销轴断裂原因分析
FRACTURE REASON ANALYSIS ON PIN-AXIS
摘 要
采用金相分析、硬度测试及化学成分分析等方法对销轴断裂的原因进行了分析。结果表明,由于零件未按要求进行热处理,导致表面脱碳层超标、组织中有马氏体等非正常组织,加上在螺纹牙底容易造成应力集中,因此在使用后不久便发生了销轴在螺纹处断裂失效。
硬度
脱碳
断裂
bolt
hardness
decarbonization
fracture
Abstract
The fracture of break drum bolt on pin-axis of entire car was analyzed by means of metallographic examination,hardness testing and chemical composition analysis. The results showed that the heat treatment was abnomal which caused the surface of decarbonization and abnormal structure such as martensite appeared. In addition,the stress concentration arised on the base of the screw. So the pin-axis screw will fracture after operating in a short time.
中图分类号 U463.33+5
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/9/10
修改稿日期
网络出版日期
作者单位点击查看
备注杨当友(1963-),男,工程师,工学学士。
引用该论文: YANG Dang-you,LI Zhang-yin,WU Gui-gen,JIANG Qi-dong,XUE Hui-feng,ZHANG Xiao-rong. FRACTURE REASON ANALYSIS ON PIN-AXIS[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(12): 721～723
杨当友,李张银,吴贵根,姜起东,薛会锋,张小荣. 销轴断裂原因分析[J]. 理化检验－物理分册, 2008, 44(12): 721～723
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】热处理编委会. 热处理手册 第一分册[M]. 北京：机械工业出版社,1984:272-298．
【2】上海市机械制造工艺研究所.金相分析[M]. 上海：上海科学技术文献出版社,1987:301-311．
【3】李炯辉. 金属材料金相图谱[M]. 北京：机械工业出版社,2006:337．
【2】上海市机械制造工艺研究所.金相分析[M]. 上海：上海科学技术文献出版社,1987:301-311．
【3】李炯辉. 金属材料金相图谱[M]. 北京：机械工业出版社,2006:337．
相关信息