SiC含量对激光熔覆原位合成WC增强铁基合金涂层组织与性能的影响
Effects of SiC Content on Microstructure and Properties of In-situ Synthesized WC Reinforced Iron-Based Alloy Coating by Laser Cladding
摘 要
以不同SiC含量(质量分数为0～12%)的合金混合粉为预置粉体, 采用激光熔覆法在45钢表面原位合成了WC颗粒增强铁基合金涂层, 研究了SiC含量对涂层组织、硬度和耐磨性能的影响。结果表明: 随着混合粉中SiC的质量分数增加, 涂层中WC的含量与尺寸逐渐增加, 贫碳相Fe3W3C的含量与尺寸先增加后减小, 涂层的硬度与耐磨性先增加后减小; 当SiC的质量分数为8%时, 涂层的硬度与耐磨性都达到最大值, 其硬度为59 HRC, 相对耐磨性约为基体的24倍。
原位合成
SiC
耐磨性
automobile crankshaft
in-situ synthesis
SiC
wear resistance
Abstract
Using the alloy powders with different SiC contents (0-12wt%) as raw material, WC particles reinforced iron-based coatings were in-situ synthesized on 45 steel surface by laser cladding; The effects of SiC content on microstructure, hardness and wear resistance of the coatings were investigated. The results show that, with the increase of mass fraction of SiC in alloy powders, the content and size of WC increased, while the content and size of Fe3W3C increased firstly and then declined. The hardness and wear resistance of the coatings increased firstly and then declined. When the mass fraction of SiC in alloy powders was 8%, the hardness of the coating was 59 HRC, and its relative wear resistance was about 24 times of the substrate.
中图分类号 TG422.1 DOI 10.11973/jxgccl201610004
所属栏目 试验研究
基金项目 湖南省教育厅科学研究课题项目(15C0710)
收稿日期 2015/7/17
修改稿日期 2016/7/21
网络出版日期
作者单位点击查看
备注刘海渔(1968-),男,湖南株洲人,副教授, 硕士。
引用该论文: LIU Hai-yu,SHEN Yan-jin. Effects of SiC Content on Microstructure and Properties of In-situ Synthesized WC Reinforced Iron-Based Alloy Coating by Laser Cladding[J]. Materials for mechancial engineering, 2016, 40(10): 15～18
刘海渔,沈言锦. SiC含量对激光熔覆原位合成WC增强铁基合金涂层组织与性能的影响[J]. 机械工程材料, 2016, 40(10): 15～18
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】田浩亮, 魏世丞, 陈永雄,等. 高速电弧喷涂再制造曲轴FeAlCr/3Cr13复合涂层的性能研究［J］. 稀有金属材料与工程, 2014, 43(3): 727-732.
【2】冯继军, 郭文芳. 汽车发动机曲轴常见的失效形式及原因分析［J］. 失效分析与预防, 2006, 1(2): 7-12.
【3】周陆飞. 曲轴气体软氮化冷却介质的改进［J］. 机械工程材料, 2013, 37(4): 47-49.
【4】李养良, 潘东, 甘春飞,等. QT-500球墨铸铁表面激光熔覆镍基合金的组织与性能［J］. 金属热处理, 2012, 37(2): 106-110.
【5】李小泉,吕云飞,赵海新,等.42CrMo钢曲轴断裂失效分析［J］.热加工工艺,2014,43(2): 217-218.
【6】张玉峰, 袁东升, 谢双显, 等. 发动机曲轴药芯焊丝堆焊层及组织结构分析［J］.热加工工艺, 2011, 40(9): 134-136.
【7】史华亮,李继强,贾志欣,等.SKD61模具钢激光仿生强化后的组织和性能［J］. 机械工程材料,2014,38(8): 39-43.
【8】彭亮.激光熔覆在曲轴修复中的应用［J］.装备制造技术,2013(1): 135-136.
【9】邹家龙, 李国松. 激光技术在修复机车柴油机曲轴中的应用［J］. 内燃机车, 2011(11): 47-48.
