冷拔无缝钢管内壁横向裂纹成因分析
Causes Analysis on Transverse Cracks Existing in Inner Surface of Cold-drawn Seamless Steel Tube
摘 要
分析了某钢管生产厂家制造的中低压锅炉用20冷拔无缝钢管内壁横向裂纹的特征，并通过一系列的试验实现了缺陷的重现，证明了横向裂纹的产生与钢管制造过程中润滑不良及退火软化不良有直接联系，是两者共同作用的结果，并对如何预防此类缺陷提出了建议措施。
冷拔无缝钢管
横向裂纹
缺陷重现
20 steel
cold-drawn seamless steel tube
transverse crack
defect reappearing
Abstract
The characteristics of transverse cracks existing in the inner surface of cold-drawn seamless steel tube used in medium & low pressure boiler produced by one steel tube manufactory were analyzed. The cracks reappeared through series of tests. The results show that transverse cracks were directly related to insufficient lubrication and poor annealing softening treatment, and they were the interaction results of these two factors. Finally some suggestions on how to prevent such defects were also put forward.
中图分类号 TG356.52 DOI 10.11973/lhjy-wl201601016
所属栏目 质量控制与失效分析
基金项目
收稿日期 2015/3/20
修改稿日期
网络出版日期
作者单位点击查看
备注吴世强(1987-),助理工程师,工学学士。
引用该论文: WU Shi-qiang,XIE Xiao-yuan. Causes Analysis on Transverse Cracks Existing in Inner Surface of Cold-drawn Seamless Steel Tube[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2016, 52(1): 57～60
吴世强,谢逍原. 冷拔无缝钢管内壁横向裂纹成因分析[J]. 理化检验－物理分册, 2016, 52(1): 57～60
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王洪礼，张琪昌.非线性动力学理论以及应用［M］.天津:天津科学技术出版社,2000.
【2】刘延柱，陈文良，陈立群，等.振动力学［M］.北京:高等教育出版社,1998.
【3】张琪昌，王炜，温殿英，等.高道次冷拔管抖纹问题分析［J］.天津大学学报(自然科学版),2005,38(4): 303-306.
【4】南清安，冯彦红.钢管表面润滑工艺对冷拔管质量的影响［J］.煤炭科学技术,1998,26(10): 29-31.
【5】马鹏飞，李美兰.热处理技术［M］.北京:化学工业出版社,2008.
【2】刘延柱，陈文良，陈立群，等.振动力学［M］.北京:高等教育出版社,1998.
【3】张琪昌，王炜，温殿英，等.高道次冷拔管抖纹问题分析［J］.天津大学学报(自然科学版),2005,38(4): 303-306.
【4】南清安，冯彦红.钢管表面润滑工艺对冷拔管质量的影响［J］.煤炭科学技术,1998,26(10): 29-31.
【5】马鹏飞，李美兰.热处理技术［M］.北京:化学工业出版社,2008.
相关信息