光敏树脂和光固化3D打印技术的发展及应用
Development and Application of Photosensitive Resin and Photo-curing 3D Printing Technology
摘 要
3D打印技术是近些年迅猛发展的一种快速制造技术, 光固化3D打印技术及光敏树脂为3D打印中最为成熟的部分。介绍了光敏树脂的组成及各组分的作用, 简述了几类光固化技术, 并概述了光敏树脂及光固化3D打印技术的研究进展和应用,最后指出光固化3D打印技术正朝着材料多样化、高精度、高速率的方向迅速发展。
光固化
光敏树脂
3D printing
photo-curing
photosensitive resin
Abstract
As one of the rapid prototyping technology, 3D printing technology is developing rapidly in recent years, and photo-curing 3D printing technology and photosensitive resin are the most mature parts of the 3D printing technology. The ingredient of photosensitive resin and the function of each ingredient were introduced, several kinds of photo-curing technologies were sketched, and the research progress and application of photosensitive resin and the photo-curing 3D printing technology were summarized. Finally, it was pointed out that the photo-curing 3D printing technology is developing rapidly in the direction of material diversification, high precision and high rate.
中图分类号 TQ322.4 DOI 10.11973/lhjy-wl201610003
所属栏目 专题报道(3D打印)
基金项目 上海3D打印材料工程技术研究中心资助项目(11DZ2251100)
收稿日期 2016/6/13
修改稿日期
网络出版日期
作者单位点击查看
备注李 振(1991-),男,硕士研究生,主要从事高分子材料改性方面的研究。
引用该论文: LI Zhen,ZHANG Yun-bo,ZHANG Xin-xin,HU Hao,QIAO Wen-yu,GU Zhe-ming. Development and Application of Photosensitive Resin and Photo-curing 3D Printing Technology[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2016, 52(10): 686～689
李振,张云波,张鑫鑫,胡浩,乔雯钰,顾哲明. 光敏树脂和光固化3D打印技术的发展及应用[J]. 理化检验－物理分册, 2016, 52(10): 686～689
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李小丽, 马剑雄,李萍,等.3D打印技术及应用趋势［J］.自动化仪表,2014,35(1): 1-5.
【2】SOOD A K, OHDAR R K, MAHAPATRA S S.Parametric appraisal of mechanical property of fused deposition modelling processed parts［J］.Materials & Design,2010,31(1): 287-295.
【3】刘海涛.光固化三维打印成形材料的研究与应用［D］.武汉: 华中科技大学,2009.
【4】谢彪,王小腾,林润雄,等.光固化3D打印材料［J］.丝网印刷,2014(10): 37-39.
【5】WANG Y Z, WANG A L, BING-SHE X U.Photosensitive resin in stereolithography process［J］.Acta Scientiarum Naturalium Universitatis Sunyatseni,2007.
【6】翟媛萍.光固化快速成型材料的研究与应用［D］.南京: 南京理工大学,2004.
【7】JARIWALA A S, DING F, BODDAPATI A, et al. Modeling effects of oxygen inhibition in mask-based stereolithography［J］.Rapid Prototyping Journal,2011,17(3): 168-175.
【8】TUMBLESTON J R, SHIRVANYANTS D, ERMOSHKIN N, et al. Additive manufacturing: Continuous liquid interface production of 3D objects［J］.Science,2015,347(6228): 1349-1352.
【9】宋晓艳,邢金峰.双光子聚合3D打印［J］.化工学报,2015,66(9): 3324-3332.
【10】谢彪,王小腾,邱俊峰,等.光固化3D打印高分子材料［J］.山东化工,2014(11): 70-72.
【11】李东方,陈继民,袁艳萍,等.光固化快速成型技术的进展及应用［J］.北京工业大学学报,2015,41(12): 1769-1774.
【12】CHANG C J, TZENG H Y.Preparation and properties of waterborne dual curable monomers and cured hybrid polymers for ink-jet applications［J］.Polymer,2006,47(26): 8536-8547.
【13】SERBIN J, GU M.Experimental evidence for superprism effects in three-dimensional polymer photonic crystals［J］.Advanced Materials,2006,18(12): 221-224.
【14】陈小文.快速成型光固化树脂体系的研究［D］.广州: 华南理工大学,2011.
【15】裴文剑.一种应用于DLP3D打印机的新型光敏树脂材料: CN104151526A［P］.2014-11-19.
【16】谢彪.光固化3D打印用光敏树脂的改性［D］.青岛: 青岛科技大学,2015.
【17】翟媛萍.光固化快速成型材料的研究与应用［D］.南京: 南京理工大学,2004.
