一种低铬达克罗涂层的制备工艺及性能
Perparation Technology and Property of a Low Chromium Dacromet Coating
摘 要
介绍了低铬达克罗涂层的制备工艺，通过极化曲线，电化学阻抗，盐水浸泡等方法对涂层性能和腐蚀行为进行了评价和研究，运用SEM和XRD手段分析了涂层的形貌和成分。结果表明: 涂层制备过程中，无机盐可取代部分铬酐，其生成的腐蚀产物作为屏蔽层能够有效阻止腐蚀介质的入浸，提高涂层的耐蚀性；加入适量的环氧树脂和KH-570硅烷偶联剂能够增强涂层在基体表面的附着力。
环氧树脂
硅烷偶联剂
无机盐
耐腐蚀性能
low-chromium dacramet film
epoxy resin
silane coupling agent
inorganic salt
corrosion resistance
Abstract
The preparation technology of a low chromium dacromet coating is introduced. The property and corrosion behavior of the coating were studied by means of polarization curve, electrochemical impedance spectroscopy (EIS) and immersion test. The morphology and composition of the coating were analysed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results showed that during the preparing process, part of chromic anhydride was replaced by inorganic salt, and the corrosion products as a shield could prevent the corrosion medium, and the corrosion resistance was increased. Adding epoxy resin and silane coupling agent could enhance the adhesion on the substrate surface.
中图分类号 TG174 DOI 10.11973/fsyfh-201603012
所属栏目 应用技术
基金项目
收稿日期 2015/3/9
修改稿日期
网络出版日期
作者单位点击查看
备注张圣麟(1960-),教授,博士,从事材料腐蚀与防护研究,
引用该论文: QIAO Jing-fei,ZHANG Ming-ming,LI Wen-chao,ZHANG Sheng-lin. Perparation Technology and Property of a Low Chromium Dacromet Coating[J]. Corrosion & Protection, 2016, 37(3): 241
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】MULKINF. A new coating for corrosion and protection of metals with zinc powder passivited by chromate. US,3673731[P].1972-06-21.
【2】KRAUSE H H N. Dacromet—A new corrosion protection for fastener[J]. Product Finishing,1997(5):29.
【3】于兴文. 达克罗技术研究进展[J]. 腐蚀与防护,2001,22(1):1-4.
【4】孙贺民. 锌铬膜——一种特殊的表面处理新技术[J]. 材料保护,1994,27(18):21-23.
【5】宋积文,杜敏. 无铬锌铝涂层发展现状[J]. 腐蚀与防护,2007,28(8):411-413.
【6】高勤. 达克罗——一种优秀的新型涂层[J]. 电镀与环保,1995,15(5):29-30.
【7】胡会利，李宁，韩家军，等. 达克罗的研究现状[J]. 电镀与涂饰,2005,24(3):31-33.
【8】LONCA M. Dacrotizing-an effective protection against corrosion[J]. Finishing,1990,14(9):35-38.
【9】MICHEL F D,FREDERIC G,PETER E W. The aplication of zinc aluminium flake non-electorlytic. Surface coatings[J]. Trans IMF,1993,71(1):21.
【10】SONTAG A. Dacrometisierung-korrosinosschutz and umwelt[J]. Galvan-otechnik,1992,83(6):13.
【11】马壮,黄圣玲,李智超,等. 达克罗技术近期进展研究[J]. 现代涂料与装涂,2008,11(6):16-18.
【12】仝飞,缪强,蒋穹. 无铬锌铝合金涂层的制备及耐蚀性能[J]. 腐蚀与防护,2014,35(2):146-149.
【13】蔡元兴. 环保型富锌涂层工艺与性能的研究[D]. 济南:山东大学,2006.
【14】李宁,胡会利,黎德育. 烧结式金属粉末涂料及以其制备金属陶瓷防腐涂层的方法. 中国100439[P].2004-10-04.
【15】赵全玺. 无机磷酸盐涂料. 中国1232060[P]，1999-05-07.
【16】安恩朋,李相波,程旭东,等. 达克罗涂层研究现状[J]. 腐蚀科学与防护技术,2014,26(1):73-76.
【17】季利亚,姚正军. 无铬达克罗涂层的工艺研究[J]. 电镀与环保,2011,31(3):3-24.
【18】李荻. 电化学原理[M]. 北京:北京航空航天大学出版社,1999:406.
【19】ZHANG L Y,MA A B,JIANG J H. Anti-corrosion performance of waterborne Zn-rich coating with modified silicon-based vehicle and lamellar Zn (Al) pigments[J]. Progress in Natural Science:Materials International,2012;22(4):326-333.
【20】吴海刚,杨飞英. 热镀锌钢表面硅烷膜的腐蚀电化学性能[J]. 中国表面工程,2009,22(5):7-69.
【2】KRAUSE H H N. Dacromet—A new corrosion protection for fastener[J]. Product Finishing,1997(5):29.
【3】于兴文. 达克罗技术研究进展[J]. 腐蚀与防护,2001,22(1):1-4.
【4】孙贺民. 锌铬膜——一种特殊的表面处理新技术[J]. 材料保护,1994,27(18):21-23.
【5】宋积文,杜敏. 无铬锌铝涂层发展现状[J]. 腐蚀与防护,2007,28(8):411-413.
【6】高勤. 达克罗——一种优秀的新型涂层[J]. 电镀与环保,1995,15(5):29-30.
【7】胡会利，李宁，韩家军，等. 达克罗的研究现状[J]. 电镀与涂饰,2005,24(3):31-33.
【8】LONCA M. Dacrotizing-an effective protection against corrosion[J]. Finishing,1990,14(9):35-38.
【9】MICHEL F D,FREDERIC G,PETER E W. The aplication of zinc aluminium flake non-electorlytic. Surface coatings[J]. Trans IMF,1993,71(1):21.
【10】SONTAG A. Dacrometisierung-korrosinosschutz and umwelt[J]. Galvan-otechnik,1992,83(6):13.
【11】马壮,黄圣玲,李智超,等. 达克罗技术近期进展研究[J]. 现代涂料与装涂,2008,11(6):16-18.
【12】仝飞,缪强,蒋穹. 无铬锌铝合金涂层的制备及耐蚀性能[J]. 腐蚀与防护,2014,35(2):146-149.
【13】蔡元兴. 环保型富锌涂层工艺与性能的研究[D]. 济南:山东大学,2006.
【14】李宁,胡会利,黎德育. 烧结式金属粉末涂料及以其制备金属陶瓷防腐涂层的方法. 中国100439[P].2004-10-04.
【15】赵全玺. 无机磷酸盐涂料. 中国1232060[P]，1999-05-07.
【16】安恩朋,李相波,程旭东,等. 达克罗涂层研究现状[J]. 腐蚀科学与防护技术,2014,26(1):73-76.
【17】季利亚,姚正军. 无铬达克罗涂层的工艺研究[J]. 电镀与环保,2011,31(3):3-24.
【18】李荻. 电化学原理[M]. 北京:北京航空航天大学出版社,1999:406.
【19】ZHANG L Y,MA A B,JIANG J H. Anti-corrosion performance of waterborne Zn-rich coating with modified silicon-based vehicle and lamellar Zn (Al) pigments[J]. Progress in Natural Science:Materials International,2012;22(4):326-333.
【20】吴海刚,杨飞英. 热镀锌钢表面硅烷膜的腐蚀电化学性能[J]. 中国表面工程,2009,22(5):7-69.
相关信息