FRACTURE ANALYSIS OF A BOLT IN LAYING HEAD
摘 要
采用化学成分分析、宏观和微观检验、金相组织分析和力学性能测定等方法分析了吐丝机用高强度螺栓发生断裂的原因。结果表明,由于机加工不当而在螺纹根部产生表面缺陷,并且这些表面缺陷周围在随后的热处理过程中发生全脱碳,大大降低了螺栓的疲劳强度,导致螺栓在使用过程中早期疲劳断裂。
Abstract
Fracture analysis of a high-strength bolt in laying head is conducted by a variety of means. The results show that a fragile fatigue fracture happened in the bolt. Surface defects in the bottom of screw threads induce a very high degree of stress concentration due to improper mechanical processing,and full-decarbonization around the defects during the following heat treatment reduces fatigue strength of the bolt greatly,thus resulting in the early fracture of the bolt.
中图分类号 TG142.41
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/7/27
修改稿日期
网络出版日期
作者单位点击查看
备注严春莲(1980-),女,工程师,硕士。
引用该论文: YAN Chun-lian,WEN Juan,LIU Xiao-lan,LIU Wei-ping,REN Qun. FRACTURE ANALYSIS OF A BOLT IN LAYING HEAD[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(6): 316~318
严春莲,温 娟,刘晓岚,刘卫平,任 群. 吐丝机螺栓断裂的失效分析[J]. 理化检验-物理分册, 2008, 44(6): 316~318
被引情况:
【1】王卫泽,梁佳春,王博,轩福贞, "烟机静叶固定螺栓的失效分析",机械工程材料 34, 84-86(2010)
【2】王兆希,郭宏梅,张小亮,於旻, "电站稳压器支承裙座锚固螺栓断裂失效分析",理化检验-物理分册 51, 747-750(2015)
【3】张彦文,陈雪艳,张友登,陈宇,陶勇, "变电站阻波器吊环断裂原因分析",理化检验-物理分册 48, 759-761(2012)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB/T 3098.1-2000 紧固件机械性能——螺栓、螺钉和螺柱[S].
【2】GB/T 5779.3-2000 紧固件表面缺陷——螺栓、螺钉和螺柱 一般要求[S].
【3】孙 智,江 利,应鹏展.失效分析:基础与应用[M].北京:机械工业出版社,2005:224-225.
【2】GB/T 5779.3-2000 紧固件表面缺陷——螺栓、螺钉和螺柱 一般要求[S].
【3】孙 智,江 利,应鹏展.失效分析:基础与应用[M].北京:机械工业出版社,2005:224-225.
相关信息