Corrosion Reason and Management Advice for Desalination Seawater Piping in a Certain Ship
摘 要
某型舰船淡化海水管路材质为镀锌管,使用一段时间后,镀锌管内部锈蚀严重,管内水质变差。通过腐蚀形貌观察、点蚀深度测量等手段,进行了宏观腐蚀形貌观察;采用荧光光谱、红外光谱和X射线衍射(XRD)等微观分析手段,分析了镀锌管的腐蚀产物成分。结果表明:镀锌管腐蚀类型为局部腐蚀,点蚀严重。镀锌管腐蚀严重的主要原因是淡化海水腐蚀性较强,水质呈弱酸性;管路锈层主要成分为不稳定的γ-FeOOH和Fe3O4,且锈层疏松,不能对底层基体提供保护。建议后期对淡化海水管路的维修更换和设计选材时选用耐蚀性更强的316L不锈钢,且需对淡化海水进行矿化调质。
Abstract
Galvanized steel pipes were used for desalination seawater pipe in a certain type of ship. Galvanized steel pipe internal corrosion was serious and the water quality became bad after a period of time at sea. Through the corrosion morphology observasion and pitting depth measurement, the macroscopic corrosion morphology was observed; using the microscopic analysis methods such as fluorescence, IR and XRD, the corrosion products of galvanized pipe were analyzed. The results show that the galvanized pipe corrosion type is localized corrosion and pitting corrosion is serious. The main reasons for the galvanized pipe corrosion were as follows:firstly, corrosion of the seawater was rather strong and the water quality was in weak acid,secondly, unstable γ-FeOOH and Fe3O4 were main ingredients in the pipe, and rust layer was loose, which provide protection to the underlying substrate. It is suggested that for seawater pipeline replacement and maintenance in the late design, 316L stainless steel with stronger corrosion resistance should be chosen, and mineralization process should be carried out in desalination.
中图分类号 TG172.3 DOI 10.11973/fsyfh-201701012
所属栏目 失效分析
基金项目
收稿日期 2016/3/22
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: WANG Guang-fu,DONG Cai-chang,WU Heng,ZHANG Bo. Corrosion Reason and Management Advice for Desalination Seawater Piping in a Certain Ship[J]. Corrosion & Protection, 2017, 38(1): 54
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王宏义,周东辉,梁沁沁,等. 碳钢在海水及海水淡化一级反渗透产水中的腐蚀行为[J]. 热力发电,2012(7):72-75.
【2】李敬,刘贵昌,王玮,等. 碳钢在反渗透水中耐蚀性研究[J]. 广州化工,2009(4):103-105.
【3】刘栓,孙虎元,范汇吉,等. 镀锌钢腐蚀行为的研究进展[J]. 材料保护,2012(12):50-53.
【2】李敬,刘贵昌,王玮,等. 碳钢在反渗透水中耐蚀性研究[J]. 广州化工,2009(4):103-105.
【3】刘栓,孙虎元,范汇吉,等. 镀锌钢腐蚀行为的研究进展[J]. 材料保护,2012(12):50-53.
相关信息