60Mn钢环件断裂原因分析
FRACTURE ANALYSIS OF 60Mn STEEL RING
摘 要
60Mn钢环件装配后,在静置状态下突然发生断裂。采用断口分析、化学成分分析和显微组织检验等方法对断裂件进行了分析。结果表明,环件中存在白点。该白点在装配应力和内部氢压的作用下发生滞后扩展而发生崩裂。
白点
氢致滞后扩展
断口分析
Steel ring
Flake
Hydrogen-induced delayed cracking
Fracture analysis
Abstract
The 60Mn steel ring burst broken in static after assembled. The fracture was analyzed through fracture surface,composition and microstructure. The results showed that there were flakes in the ring and the hydrogen-induced delayed cracking was induced under the hydrogen pressure and the assemble stress. When the flake grew to a critical size to result in burst fracture.
中图分类号 TG142.21
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/3/7
修改稿日期
网络出版日期
作者单位点击查看
备注陈 刚(1973-),男,工程师。
引用该论文: CHEN Gang,REN Xue-chong. FRACTURE ANALYSIS OF 60Mn STEEL RING[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(4): 206～208
陈 刚,任学冲. 60Mn钢环件断裂原因分析[J]. 理化检验－物理分册, 2008, 44(4): 206～208
被引情况:
【1】郭立波,李朋,高延庆, "钢中白点的微观形貌及其与夹杂物和偏析的关系",理化检验－物理分册 52, 768-771(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】褚武扬.氢损伤和滞后断裂［M］.北京:冶金工业出版社,1988．
【2】任学冲,褚武扬,李金许,等.车轮钢中的白点及其断口研究［J］.金属学报,2006,42(3):273-279．
【3】陈 廉,刘民治,张维斗,等.气瓶钢中白点焊合的研究［J］.金属学报,1979,15(4):446-455．
【4】任学冲,褚武扬,李金许,等.原子氢和白点对车轮钢力学性能的影响［J］.金属学报,2006,42(2):153-157．
【5】武 明,褚武扬,李金许,等.应力和夹杂对车轮钢中氢鼓泡的影响［J］.金属学报,2006,42(8):815-819．
【2】任学冲,褚武扬,李金许,等.车轮钢中的白点及其断口研究［J］.金属学报,2006,42(3):273-279．
【3】陈 廉,刘民治,张维斗,等.气瓶钢中白点焊合的研究［J］.金属学报,1979,15(4):446-455．
【4】任学冲,褚武扬,李金许,等.原子氢和白点对车轮钢力学性能的影响［J］.金属学报,2006,42(2):153-157．
【5】武 明,褚武扬,李金许,等.应力和夹杂对车轮钢中氢鼓泡的影响［J］.金属学报,2006,42(8):815-819．
相关信息