X65管线钢在模拟土壤中的腐蚀行为
Corrosion Behavior of X65 Pipeline Steel in Simulated Soil
摘 要
以华南某地酸性土壤为参考土壤体系，采用硅藻土模拟土壤实验室加速腐蚀法，应用X射线衍射仪、扫描电镜、电化学工作站等系统研究了X65管线钢在模拟土壤腐蚀环境介质中埋地腐蚀不同周期的腐蚀行为。结果表明：在该模拟土壤环境中X65管线钢表面腐蚀形貌由不均匀的点蚀发展为较为均匀的全面腐蚀，电化学极化曲线表现为阳极活化控制，自腐蚀电位出现正移，腐蚀产物主要由α-FeOOH、Fe3O4、Fe2O3等组成。
模拟土壤腐蚀
腐蚀行为
X65 pipeline steel
simulated soil corrosion
corrosion behavior
Abstract
Taking the acidic soil in southern china as a reference, indoor accelerated corrosion testing in simulated acidic soil environment prepared using diatomite was performed. X-ray diffractometer, scanning electron microscopy and electrochemical workstation were used to research the corrosion behavior of X65 pipeline steel buried in simulated soil conosion environment for different periods. The results show that the corrosion morphology of X65 pipeline steel developed from non-uniform pitting corrosion to uniform corrosion in the simulated soil environment. The polarization curves showed an anodic active controlled behavior and the free corrosion potential shifted positivly. The corrosion products were mainly composed of α-FeOOH, Fe3O4 and Fe2O3.
中图分类号 TG174 DOI 10.11973/fsyfh-201705002
所属栏目 管道防护技术
基金项目 陕西电力科学研究院项目（2012037）
收稿日期 2016/10/28
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: WANG Fan,HUANG Tao,CHEN Xiaoping,WANG Xiangdong. Corrosion Behavior of X65 Pipeline Steel in Simulated Soil[J]. Corrosion & Protection, 2017, 38(5): 331
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘智勇,王力伟,杜翠薇,等. Q235钢和X70管线钢在北美山地灰钙土中的短期腐蚀行为[J]. 北京科技大学学报,2013,35(8):1021-1026.
【2】郭晋,廖景娱,刘钧泉,等. 华南酸性土壤对碳钢腐蚀的研究[J]. 广东化工,2001(1):30-32.
【3】余建飞,陈心河,李善风,等. Q235钢在湖北变电站土壤中的腐蚀行为研究[J]. 全面腐蚀控制,2011,25(10):39-45.
【4】LIU Z Y,ZHAI G L,LI X G,et al. Effect of deteriorated microstructures on stress corrosion cracking of X70 pipeline steel in acidic soil environment[J]. Journal Universe Science Technology Beijing,2008,15(6):707.
【5】闫爱军,黄涛. 一种模拟土壤腐蚀过程的加速腐蚀测试方法:CN103308443A[P]. 2013-10-03.
【6】姜玉芝,贾嵩阳. 硅藻土的国内外开发应用现状及进展[J]. 有色矿冶,2011,27(5):31-37.
【7】赵其仁,李林蓓. 硅藻土开发应用及其进展[J]. 化工矿产地质,2005,27(2):96-102.
【8】刘智勇,翟国丽,杜翠薇,等. X70钢在鹰潭酸性土壤中的应力腐蚀行为[J]. 四川大学学报(工程科学版),2008,40(2):76-81.
【9】耿进锋,时洪飞. 变电站接地网腐蚀与防护技术进展[J]. 腐蚀与防护,2009,30(8):522-525.
【10】杜翠薇,李晓刚,武俊伟,等. 三种土壤对X70钢腐蚀行为的比较[J]. 北京科技大学学报,2004,26(5):529-532.
【11】翁永基,李相怡. 土壤中碳钢平均腐蚀速度统计特征的分形研究[J]. 中国腐蚀与防护学报,2005,25(4):200-204.
【12】黄涛,闫爱军,陈小平,等. 含水率对Q235钢在模拟酸性土壤中的腐蚀行为的影响[J]. 腐蚀科学与防护技术,2014,26(6):511.
【13】高磊,吕维玲,曹江利. 埋地热力管线材Q235钢在北京土壤模拟溶液中的腐蚀行为[J]. 材料保护,2012,45(6):54-58.
【14】丁文华,李淼泉. 合金元素和控轧控冷工业在管线钢研制中的应用[J]. 材料导报,2007,21(9):67-70,76.
【15】XIAO F R. Acicular ferrite microstructure of a low carbon Mn-Mo-Nb micro-alloyed pipeline steels[J]. Mater Character,2005,54(3):305.
【16】米丰毅,王向东,汪兵,等. 显微组织对低碳钢耐蚀性的影响[J]. 中国腐蚀与防护学报,2010,30(5):391-395.
