HJ曼尼希碱缓蚀剂的合成及其性能
Synthesis and Performance of HJ Mannich Base Inhibitor
摘 要
采用糠醛、苯乙酮和水合肼合成了HJ曼尼希碱缓蚀剂。通过静态失重法和电化学方法评价了该缓蚀剂对N80钢的缓蚀性能。静态失重法表明, N80钢片在加有1.0%(质量分数)HJ曼尼希碱的15%(体积分数, 下同)盐酸溶液中的腐蚀速率为 0.623 5 g·m-2·h-1, 远低于SY/T5405-1996标准中的一级标准。电化学测试结果表明, 该缓蚀剂是以抑制阳极腐蚀过程为主的混合型缓蚀剂。该缓蚀剂在N80钢表面上的吸附行为服从Langmiur吸附等温式。
缓蚀剂
吸附
缓蚀机理
mannich base
inhibitor
adsorption
inhibition mechanism
Abstract
HJ Mannich base was synthesized using furfural, acetophenone and hydrazine hydrate. The inhibition property of HJ Mannich base on N80 steel was investigated by mass loss method and electrochemical techniques. The results show that the corrosion rate of N80 steel was 0.623 5 g·m-2·h-1 in 15% HCl solution containing 1.0% of HJ, which was lower than that in the first grade standard of SY/T 5405-1996. Electrochemical test results showed that the HJ Mannich base belonged to a mainly anodic-controlling composite corrosion inhibitor. The adsorption behavior of the HJ on the surface of N80 steel was subject to Langmiur adsorption isotherm.
中图分类号 TG174.4 DOI 10.11973/fsyfh-201606007
所属栏目 试验研究
基金项目 国家自然科学基金(41202111); 国家大学生创新实验计划(111048910)
收稿日期 2015/4/3
修改稿日期
网络出版日期
作者单位点击查看
备注李克华(1964-), 教授, 博士, 从事金属腐蚀与防护的研究工作,
引用该论文: LI Ke-hua,LAN Zhi-wei,YANG Bing-bing,SHI Dong-po. Synthesis and Performance of HJ Mannich Base Inhibitor[J]. Corrosion & Protection, 2016, 37(6): 467
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李俊莉, 白方林, 卢永斌, 等. 新型席夫碱酸化缓蚀剂的合成及性能评价[J]. 腐蚀与防护, 2012, 33(9):786-791.
【2】张娟涛, 李谦定, 赵俊. 油气井酸化缓蚀剂研究现状[J]. 腐蚀与防护, 2014, 35(6):593-597.
【3】张大全, 高立新, 周国定. 国内外缓蚀剂研究开发与展望[J]. 腐蚀与防护, 2009, 30(9):604-610.
【4】王慧龙, 辛剑, 袁万钟, 等. 盐酸介质中Mannich碱缓蚀剂在碳钢表面的吸附热力学研究[J]. 中国腐蚀与防护学报, 2001, 21(3):144-149.
【5】曹楚南. 腐蚀电化学原理［M］. 北京: 化学工业出版社, 2008:211-212.
【6】段世泽, 谭逸玲. 界面化学[M]. 北京:高等教育出版社, 1990:124.
【7】MARTINEZS S. Inhibitory mechanism of low-carbon steel corrosion by mimosa tannin in sulphuric acid solutions[J]. Journal of Applied Electrochemistry, 2001, 31(9):973-978.
【8】REHIM S A E, IBRAHIM M A M, KHALED K F. The inhibition of 4-(2-amino-5-methylphenylazo) antipyrine on corrosion of mild steel in HCl solution[J]. Materials Chemistry and Physics, 2001, 70(3):268-273.
【9】曹楚南. 腐蚀电化学[M]. 北京: 化学工业出版社, 1994: 134.
【10】ALBERTY R A. Thermodynamics of reactions of nicotinamide adenine dinucleotie and nicotinamide adenine dinucleotide phosphate[J]. Biochemistry and Biophy Sics, 1993, 307(1):8-14.
【11】何桥, 张胜涛, 李伟华, 等. 酸性介质中新型三唑类缓蚀剂在碳钢上的吸附行为[J]. 腐蚀与防护, 2008, 29(5):243-246.
【2】张娟涛, 李谦定, 赵俊. 油气井酸化缓蚀剂研究现状[J]. 腐蚀与防护, 2014, 35(6):593-597.
【3】张大全, 高立新, 周国定. 国内外缓蚀剂研究开发与展望[J]. 腐蚀与防护, 2009, 30(9):604-610.
【4】王慧龙, 辛剑, 袁万钟, 等. 盐酸介质中Mannich碱缓蚀剂在碳钢表面的吸附热力学研究[J]. 中国腐蚀与防护学报, 2001, 21(3):144-149.
【5】曹楚南. 腐蚀电化学原理［M］. 北京: 化学工业出版社, 2008:211-212.
【6】段世泽, 谭逸玲. 界面化学[M]. 北京:高等教育出版社, 1990:124.
【7】MARTINEZS S. Inhibitory mechanism of low-carbon steel corrosion by mimosa tannin in sulphuric acid solutions[J]. Journal of Applied Electrochemistry, 2001, 31(9):973-978.
【8】REHIM S A E, IBRAHIM M A M, KHALED K F. The inhibition of 4-(2-amino-5-methylphenylazo) antipyrine on corrosion of mild steel in HCl solution[J]. Materials Chemistry and Physics, 2001, 70(3):268-273.
【9】曹楚南. 腐蚀电化学[M]. 北京: 化学工业出版社, 1994: 134.
【10】ALBERTY R A. Thermodynamics of reactions of nicotinamide adenine dinucleotie and nicotinamide adenine dinucleotide phosphate[J]. Biochemistry and Biophy Sics, 1993, 307(1):8-14.
【11】何桥, 张胜涛, 李伟华, 等. 酸性介质中新型三唑类缓蚀剂在碳钢上的吸附行为[J]. 腐蚀与防护, 2008, 29(5):243-246.
相关信息