机场供油管线X52钢腐蚀的影响因素
Influencing Factors on Corrosion of Oil Supply Pipeline with X52 Steel for Airport
摘 要
通过极化曲线和电化学阻抗谱研究了交流杂散电流、温度、pH和氯离子含量对天津机场供油管线钢X52钢腐蚀行为的影响。结果表明:在交流干扰情况下X52钢的腐蚀速率要比没有干扰情况下更快，且随着干扰电压的增大而增大；在15 V交流干扰电压条件下，改变温度、pH和氯离子含量都会使X52钢的腐蚀速率发生变化，且腐蚀产物不同；此供油管线的最佳保护电位应该在-987~-1 006 mV(SCE)，且腐蚀控制形式都偏向于阳极控制。
温度
pH
氯离子浓度
腐蚀速率
最佳保护电位
阳极控制
AC stray current
temperature
pH
chloride ion concentration
corrosion rate
the best protection potential
anodic control
Abstract
The influence of AC stray current, temperature, pH and chloride ion concentration on grade X52 airport oil supply pipeline steel corrosion was studied by means of polarization curves and electrochemical impedance spectroscopy. The experimental results show that the corrosion rate of X52 steel in the presence of AC stray current was faster than that without the interference, and it increased with the increase of interference voltage. At 15V AC voltage, the corrosion rate changed with the variation of temperature, pH value and chloride ion concentration. And the corrosion products had significant changes in these three cases. The best protection potential for the oil supply pipeline should be within the range of -987- -1 006 mV (SCE), and the corrosion process is controlled by anodic reaction.
中图分类号 TG174 DOI 10.11973/fsyfh-201604016
所属栏目 应用技术
基金项目 国家自然科学青年基金资助(51206179)； 中央高校基金项目(3122014D027)； 大学生创新创业训练计划项目(201410059046)
收稿日期 2015/2/10
修改稿日期
网络出版日期
作者单位点击查看
备注丁清苗(1984-),讲师,博士,从事材料腐蚀与防护方面的研究,
引用该论文: DING Qing-miao,FAN Yue-ming,SHEN Tao,ZHANG Liang-liang,ZHANG Xuan. Influencing Factors on Corrosion of Oil Supply Pipeline with X52 Steel for Airport[J]. Corrosion & Protection, 2016, 37(4): 345
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王立刚. 烟台机场供油工程规划研究[D]. 北京:北京交通大学,2010:2-5.
【2】司敏. 广州白云国际机场迁建供油工程航煤长输管道工程项目管理信息系统开发研究[D]. 武汉:武汉理工大学,2002:1-5.
【3】邓祖荣,杨惠谷,刘威力. 上海浦东国际机场扩建场外供油输油管线通球试压[J]. 化工装备技术,2008,29(4):46-47.
【4】刘悦明. 阴极保护技术在深圳机场埋地输油管道上的应用[J]. 化工设备与管道,2004,40(4):42-45.
【5】GUMMOW R A,WAKELIN R G,SEGALL S M. AC corrosion—a new challenge to pipeline integrity[R]. Houston,TX(United States):NACE International,1998.
【6】尚秦玉,许进,尚思贤. 高压线路对地下输油管道中杂散电流影响规律[J]. 腐蚀科学与防护技术,2007,19(5):371-372.
【7】SYROTYUK A M,DMYTRAKH I M. Methods for the evaluation of fracture and strength of pipeline steels and structures under the action of working media. part ⅰ. influence of the corrosion factor[J]. Materials Science,2014,50(3):324-339.
【8】FANG B Y,ATRENS A,WANG J Q,et al. Review of stress corrosion cracking of pipeline steels in “low” and “high” pH solutions[J]. Journal of Materials Science,2003,38(1):127-132.
【9】CHEN W,KING F,VOKES E. Characteristics of near-neutral-pH stress corrosion cracks in an X-65 pipeline[J]. Corrosion,2002,58(3):267-275.
【10】秦有冰,程伯秀,单云明. pH和氯离子浓度对碳钢在酸溶液中的腐蚀电化学行为的影响[J]. 南京工业大学学报(自然科学版),1989(3):2.
【11】丁清苗,王辉,吕亳龙,等. 电化学方法研究交流干扰对阴极保护电位的影响[J]. 腐蚀与防护,2012,32(12):984-987.
【12】崔晓莉,江志裕. 交流阻抗谱的表示及应用[J]. 上海师范大学学报(自然科学版),2001,30(4):53-61.
【2】司敏. 广州白云国际机场迁建供油工程航煤长输管道工程项目管理信息系统开发研究[D]. 武汉:武汉理工大学,2002:1-5.
【3】邓祖荣,杨惠谷,刘威力. 上海浦东国际机场扩建场外供油输油管线通球试压[J]. 化工装备技术,2008,29(4):46-47.
【4】刘悦明. 阴极保护技术在深圳机场埋地输油管道上的应用[J]. 化工设备与管道,2004,40(4):42-45.
【5】GUMMOW R A,WAKELIN R G,SEGALL S M. AC corrosion—a new challenge to pipeline integrity[R]. Houston,TX(United States):NACE International,1998.
【6】尚秦玉,许进,尚思贤. 高压线路对地下输油管道中杂散电流影响规律[J]. 腐蚀科学与防护技术,2007,19(5):371-372.
【7】SYROTYUK A M,DMYTRAKH I M. Methods for the evaluation of fracture and strength of pipeline steels and structures under the action of working media. part ⅰ. influence of the corrosion factor[J]. Materials Science,2014,50(3):324-339.
【8】FANG B Y,ATRENS A,WANG J Q,et al. Review of stress corrosion cracking of pipeline steels in “low” and “high” pH solutions[J]. Journal of Materials Science,2003,38(1):127-132.
【9】CHEN W,KING F,VOKES E. Characteristics of near-neutral-pH stress corrosion cracks in an X-65 pipeline[J]. Corrosion,2002,58(3):267-275.
【10】秦有冰,程伯秀,单云明. pH和氯离子浓度对碳钢在酸溶液中的腐蚀电化学行为的影响[J]. 南京工业大学学报(自然科学版),1989(3):2.
【11】丁清苗,王辉,吕亳龙,等. 电化学方法研究交流干扰对阴极保护电位的影响[J]. 腐蚀与防护,2012,32(12):984-987.
【12】崔晓莉,江志裕. 交流阻抗谱的表示及应用[J]. 上海师范大学学报(自然科学版),2001,30(4):53-61.
相关信息