核电厂蒸汽发生器SA213T22传热管表面氧化膜的耐蚀性
Corrosion Resistance of Oxidation Film on SA213T22 Heat Transfer Tube Surface for Steam Generator in Nuclear Power Plant
摘 要
人工研制了核电厂蒸汽发生器SA213T22传热管的高温氧化膜，采用SEM、XRD、热重分析法分别对氧化膜厚度、微观形貌、成分和稳定性进行了观察和分析。结果表明：氧化膜具有均匀、完整、无孔隙、稳定性好的特点;经高温氧化及矿物油封闭处理后，SA213T22传热管的耐蚀性得到了显著提高，在不同环境中挂片31个月后，试样均未发生腐蚀，完全满足工程应用的要求。
蒸汽发生器
SA213T22传热管
氧化膜
腐蚀
nuclear power plant
steam generator
SA213T22 heat transfer tube
oxidation film
corrosion
Abstract
The artificial oxidation film on SA213T22 heat transfer tubes for steam generator in nuclear power plant was studied, the thickness, microstructure, compositions and stabilization of the oxidation film were analyzed by SEM, XRD and thermo gravimetric analysis method, respectively. The results showed that oxidation film had characteristics of homogeneity, integrity, inporosity and good stabilization. The samples were not corroded in different environments for 31 months. The corrosion resistance fully meets the requirements of engineering applications.
中图分类号 TG174 DOI 10.11973/fsyfh201607009
所属栏目 核电设备材料防护
基金项目
收稿日期 2015/10/20
修改稿日期
网络出版日期
作者单位点击查看
联系人作者朱兴华(14451147@qq.com)
备注朱兴华(1982-),高级工程师,本科,从事核电材料相关研究工作
引用该论文: LI Jufeng,ZHU Xinghua,XIONG Wenbin,WANG Yin. Corrosion Resistance of Oxidation Film on SA213T22 Heat Transfer Tube Surface for Steam Generator in Nuclear Power Plant[J]. Corrosion & Protection, 2016, 37(7): 572
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】PILLING N B,BEDWORTH R E. The oxidation of metals in high temperature\[J\]. Journal of Institute of Metals,1923(29)：529.
【2】李隆盛. 铸钢及其熔炼\[M\]. 北京：机械工业出版社，1981：80.
【3】李铁藩. 金属高温氧化和热腐蚀\[M\]. 北京：化学工业出版社，2003：169.
【4】胡赓祥，蔡珣，戎咏华. 材料科学基础\[M\]. 2版. 上海：上海交通大学出版社，2006：64.
【5】H.Π.梁基谢夫（俄）. 金属二元系相图手册\[M\]. 北京：化学工业出版社，2009：598.
【2】李隆盛. 铸钢及其熔炼\[M\]. 北京：机械工业出版社，1981：80.
【3】李铁藩. 金属高温氧化和热腐蚀\[M\]. 北京：化学工业出版社，2003：169.
【4】胡赓祥，蔡珣，戎咏华. 材料科学基础\[M\]. 2版. 上海：上海交通大学出版社，2006：64.
【5】H.Π.梁基谢夫（俄）. 金属二元系相图手册\[M\]. 北京：化学工业出版社，2009：598.
相关信息