X射线衍射谱分析软件CSM的功能扩展
IMPROVEMENT OF THE SOFTWARE OF CRYSTALLOGRAPHICA SEARCH-MATCH
摘 要
针对粉末X射线衍射谱分析软件CSM的特点和存在的缺陷,提出一种简单的算法,利用CSM软件附带的用户程序库功能,实现了固溶体的物相分析和固溶度的定量计算,扩展了软件的使用范围,提高了软件用于物相分析的准确程度。
软件
物相分析
X-ray diffraction
Software
Phase analysis
Abstract
A simple arithmetic was put forward in allusion to the characteristic and bug of the CSM software. The phase analysis and quantitative calculating of solid solution were completed with the user database of CSM. So the capabilities of CSM were extended. And the accuracy of phase analysis was promoted.
中图分类号 O722
所属栏目 试验技术与方法
基金项目
收稿日期 2006/10/25
修改稿日期
网络出版日期
作者单位点击查看
备注殷士龙(1947-),男,教授。
引用该论文: YIN Shi-long,ZHU Chun-xiang,BIAN Qing,WANG Xiao. IMPROVEMENT OF THE SOFTWARE OF CRYSTALLOGRAPHICA SEARCH-MATCH[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(9): 455～457
殷士龙,朱春祥,卞 清,王 晓. X射线衍射谱分析软件CSM的功能扩展[J]. 理化检验－物理分册, 2007, 43(9): 455～457
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】麦振洪.晶体X射线衍射的发现及其深远影响［J］.现代物理知识,2003,15(5):53-55．
【2】吴小山,张 维,林 涛.掠入射X射线散射方法与应用［J］.常熟理工学院学报,2006,20(2):14-22．
【3】何元金,马兴坤.近代物理试验［M］.北京:清华大学出版社,2003:138-157．
【4】马礼敦.近代X射线多晶体衍射［M］.北京:化学工业出版社,2004:4-6．
【5】Srinivas V,Barua P,Murty B S. On icosahedral phase formation in mechanically alloyed Al70Cu20Fe10［J］. Materials Science and Engineering,2000,A294-296:65-67．
【6】Barua P,Srinivas V,Murty B S. Synthesis of quasicrystalline phase by mechanical alloying of Al70Cu20Fe10［J］. Philosophical Magazine A,2000,80(5):1207-1217．
【7】Barur P,Murty B S,Srinivas V. Mechanical alloying of Al-Cu-Fe elemental powders［J］. Materials Science and Engineering,2001,A304-306:863-866．
【2】吴小山,张 维,林 涛.掠入射X射线散射方法与应用［J］.常熟理工学院学报,2006,20(2):14-22．
【3】何元金,马兴坤.近代物理试验［M］.北京:清华大学出版社,2003:138-157．
【4】马礼敦.近代X射线多晶体衍射［M］.北京:化学工业出版社,2004:4-6．
【5】Srinivas V,Barua P,Murty B S. On icosahedral phase formation in mechanically alloyed Al70Cu20Fe10［J］. Materials Science and Engineering,2000,A294-296:65-67．
【6】Barua P,Srinivas V,Murty B S. Synthesis of quasicrystalline phase by mechanical alloying of Al70Cu20Fe10［J］. Philosophical Magazine A,2000,80(5):1207-1217．
【7】Barur P,Murty B S,Srinivas V. Mechanical alloying of Al-Cu-Fe elemental powders［J］. Materials Science and Engineering,2001,A304-306:863-866．
相关信息