日期 2006/11/3

修改稿日期

网络出版日期

作者单位点击查看

备注林晓云(1961-),女,工程师。

引用该论文: LIN Xiao-yun. EVALUATION AND CONTROL OF THE AUSTENITIC 18-8 STAINLESS STEEL WELDED JOINT INTERGRANULAR CORROSION[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(5): 236～238
林晓云. 18-8奥氏体不锈钢焊接接头晶间腐蚀的评定及控制[J]. 理化检验－物理分册, 2007, 43(5): 236～238

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

相关信息

	标题	相关频次
	热处理对复合板焊接接头中316L不锈钢焊缝组织及耐蚀性的影响	6
	304奥氏体不锈钢管焊接接头开裂原因	4
	304奥氏体不锈钢护栏断裂失效分析	4
	Incoloy825合金TIG和PAW焊接接头耐晶间腐蚀性能的对比	4
	TP304H奥氏体锅炉管高温运行显微特征	4
	奥氏体不锈钢小径管焊接接头的相控阵超声检测	4
	不锈钢热轧板材焊接接头的晶间腐蚀试验	4
	超薄层0Cr18Ni9/20g复合钢板的焊接工艺及接头组织	4
	304奥氏体不锈钢焊缝低温热老化后的显微组织与力学性能	3
	LF2铝合金燃油导管接头焊缝开裂原因及改进	3
	WP304WX管道泄漏原因分析	3
	奥氏体不锈钢管道环焊缝的超声相控阵检测	3
	高温过热器TP347H钢管焊接接头开裂原因	3
	铬镍奥氏体不锈钢焊缝铁素体含量的测定	3
	焊接工艺对奥氏体不锈钢焊接接头应变强化性能的影响	3
	厚壁焊缝阵列超声SH波检测的成像方法	3
	在役压力容器焊接裂纹的成因分析及预防措施	3
	06Cr17Ni5N奥氏体不锈钢热轧板表面脱皮原因	2
	0Cr18Ni9钢表面等离子铌合金化层的显微组织和摩擦磨损性能	2
	10Ni5CrMoV钢MAG焊接接头的显微组织与力学性能	2
	12Cr2Mo1R钢焊条电弧焊焊接接头的性能	2
	14NiCrMo10 6V与Q345E钢过渡匹配焊接接头的组织与力学性能	2
	17MnNiVNbR钢焊接接头的性能	2
	1Cr18Ni9Ti不锈钢管焊接接头断裂原因分析	2
	1Cr18Ni9Ti不锈钢脉冲超窄间隙焊接头的组织及耐腐蚀性能	2
	2197铝锂合金在不同热处理状态下的晶间腐蚀及剥蚀行为	2
	2219高强铝合金焊接接头的腐蚀性能	2
	3003铝合金薄板超高转速搅拌摩擦焊接头的组织与性能	2
	304H不锈钢板焊接接头的性能	2
	304L/ER316L奥氏体不锈钢焊接板的点蚀行为	2