AUT of Weld Zones of the Girth Welds in the CRA Composite Subsea Pipeline
摘 要
CRA(耐腐蚀合金)复合材料海底管道内表面通常堆焊约3 mm厚的625不锈钢, 该海底管道环焊缝通常采用射线(RT)检测技术评估焊缝的焊接质量。由于RT检测效率较低, 安全风险较高, 极大地影响了CRA复合材料海底管道铺设效率。针对以上问题, 对全自动超声波(AUT)检测工艺进行研究, 主要通过综合运用低频纵波相控阵(PA)探头, 爬波探头、双晶纵波相控阵(TRL)探头以及超声衍射时差(TOFD)探头, 对制作的22个人工缺陷焊缝(共242个不同区域的人工缺陷)进行评价试验, 并与RT检测评价结论进行对比分析, 以评估该AUT检测工艺对CRA复合材料海底管道环焊缝各个区域缺陷的检出率。
Abstract
The inner surface of the CRA composite subsea pipe is always overlaid by 3 mm stainless steel. RT is the normal inspection method of the girth weld. Due to the low efficiency and high risk of RT, the CRA pipe-laying efficiency will pull down. This essay makes a research of the AUT technique focusing on performing the evaluation test on the 22 defective welds (242 induced defects located in different area) by the combination of the low frequency LW PA probes, creep probes, TRL probes and TOFD probes, so as to evaluate the POD of individual area in the CRA girth weld.
中图分类号 TG115.28 DOI 10.11973/wsjc201609012
所属栏目
基金项目
收稿日期 2016/4/7
修改稿日期
网络出版日期
作者单位点击查看
联系人作者裴彪(yimignet@163.com)
备注裴 彪(1987-),男, 工程师, 主要从事海底管线质量控制及NDT技术应用工作。
引用该论文: PEI Biao,XU Zhen,CHANG Yu. AUT of Weld Zones of the Girth Welds in the CRA Composite Subsea Pipeline[J]. Nondestructive Testing, 2016, 38(9): 46~48
裴 彪,徐 振,常 宇. 耐腐蚀合金复合材料海底管道环焊缝各区域全自动超声波检测[J]. 无损检测, 2016, 38(9): 46~48
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】DNV-OS-F101 海底管线系统[S].
【2】陈亮, 孙晓明, 尤卫宏.海底管线AUT分区法缺陷高度定量测量修正方法[J].无损检测, 2014,36(7):81-84.
【2】陈亮, 孙晓明, 尤卫宏.海底管线AUT分区法缺陷高度定量测量修正方法[J].无损检测, 2014,36(7):81-84.
相关信息