【18】王广春,袁圆,刘东旭.光固化快速成型技术的应用及其进展［J］.航空制造技术,2011(6): 26-29.
【19】李晓燕.3DP成形技术的机理研究及过程优化［D］.上海: 同济大学,2006.
【20】余东满,朱成俊,曹龙斌,等.光固化快速成型工艺过程分析及应用［J］.机械设计与制造,2011(10): 236-238.
【21】郭长龙,黄蓓青,魏先福.混杂光固化体系在3D打印成型制作柔性版中的应用［C］//2015第十六届中国辐射固化年会暨中国感光学会2015年学术年会论文集.广州: ［出版者不详］,2015: 151-156.
【22】本刊.可乐丽开发出可3D打印的透明柔软光固化弹性体［J］.橡塑技术与装备,2015,41(22): 106.
【23】林润雄,李志乾,马凤国,等.一种紫外光固化3D打印用光敏树脂的制备方法及应用: CN104570603A［P］.2015-04-29.
【24】兰红波,李涤尘,卢秉恒.微纳尺度3D打印［J］.中国科学: 技术科学,2015,45(9): 919-940.
【2】SOOD A K, OHDAR R K, MAHAPATRA S S.Parametric appraisal of mechanical property of fused deposition modelling processed parts［J］.Materials & Design,2010,31(1): 287-295.
【3】刘海涛.光固化三维打印成形材料的研究与应用［D］.武汉: 华中科技大学,2009.
【4】谢彪,王小腾,林润雄,等.光固化3D打印材料［J］.丝网印刷,2014(10): 37-39.
【5】WANG Y Z, WANG A L, BING-SHE X U.Photosensitive resin in stereolithography process［J］.Acta Scientiarum Naturalium Universitatis Sunyatseni,2007.
【6】翟媛萍.光固化快速成型材料的研究与应用［D］.南京: 南京理工大学,2004.
【7】JARIWALA A S, DING F, BODDAPATI A, et al. Modeling effects of oxygen inhibition in mask-based stereolithography［J］.Rapid Prototyping Journal,2011,17(3): 168-175.
【8】TUMBLESTON J R, SHIRVANYANTS D, ERMOSHKIN N, et al. Additive manufacturing: Continuous liquid interface production of 3D objects［J］.Science,2015,347(6228): 1349-1352.
【9】宋晓艳,邢金峰.双光子聚合3D打印［J］.化工学报,2015,66(9): 3324-3332.
【10】谢彪,王小腾,邱俊峰,等.光固化3D打印高分子材料［J］.山东化工,2014(11): 70-72.
【11】李东方,陈继民,袁艳萍,等.光固化快速成型技术的进展及应用［J］.北京工业大学学报,2015,41(12): 1769-1774.
【12】CHANG C J, TZENG H Y.Preparation and properties of waterborne dual curable monomers and cured hybrid polymers for ink-jet applications［J］.Polymer,2006,47(26): 8536-8547.
【13】SERBIN J, GU M.Experimental evidence for superprism effects in three-dimensional polymer photonic crystals［J］.Advanced Materials,2006,18(12): 221-224.
【14】陈小文.快速成型光固化树脂体系的研究［D］.广州: 华南理工大学,2011.
【15】裴文剑.一种应用于DLP3D打印机的新型光敏树脂材料: CN104151526A［P］.2014-11-19.
【16】谢彪.光固化3D打印用光敏树脂的改性［D］.青岛: 青岛科技大学,2015.
【17】翟媛萍.光固化快速成型材料的研究与应用［D］.南京: 南京理工大学,2004.
【18】王广春,袁圆,刘东旭.光固化快速成型技术的应用及其进展［J］.航空制造技术,2011(6): 26-29.
【19】李晓燕.3DP成形技术的机理研究及过程优化［D］.上海: 同济大学,2006.
【20】余东满,朱成俊,曹龙斌,等.光固化快速成型工艺过程分析及应用［J］.机械设计与制造,2011(10): 236-238.
【21】郭长龙,黄蓓青,魏先福.混杂光固化体系在3D打印成型制作柔性版中的应用［C］//2015第十六届中国辐射固化年会暨中国感光学会2015年学术年会论文集.广州: ［出版者不详］,2015: 151-156.
【22】本刊.可乐丽开发出可3D打印的透明柔软光固化弹性体［J］.橡塑技术与装备,2015,41(22): 106.
【23】林润雄,李志乾,马凤国,等.一种紫外光固化3D打印用光敏树脂的制备方法及应用: CN104570603A［P］.2015-04-29.
【24】兰红波,李涤尘,卢秉恒.微纳尺度3D打印［J］.中国科学: 技术科学,2015,45(9): 919-940.
相关信息