Reasons Analysis on Fracture of the Axle of a Shipbuilding Gantry Crane
摘 要
某造船厂一台龙门起重机车轮轴在服役4 a(年)之后发生断裂, 通过现场勘查并对试样进行理化检验, 分析了该车轮轴断裂的原因。结果表明:该车轮轴轴肩部位存在较深加工痕迹和缺欠, 在承受较大交变剪切应力之后, 表层加工痕迹和缺欠成为疲劳裂纹源, 撕裂表层针状铁素体向内扩展, 最终导致车轮轴发生断裂失效。
Abstract
The axle of a shipbuilding gantry crane fractured after 4 years of service, and the fracture reasons were analyzed through field investigation and physical and chemical test. The results show that there were deep machining marks and defects which became fatigue crack sources when bearing large alternating shear stress at the axle shoulder position. Then the cracks tore the surface acicular ferrite and extended to the inside, and finally resulted in the fracture of the axle.
中图分类号 TH218 DOI 10.11973/lhjy-wl201602017
所属栏目 质量控制与失效分析
基金项目 广东省质监局科技资助项目(2015CT02)
收稿日期 2015/12/3
修改稿日期
网络出版日期
作者单位点击查看
备注江爱华(1983-),男,工程师,硕士。
引用该论文: JIANG Ai-hua,HU Sheng-wen,DENG Xian-yuan,HE Shan. Reasons Analysis on Fracture of the Axle of a Shipbuilding Gantry Crane[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2016, 52(2): 139~141
江爱华,胡胜文,邓贤远,何山. 造船龙门起重机车轮轴断裂原因分析[J]. 理化检验-物理分册, 2016, 52(2): 139~141
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】TSG Q0002-2008 起重机械安全技术监察规程[S].
【2】冯凌超, 苑鸿成, 赵国强.电机主轴断裂分析[J].理化检验-物理分册,2015,51(5): 365-368.
【3】陈汉明,方可伟.某汽轮机抽汽疏水弯管泄漏失效分析[J].理化检验-物理分册,2015,51(8): 593-595.
【4】夏建新.门式起重机大车轮轴断裂原因分析[J].起重运输机械,2001(5): 29-32.
【5】陈建业,张莉,王茂,等.起重机行走机构车轮轴断裂原因分析[J].甘肃科学学报,2006,18(1): 117-119.
【6】祁学军, 杨冬梅, 宴高华.42CrMo轴件断裂原因分析[J].理化检验-物理分册, 2015,51(1): 55-58.
【2】冯凌超, 苑鸿成, 赵国强.电机主轴断裂分析[J].理化检验-物理分册,2015,51(5): 365-368.
【3】陈汉明,方可伟.某汽轮机抽汽疏水弯管泄漏失效分析[J].理化检验-物理分册,2015,51(8): 593-595.
【4】夏建新.门式起重机大车轮轴断裂原因分析[J].起重运输机械,2001(5): 29-32.
【5】陈建业,张莉,王茂,等.起重机行走机构车轮轴断裂原因分析[J].甘肃科学学报,2006,18(1): 117-119.
【6】祁学军, 杨冬梅, 宴高华.42CrMo轴件断裂原因分析[J].理化检验-物理分册, 2015,51(1): 55-58.
相关信息