MICROSTRUCTURE AND MECHANICAL PROPERTIES OF FRICTION STIR WELDING JOINT OF DISSIMILAR Al-ALLOYS
摘 要
采用搅拌摩擦焊方法对4 mm厚的5083铝合金与6082铝合金进行了焊接,对焊接接头的微观组织和力学性能进行了分析。结果表明,焊核区由细小的等轴再结晶组织构成,6082铝合金在前进侧的抗拉强度大于5083铝合金在前进侧的抗拉强度,正弯试验与背弯试验角度都达到180°。
Abstract
Dissimilar 5083-6082 Al-Alloys in 4 mm thickness were successfully friction stir welded. The metallographic observation demonstrates that the dynamic recrystallization occurred in the weld nugget,which consists of refined equiaxed grains. Mechanical tests demonstrate that the joint in which 6082 Al-Alloy was located on advancing side shows a higher tensile strength than that of 5083 Al-Alloy on advancing side;the angles upon face and root bend tests attains to 180°.
中图分类号 TG453.9
所属栏目 试验与研究
基金项目
收稿日期 2007/6/28
修改稿日期
网络出版日期
作者单位点击查看
备注常学斌(1979-),男,硕士研究生。
引用该论文: CHANG Xue-bin,GE Ji-ping,LIU Shu-hua,DONG Chun-lin. MICROSTRUCTURE AND MECHANICAL PROPERTIES OF FRICTION STIR WELDING JOINT OF DISSIMILAR Al-ALLOYS[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(6): 281~282
常学斌,葛继平,刘书华,董春林. 异种铝合金搅拌摩擦焊接接头的微观组织与力学性能[J]. 理化检验-物理分册, 2008, 44(6): 281~282
被引情况:
【1】田莉莉,常学斌,周英杰,于正洋, "5083铝合金搅拌摩擦焊接头的显微组织与力学性能",理化检验-物理分册 49, 225-228(2013)
【2】田莉莉,常学斌,周英杰,杨坚,贺晔红, "6082-T6铝合金搅拌摩擦焊接头的显微组织与力学性能",理化检验-物理分册 48, 23-25(2012)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Thomas W M,Nicholas J C,Dawes C J,et al. Friction Stir Butt Welding: England,No. PCTPGB92P02203 and No. 9125978. 8[P]. 1991-12-06.
【2】Colegrove P A,Shercliff H R. Experimental and numerical analysis of aluminium alloy 7075-T7351 friction stir welds[J]. Science and Technology of Welding and Joining,2003,8(5):360-370.
【3】王文峰,童彦刚,王纯祥.一种新型焊接工艺——搅拌摩擦焊[J].电焊机,2004(1):15-18.
【4】栾国红,胡煌辉,柴 鹏.搅拌摩擦焊——新型列车制造新技术[J].电力机车及城市车辆,2006,29(4):40-43.
【2】Colegrove P A,Shercliff H R. Experimental and numerical analysis of aluminium alloy 7075-T7351 friction stir welds[J]. Science and Technology of Welding and Joining,2003,8(5):360-370.
【3】王文峰,童彦刚,王纯祥.一种新型焊接工艺——搅拌摩擦焊[J].电焊机,2004(1):15-18.
【4】栾国红,胡煌辉,柴 鹏.搅拌摩擦焊——新型列车制造新技术[J].电力机车及城市车辆,2006,29(4):40-43.
相关信息