Radiographic Testing Process of Hydrogen Double-Walled Stainless Steel Pipe Weld of Nuclear Power Plant
摘 要
核电厂某段SHY系统输氢不锈钢双壁管在外管已安装到位的情况下, 发现未对内管环焊缝进行射线检测。为解决此问题, 提出了不切割拆除双壁不锈钢外管, 而直接隔着外管对内管进行射线检测的工艺, 结合规范分析确定了射线检测的关键工艺参数, 并采用已知缺陷的内管加套管模拟试块, 对工艺进行了试验, 验证了该工艺的合理有效性。
Abstract
The certain SHY hydrogen stainless steel double-walled tube outer tube was in place, but the inner pipe ring welds had not been detected. To solve this problem, it was proposed that do not cut the double-walled stainless steel tube, but directly detected the inner tube across the outer tube, combined normative analysis identified the key process parameters of X-Ray detector, and used known defect test block, the test was carried out to verify the effectiveness of the process is reasonable.
中图分类号 TG115.28 DOI 10.11973/wsjc201609006
所属栏目 试验研究
基金项目
收稿日期 2016/4/25
修改稿日期
网络出版日期
作者单位点击查看
联系人作者李学军(21140475@qq.com)
备注李学军(1981-), 男, 硕士, 主要从事核电厂机械部件的无损检测设计及核电厂役前及在役检查设计工作。
引用该论文: LI Xue-jun,GUO Xiao-kai,SUN Guang,CAO Bang-xing. Radiographic Testing Process of Hydrogen Double-Walled Stainless Steel Pipe Weld of Nuclear Power Plant[J]. Nondestructive Testing, 2016, 38(9): 21~24
李学军,郭晓凯,孙 广,曹邦兴. 核电厂输氢不锈钢双壁管焊缝的射线检测工艺[J]. 无损检测, 2016, 38(9): 21~24
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】DL/T 821-2002 钢制承压管道对接焊接接头射线检验技术规程[S].
【2】张小海, 王广坤.小径管对接环焊缝有效透照厚度的计算[J] .无损检测, 2006, 28(7):389-391.
【3】强天鹏.NDT全国特种设备无损检测人员资格考核统编教材射线检测[M].2版, 北京: 人民卫生出版社, 2005.
【2】张小海, 王广坤.小径管对接环焊缝有效透照厚度的计算[J] .无损检测, 2006, 28(7):389-391.
【3】强天鹏.NDT全国特种设备无损检测人员资格考核统编教材射线检测[M].2版, 北京: 人民卫生出版社, 2005.
相关信息