Corrosion Mechanism of Wires Used for Transmission and Transformation Project
摘 要
在某输电线路工程现场用导线发生大面积腐蚀,腐蚀产物为白色胶状细颗粒。采用理化分析、试验模拟等方法对腐蚀产物及导线接触物进行分析,并探究腐蚀机理。结果表明:Cl是导致导线腐蚀的主要元素,导线中弥散分布的第二相粒子加速了腐蚀进程。据此,提出了导线在加工制造、运输存贮及使用过程中避免腐蚀的方法。
Abstract
Serious corrosion of wires used in a transmission project appeared. The corrosion product was white colloidal fine particles. The composition of corrosion products and mechanism of corrosion were explored by means of physical and chemical analysis and simulation test. The results show that Cl was the main element leading to the corrosion of the wire, and the second phase particles dispersed in the wire accelerated the corrosion process. Accordingly, some suggestions for avoiding the wire corrosion in the process of manufacture, transport and use were proposed.
中图分类号 TG115.2 DOI 10.11973/fsyfh-201705019
所属栏目 失效分析
基金项目
收稿日期 2017/3/16
修改稿日期
网络出版日期
作者单位点击查看
联系人作者张旭(jancy001@126.com)
引用该论文: ZHANG Xu,ZHAO Jingfeng,LI Yiwen,LI Junbo,WANG Jingyi,LIU Enjing. Corrosion Mechanism of Wires Used for Transmission and Transformation Project[J]. Corrosion & Protection, 2017, 38(5): 403
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB/T 3190-2008变形铝合金及铝合金化学成分[S].
【2】郑艺,郭伟,丁洪生,等. 不同状态AZ80镁合金的金相试样制备方法[J]. 理化检验-物理分册,2015,51(7):477-479.
【3】李劲风. 第二相在铝合金局部腐蚀中的作用机制腐蚀[J]. 材料导报,2005,19(2):81-83.
【4】马腾,王振尧,韩薇. 铝和铝合金的大气腐蚀[J]. 腐蚀科学与防护技术,2004,16(3):156-161.
【2】郑艺,郭伟,丁洪生,等. 不同状态AZ80镁合金的金相试样制备方法[J]. 理化检验-物理分册,2015,51(7):477-479.
【3】李劲风. 第二相在铝合金局部腐蚀中的作用机制腐蚀[J]. 材料导报,2005,19(2):81-83.
【4】马腾,王振尧,韩薇. 铝和铝合金的大气腐蚀[J]. 腐蚀科学与防护技术,2004,16(3):156-161.
相关信息