X80钢在新疆不同土壤环境中的氢脆行为
Hydrogen Embrittlement Behavior of X80 Steel in Different Xinjiang Soil Environments
摘 要
在外加阴极保护电位下，采用慢应变速率试验、动电位极化方法以及扫描电镜（SEM）观察等方法对比分析了西部管道用大口径X80钢在新疆三种典型土壤模拟溶液中的氢脆行为。结果表明：在外加-1.1 V（CSE）电位条件下，在新疆农田、戈壁和沙漠三种典型土壤的模拟溶液中，X80钢均发生强度和塑性损失，表现出氢脆敏感性；在不同的环境中，随着土壤电导率的增加和pH的降低，X80钢的氢脆敏感性增加。
X80管线钢
氢脆
土壤模拟溶液
cathodic polarization
X80 pipeline steel
hydrogen embrittlement
soil simulation solution
Abstract
Hydrogen embrittlement of large diameter X80 pipeline steel in the simulation solutions of three typical soils in Xinjiang was studied by slow strain rate test (SSRT) with applied potential, SEM and potentiodynamic polarization curve. The results showed that at -1.1 V (CSE) cathodic potential, the strength and plastic deformation losses of X80 steel occurred, indicating the hydrogen embrittlement sensitivity. In different environments, with the increase of soil electrical conductivity and the decrease of pH, hydrogen embrittlement sensitivity of the X80 steel increased.
中图分类号 TG174 DOI 10.11973/fsyfh-201701011
所属栏目 试验研究
基金项目
收稿日期 2015/7/3
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: YANG Yong-he,HU Jiang-feng,DING Rong,WU Jian-cheng,XU Chun-yan,LI Zhen-jun,FANG Wei-lin,SUN Bing-bing,WANG Xiu-yun. Hydrogen Embrittlement Behavior of X80 Steel in Different Xinjiang Soil Environments[J]. Corrosion & Protection, 2017, 38(1): 50
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】褚武扬. 氢损伤与滞后断裂[M]. 北京:冶金工业出版社,1988.
【2】谭文志,杜元龙,傅超,等. 阴极保护导致ZC-120钢在海水中环境氢脆[J]. 材料保护,1988,21(3):10-13.
【3】邱开元, 魏宝明,方耀华. 16Mn钢在3%氯化钠水溶液中的阴极保护及其氢脆敏感性[J]. 南京工业大学学报(自然科学版),1992,14(2):8-14.
【4】王洪仁,曾庆福. 阴极保护电位对921钢海水中应力腐蚀性能影响研究[C]//2004年腐蚀电化学及测试方法学术交流会论文集. 武汉:[出版者不详]. 2004:164-169.
【5】BATT C,DODSON J,ROBINSON M J. Hydrogen embrittlement of cathodically protected high strength in seawater and seabed sediment[J]. British Corrosion Journal,2002,37(3):194-198.
【6】COUDREUSE L,RENAUDIN C,BOCQUET P,et al. Evaluation of hydrogen assisted cracking resistance of high strength jack-up steel[J]. Marine Structures,1997,10(2):85-106.
【7】ONI A. Effects of cathodic overprotection on some mechanical properties of a dual-phaselow-alloy steel in sea water[J]. Construction and Building Materials,1996,10(6):481-484.
【8】郏义征,李辉,胡楠楠,等. 外加阴极电位对X100管线钢近中性pH值应力腐蚀开裂行为的影响[J]. 四川大学学报(工程科学版),2013,45(4):186-191.
【9】王炳英,霍立兴,王东坡,等. X80管线钢在近中性pH溶液中的应力腐蚀开裂[J]. 天津大学学报,2007,40(6):757-760.
【10】PING L,LI X G,DU C W,et al. Stress corrosion cracking of X80 pipeline steel in simulated alkaline soil solution[J]. Materials and Design,2009,30:1712-1717.
【11】刘智勇,王长朋,杜翠薇,等. 外加电位对X80管线钢在鹰潭土壤模拟溶液中应力腐蚀行为的影响[J]. 金属学报,2011,47(11):1434-1439.
【12】翟国丽,刘智勇,杜翠薇,等. 不同组织X70钢在酸性土壤模拟溶液中的应力腐蚀敏感性[J]. 腐蚀与防护,2009,30(3):149-171.
【2】谭文志,杜元龙,傅超,等. 阴极保护导致ZC-120钢在海水中环境氢脆[J]. 材料保护,1988,21(3):10-13.
【3】邱开元, 魏宝明,方耀华. 16Mn钢在3%氯化钠水溶液中的阴极保护及其氢脆敏感性[J]. 南京工业大学学报(自然科学版),1992,14(2):8-14.
【4】王洪仁,曾庆福. 阴极保护电位对921钢海水中应力腐蚀性能影响研究[C]//2004年腐蚀电化学及测试方法学术交流会论文集. 武汉:[出版者不详]. 2004:164-169.
【5】BATT C,DODSON J,ROBINSON M J. Hydrogen embrittlement of cathodically protected high strength in seawater and seabed sediment[J]. British Corrosion Journal,2002,37(3):194-198.
【6】COUDREUSE L,RENAUDIN C,BOCQUET P,et al. Evaluation of hydrogen assisted cracking resistance of high strength jack-up steel[J]. Marine Structures,1997,10(2):85-106.
【7】ONI A. Effects of cathodic overprotection on some mechanical properties of a dual-phaselow-alloy steel in sea water[J]. Construction and Building Materials,1996,10(6):481-484.
【8】郏义征,李辉,胡楠楠,等. 外加阴极电位对X100管线钢近中性pH值应力腐蚀开裂行为的影响[J]. 四川大学学报(工程科学版),2013,45(4):186-191.
【9】王炳英,霍立兴,王东坡,等. X80管线钢在近中性pH溶液中的应力腐蚀开裂[J]. 天津大学学报,2007,40(6):757-760.
【10】PING L,LI X G,DU C W,et al. Stress corrosion cracking of X80 pipeline steel in simulated alkaline soil solution[J]. Materials and Design,2009,30:1712-1717.
【11】刘智勇,王长朋,杜翠薇,等. 外加电位对X80管线钢在鹰潭土壤模拟溶液中应力腐蚀行为的影响[J]. 金属学报,2011,47(11):1434-1439.
【12】翟国丽,刘智勇,杜翠薇,等. 不同组织X70钢在酸性土壤模拟溶液中的应力腐蚀敏感性[J]. 腐蚀与防护,2009,30(3):149-171.
相关信息