金属软管点蚀分析
Pitting Analysis of a Flexible Metal Tubing
摘 要
某炼油厂储油罐底翻油用金属软管发生腐蚀泄漏。通过对腐蚀情况宏观形貌和腐蚀发生区域特点的观察，对金属软管内波纹管进行成分分析、金相分析以及对软管内表面腐蚀坑底形貌和腐蚀产物进行扫描电镜和X射线衍射（XRD）分析，确认了发生腐蚀泄漏的原因是在软管内水溶液里浓缩了Cl-，导致了腐蚀穿孔。
形变诱发马氏体
氯离子腐蚀
corrosion perforation
strain induced martensite
chloride corrosion
Abstract
Corrosion leakage of in a refinery storage tank's metal hose occurred. By the observation of the corrosion morphology and characteristics corrosion region, the composition analysis, metallographic analysis, scanning electron microscopy and XRD of the bellow inside the metal hose, it is confirmed that the cause of corrosion leakage was due to the Cl- concentration in aqueous solution inside the hose, which led to corrosion perforation.
中图分类号 TG172 DOI 10.11973/fsyfh-201703018
所属栏目 失效分析
基金项目
收稿日期 2015/9/14
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: WANG Li-kun,ZHOU Yang,WEI Chao,WANG Yan-fang,ZHANG Xue-tao. Pitting Analysis of a Flexible Metal Tubing[J]. Corrosion & Protection, 2017, 38(3): 243
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张绳,张津,郑卉凌,等. 不锈钢波纹管海水腐蚀失效机理对比分析[J]. 腐蚀与防护,2012,33(3):106-109.
【2】盛水平,陈海云,伍红军,等. 基于磁性测定法研究奥氏体不锈钢波纹管的形变马氏体含量[J]. 理化检验-物理分册,2012,48(2):71-75.
【3】有移亮,杨柯,苏梅,等. 波纹管失效分析[J]. 金属热处理,2005,30(3):74-77.
【2】盛水平,陈海云,伍红军,等. 基于磁性测定法研究奥氏体不锈钢波纹管的形变马氏体含量[J]. 理化检验-物理分册,2012,48(2):71-75.
【3】有移亮,杨柯,苏梅,等. 波纹管失效分析[J]. 金属热处理,2005,30(3):74-77.
相关信息