等角速万向节轴杆断裂原因分析
Causes Analysis on Fracture of the Rods of Constant Velocity Universal Joints
摘 要
某公司生产的等角速万向节轴杆淬火后出现杆部断裂现象。采用宏观检验、化学成分分析、低倍组织分析及金相检验等方法, 对该万向节轴杆的断裂原因进行分析。结果表明: 等角速万向节轴杆的原材料心部带状偏析及后续的热处理不当, 导致工件淬火过程中在心部形成裂纹源, 并最终在应力作用下发生断裂。
轴杆
淬火开裂
带状偏析
淬火马氏体
constant velocity universal joint
rod
quenching crack
band segregation
quenching martensite
Abstract
Several constant velocity universal joints produced by a company were fractured after quenching. The fracture causes of constant velocity universal joints were analyzed by means of macroscopic examination, chemical composition analysis, macrostructure examination, metallographic examination and so on. The results show that because of the band segregation in core area of the raw material and improperly heat-treatment, the source of the cracks formed in the core area during the quenching process, and finally caused the fracture of the constant velocity universal joints under the action of stress.
中图分类号 TG157 DOI 10.11973/lhjy-wl201603015
所属栏目
基金项目
收稿日期 2015/3/14
修改稿日期
网络出版日期
作者单位点击查看
备注黄金富(1983-), 男, 学士。
引用该论文: HUANG Jin-fu,XU Wan-jian,YANG Chun-li,MI Liang,CHEN An-yuan,DAI Bing. Causes Analysis on Fracture of the Rods of Constant Velocity Universal Joints[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2016, 52(3): 206～209
黄金富,许万剑,杨春丽,糜亮,陈安源,戴冰. 等角速万向节轴杆断裂原因分析[J]. 理化检验－物理分册, 2016, 52(3): 206～209
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李炯辉.金属材料金相图谱[M].北京:机械工业出版社,2006: 403.
【2】朱晓红,陈国琦.哥林柱断裂失效分析[J].理化检验-物理分册,2013,49(6): 407-412.
【3】高宗仁.中外钢号速查手册[M].太原:山西科学技术出版社,2008: 384.
【4】金林奎,赵建国,王春亮,等.40Cr钢汽车半轴断裂失效分析[J].金属热处理,2015(2): 220-223.
【5】马勇杰.热处理工艺方法600种[M].北京: 化学工业出版社,2008: 137.
【2】朱晓红,陈国琦.哥林柱断裂失效分析[J].理化检验-物理分册,2013,49(6): 407-412.
【3】高宗仁.中外钢号速查手册[M].太原:山西科学技术出版社,2008: 384.
【4】金林奎,赵建国,王春亮,等.40Cr钢汽车半轴断裂失效分析[J].金属热处理,2015(2): 220-223.
【5】马勇杰.热处理工艺方法600种[M].北京: 化学工业出版社,2008: 137.
相关信息