自动扶梯扶手驱动轴断裂原因分析
Cause Analysis on Fracture of Drive Shaft of Escalator Handrail
摘 要
采用断口分析、金相检验、力学性能测试、化学成分分析的方法对某型号自动扶梯扶手传动轴的断裂原因进行了分析。结果表明: 驱动轴断裂性质是高周疲劳断裂，传动轴台阶处倒圆设计不合理、机加工不符合要求引起的应力集中是造成驱动轴疲劳断裂的主要原因。
传动轴
疲劳
应力集中
断裂
escalator
drive shaft
fatigue
stress concentration
fracture
Abstract
Fracture reasons of the drive shaft of an escalator handrail were investigated by means of fracture analysis, metallographic inspection, mechanical properties test and chemical compositions analysis. The results indicate that the failure mechanism of the drive shaft was the high-cycle fatigue fracture. Stress concentration caused by unreasonable design and substandard machining of fillet section was the main reason for fatigue fracture of the drive shaft.
中图分类号 TG142.1 DOI 10.11973/lhjy-wl201601011
所属栏目 质量控制与失效分析
基金项目 浙江省质监系统科研计划资助项目(20140257)
收稿日期 2015/10/16
修改稿日期
网络出版日期
作者单位点击查看
备注王慧(1982-),男，高级工程级，博士。
引用该论文: WANG Hui,LIAO Wei,SUN Guo-feng,LIU Hai-bo. Cause Analysis on Fracture of Drive Shaft of Escalator Handrail[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2016, 52(1): 39～42
王慧,廖为,孙国峰,刘海波. 自动扶梯扶手驱动轴断裂原因分析[J]. 理化检验－物理分册, 2016, 52(1): 39～42
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李明.自动扶手电梯传动轴断裂分析［J］.理化检验-物理分册，1998,34(4): 31-32.
【2】黄忠堂.浅谈影响自动扶梯安全运行的主要原因分析［J］.科技与企业,2005(2): 215.
【3】龚帅,任学冲,马英霞，等.热处理工艺对高速车轮钢显微组织和断裂韧性的影响［J］.材料热处理学报,2015,36(4): 367-370.
【4】王春亮，孙浩，李晋，等.电机连接轴失效分析［J］.理化检验-物理分册，2005,41(11): 581-584.
【5】王慧，朱凌静，王平，等.发动机气门弹簧断裂失效分析［J］.理化检验-物理分册，2015,51(2): 139-142.
【6】宋仲明，黄晋，冯健，等.铁路车辆用LZ50钢车轴裂纹的形成机理［J］.理化检验-物理分册，2015,51(5): 315-319.
【7】GB/T 6403.4-2008 零件倒圆与倒角［S］.
【2】黄忠堂.浅谈影响自动扶梯安全运行的主要原因分析［J］.科技与企业,2005(2): 215.
【3】龚帅,任学冲,马英霞，等.热处理工艺对高速车轮钢显微组织和断裂韧性的影响［J］.材料热处理学报,2015,36(4): 367-370.
【4】王春亮，孙浩，李晋，等.电机连接轴失效分析［J］.理化检验-物理分册，2005,41(11): 581-584.
【5】王慧，朱凌静，王平，等.发动机气门弹簧断裂失效分析［J］.理化检验-物理分册，2015,51(2): 139-142.
【6】宋仲明，黄晋，冯健，等.铁路车辆用LZ50钢车轴裂纹的形成机理［J］.理化检验-物理分册，2015,51(5): 315-319.
【7】GB/T 6403.4-2008 零件倒圆与倒角［S］.
相关信息