B7螺杆上的螺纹剥落原因分析
THREAD STRIPPING ANALYSIS ON B7 STUD
摘 要
应用光学显微镜、洛氏硬度计、显微硬度仪和光电直读光谱仪,对表面开裂并严重剥落的B7螺杆及同批经退火、拉拔后原材料的金相组织、洛氏硬度、显微硬度和化学成分进行了分析。结果表明,原材料中存在的夹杂物及带状偏析是引起螺杆纵向开裂的主要原因;原材料退火时引起表面脱碳,使螺杆在进行中频感应淬火时出现了层裂纹,最终因螺杆表面严重剥落而失效。
裂纹
剥落
带状偏析
夹杂物
脱碳
B7 stud
crack
stripping
banded segregation
inclusion
decarburization
Abstract
The microstructure,micro-penetration hardness and chemical composition of B7 stud which thread stripped and the same lot number raw material after drawing and tempering were analyzed by means of light microscope,rockwell apparatus,HX-100 micro-hardness tester and Baird DV-6 optical emission spectrometer. The result showed that some microstructure defects in raw material such as banded segregation and inclusion result in the B7 stud longitudinal cracking;the surface decarburization of the raw material made hypo-crack taken place,even the thread stripped.
中图分类号 TG142.41
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/6/28
修改稿日期
网络出版日期
作者单位点击查看
备注张青春(1974-),女,工程师。
引用该论文: ZHANG Qing-chun,ZHAO Hai-li,CHEN Qi-feng,WANG Ji-liang,JIANG Zhao-xi. THREAD STRIPPING ANALYSIS ON B7 STUD[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(9): 521～523
张青春,赵海丽,陈琦峰,王继良,姜招喜. B7螺杆上的螺纹剥落原因分析[J]. 理化检验－物理分册, 2008, 44(9): 521～523
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】祝国华,战祥丽. 零件热处理裂纹的分析与对策[J]. 机械工人(热加工),2004(8)：75．
【2】柳得橹,邵伟然.钢的表面带状组织及其引起的冷弯裂纹[J]. 北京科技大学学报,2005,27(1)：40-44．
【3】张 丽. 热处理缺陷裂纹产生原因的分析[J]. 装备制造技术,2006(4)：25．
【4】郑香增,夏佃秀. 34～50 mm厚钢板的研制开发[J]. 山东冶金,2006,28(1): 11-13．
【5】付秀琴,张 斌,张 弘. C62AT货车车轮崩裂分析[J]. 理化检验-物理分册,2006,42(9): 476-478,481．
【2】柳得橹,邵伟然.钢的表面带状组织及其引起的冷弯裂纹[J]. 北京科技大学学报,2005,27(1)：40-44．
【3】张 丽. 热处理缺陷裂纹产生原因的分析[J]. 装备制造技术,2006(4)：25．
【4】郑香增,夏佃秀. 34～50 mm厚钢板的研制开发[J]. 山东冶金,2006,28(1): 11-13．
【5】付秀琴,张 斌,张 弘. C62AT货车车轮崩裂分析[J]. 理化检验-物理分册,2006,42(9): 476-478,481．
相关信息