Effect of Heat Treatment on Microstructure and Corrosion Resistance of Alloy Mg9Gd2Y0.6Zr
摘 要
采用失重法、扫描电子显微镜、光学显微镜研究了热处理对Mg9Gd2Y0.6Zr合金显微组织和耐蚀性的影响。结果表明:合金铸态组织由αMg基体和粗大的枝晶β相组成,热处理后,合金中的β相经过溶解再析出的过程,β相由断续网状转变为方块颗粒状;热处理工艺显著提高了合金在Hanks模型中的耐蚀性,且腐蚀产物以Mg(OH)2为主。
Abstract
Weight loss method, SEM and OM were used to investigate the effect of heat treatment on microstructure and corrosion resistance of Mg9Gd2Y0.6Zr alloy. The results show that the microstructure of the ascast alloy was composed of αMg matrix and coarse crystal β phase. After heat treatment, the precipitation mode of β phase was different, the discontinued β phase transformed into cuboidshaped particles after the solution and aging treatment. The alloy had a superior corrosion resistant performance in Hanks simulated body fluid. After heat treatment, the corrosion resistance of the alloy in Hanks simulated solution increased, and the corrosion product of the alloy was mainly Mg(OH)2.
中图分类号 TG146.2 DOI 10.11973/fsyfh201607013
所属栏目 试验研究
基金项目
收稿日期 2015/7/31
修改稿日期
网络出版日期
作者单位点击查看
备注戴丽娟(1963-),副教授,从事金属材料热处理技术研究
引用该论文: DAI lijuan,ZHUO Heng. Effect of Heat Treatment on Microstructure and Corrosion Resistance of Alloy Mg9Gd2Y0.6Zr[J]. Corrosion & Protection, 2016, 37(7): 592
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】付三玲,李全安,井晓天,等. 热处理对Mg12Gd2Y0.5Sm0.5Sb0.5Zr显微组织的影响\[J\]. 材料热处理学报,2014,35(4):4752.
【2】马莹,郭阳,张忠明,等. Ca对铸态Mg4Zn合金组织及腐蚀性能的影响\[J\]. 材料热处理学报,2015,36(1):6269.
【3】付三玲,李全安,井晓天,等. 热处理对Mg12Gd3YSm0.5Sb0.5Zr合金组织和性能的影响\[J\]. 材料热处理学报,2014,35(5):4448.
【4】李全安,李克杰,张清. Sm对时效Mg12Gd2Y0.5Zr合金组织和力学性能的影响\[J\]. 材料热处理学报,2011,32(12):8490.
【5】李凌杰,王莎,潘复生,等. AM60镁合金在汽车发动机冷却液中的腐蚀电化学行为\[J\]. 电化学,2010,49(16):425429.
【6】付三玲,李全安,井晓天,等. Mg9Gd2YSm0.5Zr合金组织和耐蚀性能研究\[J\]. 稀土,2014,35(4):5256.
【7】黄亮,黄元伟,王晨,等. 含稀土元素的MgAl合金在NaCl溶液中腐蚀产物膜的研究\[J\]. 中国腐蚀与防护学报,2012,33(3):167171.
【8】周京,冯芝勇,张金玲,等. 稀土Nd含量对AM60镁合金耐蚀性能的影响\[J\]. 中国腐蚀与防护学报,2014,34(2):185191.
【9】刘子利,朱晓春,周桂斌,等. Sb对Mg5Al2Sr合金耐腐蚀性能的影响\[J\]. 中国腐蚀与防护学报,2012,32(6):478482.
【10】易建龙,张新明. Ce对Mg9Gd4Y1Nd0.6Zr合金微观组织和耐蚀性的影响\[J\]. 中国腐蚀与防护学报,2012,32(3):262268.
【11】吴国华,樊昱,翟春泉,等. 稀土La对AZ91D镁合金在NaCl溶液中耐蚀性的影响\[J\]. 金属学报,2008,44(10):12471253.
【12】曾荣昌,郭小龙,刘成龙,等. 医用MgCa和MgLiCa合金腐蚀研究\[J\]. 金属学报,2011,47(11):14771482.
【13】张亚丛,王锦程,吕文泉. MgZnYZr合金在NaCl溶液中的腐蚀行为\[J\]. 金属学报,2011,47(9):11741180.
【14】张金玲,刘阳力,周京,等. T6处理对Mg9AlZn0.16La合金耐蚀性能的影响\[J\]. 材料热处理学报,2014,35(5):6469.
【15】李克杰,李全安. Sm和Sb对时效态 Mg12Gd2Y0.5Zr合金组织与力学性能的影响\[J\]. 材料热处理学报,2011,32(5):110115.
【2】马莹,郭阳,张忠明,等. Ca对铸态Mg4Zn合金组织及腐蚀性能的影响\[J\]. 材料热处理学报,2015,36(1):6269.
【3】付三玲,李全安,井晓天,等. 热处理对Mg12Gd3YSm0.5Sb0.5Zr合金组织和性能的影响\[J\]. 材料热处理学报,2014,35(5):4448.
【4】李全安,李克杰,张清. Sm对时效Mg12Gd2Y0.5Zr合金组织和力学性能的影响\[J\]. 材料热处理学报,2011,32(12):8490.
【5】李凌杰,王莎,潘复生,等. AM60镁合金在汽车发动机冷却液中的腐蚀电化学行为\[J\]. 电化学,2010,49(16):425429.
【6】付三玲,李全安,井晓天,等. Mg9Gd2YSm0.5Zr合金组织和耐蚀性能研究\[J\]. 稀土,2014,35(4):5256.
【7】黄亮,黄元伟,王晨,等. 含稀土元素的MgAl合金在NaCl溶液中腐蚀产物膜的研究\[J\]. 中国腐蚀与防护学报,2012,33(3):167171.
【8】周京,冯芝勇,张金玲,等. 稀土Nd含量对AM60镁合金耐蚀性能的影响\[J\]. 中国腐蚀与防护学报,2014,34(2):185191.
【9】刘子利,朱晓春,周桂斌,等. Sb对Mg5Al2Sr合金耐腐蚀性能的影响\[J\]. 中国腐蚀与防护学报,2012,32(6):478482.
【10】易建龙,张新明. Ce对Mg9Gd4Y1Nd0.6Zr合金微观组织和耐蚀性的影响\[J\]. 中国腐蚀与防护学报,2012,32(3):262268.
【11】吴国华,樊昱,翟春泉,等. 稀土La对AZ91D镁合金在NaCl溶液中耐蚀性的影响\[J\]. 金属学报,2008,44(10):12471253.
【12】曾荣昌,郭小龙,刘成龙,等. 医用MgCa和MgLiCa合金腐蚀研究\[J\]. 金属学报,2011,47(11):14771482.
【13】张亚丛,王锦程,吕文泉. MgZnYZr合金在NaCl溶液中的腐蚀行为\[J\]. 金属学报,2011,47(9):11741180.
【14】张金玲,刘阳力,周京,等. T6处理对Mg9AlZn0.16La合金耐蚀性能的影响\[J\]. 材料热处理学报,2014,35(5):6469.
【15】李克杰,李全安. Sm和Sb对时效态 Mg12Gd2Y0.5Zr合金组织与力学性能的影响\[J\]. 材料热处理学报,2011,32(5):110115.
相关信息