Corrosion and Repair of 1.4301 Stainless Steel Pipeline
摘 要
某水泵站项目中出现不锈钢管道腐蚀问题。对管线母材和焊缝材料进行了成分分析和微观分析, 发现焊缝处耐蚀合金含量低于母材处, 腐蚀主要发生在焊缝处。对腐蚀机理进行了探讨, 水中的氯离子含量高是导致腐蚀的主要原因, 现场温度高是次要原因。根据现场实际情况, 对腐蚀处采用BELZONA高分子材料进行修复, 有效解决了不锈钢的腐蚀问题, 保证了管道的正常运行。
Abstract
In order to resolve the corrosion problem of stainless steel pipeline in a pump station project, the chemical composition of the pipe material and welding seam were analyzed. It was found that the anticorrosion element in the welding seam was lower than that in the pipe material, and thus most of the corrosion happened on the welding seam. The corrosion mechanism was probed. the results showed that the high chloride content was the main reason for corrosion, and high temperature in site was the second factor. According to the site condition, the BELZONA high polymer material repair method was adopted, which could solve the corrosion problem effectively.
中图分类号 TG174.4 DOI 10.11973/fsyfh-201511018
所属栏目 应用技术
基金项目
收稿日期 2014/10/29
修改稿日期
网络出版日期
作者单位点击查看
备注于香利(1966-),高级工程师,硕士,从事水处理工艺研究,
引用该论文: YU Xiang-li,SHEN Quan-feng,LUO Shuang-quan,CHU Yong,LIU Jun. Corrosion and Repair of 1.4301 Stainless Steel Pipeline[J]. Corrosion & Protection, 2015, 36(11): 1096
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈小年. 304不锈钢基于氯离子环境点腐蚀失效机理的研究[D]. 扬州:扬州大学,2011.
【2】杨铁军, 李国明, 陈珊, 等. 低合金钢点蚀扩展过程中的自催化作用[J]. 腐蚀与防护,2010,31(7):541-542.
【3】中国石油大学(华东)油气CAE技术研究中心. 沙漠长距离输水工艺及控制优化技术研究报告[R]. 东营:2013.
【4】GB/T 50619-2010火力发电厂海水淡化工程设计规范[S].
【5】吴玮巍, 蒋益明, 廖家兴, 等. Cl离子对304、316不锈钢临界点蚀温度的影响[J]. 腐蚀科学与防护技术, 2007, 27(1): 18-19.
【2】杨铁军, 李国明, 陈珊, 等. 低合金钢点蚀扩展过程中的自催化作用[J]. 腐蚀与防护,2010,31(7):541-542.
【3】中国石油大学(华东)油气CAE技术研究中心. 沙漠长距离输水工艺及控制优化技术研究报告[R]. 东营:2013.
【4】GB/T 50619-2010火力发电厂海水淡化工程设计规范[S].
【5】吴玮巍, 蒋益明, 廖家兴, 等. Cl离子对304、316不锈钢临界点蚀温度的影响[J]. 腐蚀科学与防护技术, 2007, 27(1): 18-19.
相关信息