【17】汪兵,刘清友,王向东. 晶粒尺寸对超低碳IF钢耐大气腐蚀性能的影响[J]. 金属学报,2012,48(5):601-606.
【18】SARKAR P P,KUMAR P,MANNA M K. Microstructural influence on the electrochemical corrosion behavior of dual-phase steel in 3.5% NaCl solution[J]. Materials Letter,2005,59(19/20):2488-2491.
【19】FU G Y,LIU Q,MEN B J. Effect of microstructure on hot corrosion of Ni-Cr alloys[J]. Rare Metal Materials and Engineering,2007,36(4):695-699.
【20】LI Y,WANG F,LIU G. Grain size effect on the electrochemical corrosion behavior of surface nanocrystallized low-carbon steel[J]. Corrosion,2004,60(10):891-896.
【21】NUNEZ E M,FRANKET G S,KIM Y H. Localized corrosion resistance of 21% Cr ferritic stainless steel[J]. Corrosion,2011,67(9):50051-50058.
【2】郭晋,廖景娱,刘钧泉,等. 华南酸性土壤对碳钢腐蚀的研究[J]. 广东化工,2001(1):30-32.
【3】余建飞,陈心河,李善风,等. Q235钢在湖北变电站土壤中的腐蚀行为研究[J]. 全面腐蚀控制,2011,25(10):39-45.
【4】LIU Z Y,ZHAI G L,LI X G,et al. Effect of deteriorated microstructures on stress corrosion cracking of X70 pipeline steel in acidic soil environment[J]. Journal Universe Science Technology Beijing,2008,15(6):707.
【5】闫爱军,黄涛. 一种模拟土壤腐蚀过程的加速腐蚀测试方法:CN103308443A[P]. 2013-10-03.
【6】姜玉芝,贾嵩阳. 硅藻土的国内外开发应用现状及进展[J]. 有色矿冶,2011,27(5):31-37.
【7】赵其仁,李林蓓. 硅藻土开发应用及其进展[J]. 化工矿产地质,2005,27(2):96-102.
【8】刘智勇,翟国丽,杜翠薇,等. X70钢在鹰潭酸性土壤中的应力腐蚀行为[J]. 四川大学学报(工程科学版),2008,40(2):76-81.
【9】耿进锋,时洪飞. 变电站接地网腐蚀与防护技术进展[J]. 腐蚀与防护,2009,30(8):522-525.
【10】杜翠薇,李晓刚,武俊伟,等. 三种土壤对X70钢腐蚀行为的比较[J]. 北京科技大学学报,2004,26(5):529-532.
【11】翁永基,李相怡. 土壤中碳钢平均腐蚀速度统计特征的分形研究[J]. 中国腐蚀与防护学报,2005,25(4):200-204.
【12】黄涛,闫爱军,陈小平,等. 含水率对Q235钢在模拟酸性土壤中的腐蚀行为的影响[J]. 腐蚀科学与防护技术,2014,26(6):511.
【13】高磊,吕维玲,曹江利. 埋地热力管线材Q235钢在北京土壤模拟溶液中的腐蚀行为[J]. 材料保护,2012,45(6):54-58.
【14】丁文华,李淼泉. 合金元素和控轧控冷工业在管线钢研制中的应用[J]. 材料导报,2007,21(9):67-70,76.
【15】XIAO F R. Acicular ferrite microstructure of a low carbon Mn-Mo-Nb micro-alloyed pipeline steels[J]. Mater Character,2005,54(3):305.
【16】米丰毅,王向东,汪兵,等. 显微组织对低碳钢耐蚀性的影响[J]. 中国腐蚀与防护学报,2010,30(5):391-395.
【17】汪兵,刘清友,王向东. 晶粒尺寸对超低碳IF钢耐大气腐蚀性能的影响[J]. 金属学报,2012,48(5):601-606.
【18】SARKAR P P,KUMAR P,MANNA M K. Microstructural influence on the electrochemical corrosion behavior of dual-phase steel in 3.5% NaCl solution[J]. Materials Letter,2005,59(19/20):2488-2491.
【19】FU G Y,LIU Q,MEN B J. Effect of microstructure on hot corrosion of Ni-Cr alloys[J]. Rare Metal Materials and Engineering,2007,36(4):695-699.
【20】LI Y,WANG F,LIU G. Grain size effect on the electrochemical corrosion behavior of surface nanocrystallized low-carbon steel[J]. Corrosion,2004,60(10):891-896.
【21】NUNEZ E M,FRANKET G S,KIM Y H. Localized corrosion resistance of 21% Cr ferritic stainless steel[J]. Corrosion,2011,67(9):50051-50058.
相关信息