【10】KOEHLER H, PARTES K, SEEFELD T, et al. Laser reconditioning of crankshafts: from lab to application［J］. Physics Procedia, 2010, 5: 387-397.
【11】XIAO Y F, TAN M, PENG L L, et al. In-situ synthesized WC particles reinforced Fe-based composite coating by argon arc cladding with tungsten powder［J］. Advanced Materials Research, 2013, 712: 378-381.
【12】唐天顺, 龚建勋, 肖逸锋,等. SiC对自保护明弧高铬堆焊合金性能的影响［J］. 材料工程, 2011(10): 61-65.
【13】龚建勋,丁芬,唐天顺,等. 硅对自保护明弧堆焊合金Fe-Cr-C-B显微组织及性能的影响［J］. 焊接学报,2013(7): 17-20.
【14】ZHOU Sheng-feng, ZENG Xiao-yan. Growth characteristics and mechanism of carbides precipitated in WC-Fe composite coatings by laser induction hybrid rapid cladding ［J］. Journal of Alloys and Compounds, 2010, 505(2): 685-691.
【15】龚建勋,许继青,路德斌,等.TiC颗粒对铁-碳-铬-硅合金堆焊层显微组织及耐磨性的影响［J］. 机械工程材料,2015,39(4): 43-47.
【2】冯继军, 郭文芳. 汽车发动机曲轴常见的失效形式及原因分析［J］. 失效分析与预防, 2006, 1(2): 7-12.
【3】周陆飞. 曲轴气体软氮化冷却介质的改进［J］. 机械工程材料, 2013, 37(4): 47-49.
【4】李养良, 潘东, 甘春飞,等. QT-500球墨铸铁表面激光熔覆镍基合金的组织与性能［J］. 金属热处理, 2012, 37(2): 106-110.
【5】李小泉,吕云飞,赵海新,等.42CrMo钢曲轴断裂失效分析［J］.热加工工艺,2014,43(2): 217-218.
【6】张玉峰, 袁东升, 谢双显, 等. 发动机曲轴药芯焊丝堆焊层及组织结构分析［J］.热加工工艺, 2011, 40(9): 134-136.
【7】史华亮,李继强,贾志欣,等.SKD61模具钢激光仿生强化后的组织和性能［J］. 机械工程材料,2014,38(8): 39-43.
【8】彭亮.激光熔覆在曲轴修复中的应用［J］.装备制造技术,2013(1): 135-136.
【9】邹家龙, 李国松. 激光技术在修复机车柴油机曲轴中的应用［J］. 内燃机车, 2011(11): 47-48.
【10】KOEHLER H, PARTES K, SEEFELD T, et al. Laser reconditioning of crankshafts: from lab to application［J］. Physics Procedia, 2010, 5: 387-397.
【11】XIAO Y F, TAN M, PENG L L, et al. In-situ synthesized WC particles reinforced Fe-based composite coating by argon arc cladding with tungsten powder［J］. Advanced Materials Research, 2013, 712: 378-381.
【12】唐天顺, 龚建勋, 肖逸锋,等. SiC对自保护明弧高铬堆焊合金性能的影响［J］. 材料工程, 2011(10): 61-65.
【13】龚建勋,丁芬,唐天顺,等. 硅对自保护明弧堆焊合金Fe-Cr-C-B显微组织及性能的影响［J］. 焊接学报,2013(7): 17-20.
【14】ZHOU Sheng-feng, ZENG Xiao-yan. Growth characteristics and mechanism of carbides precipitated in WC-Fe composite coatings by laser induction hybrid rapid cladding ［J］. Journal of Alloys and Compounds, 2010, 505(2): 685-691.
【15】龚建勋,许继青,路德斌,等.TiC颗粒对铁-碳-铬-硅合金堆焊层显微组织及耐磨性的影响［J］. 机械工程材料,2015,39(4): 43-47.
相关信息