Effects of Two Water Treatment Processes on Corrosion of Recycled Water Pipeline
摘 要
基于某再生水厂现有水处理工艺,对其混凝沉淀和消毒工艺进行优化,通过挂片失重试验、扫描电镜(SEM)观察和X射线衍射(XRD)分析对比研究了两种再生水处理工艺对管网腐蚀的影响。结果表明:优化工艺出水的Larson指数和微生物活性比原工艺出水的显著降低,金属表面腐蚀层呈光滑晶态状,在优化工艺产出的再生水中,对管体起到保护作用的CaCO3层从腐蚀初期就开始形成并贯穿整个腐蚀过程中,使再生水管网的腐蚀情况得到缓解,因此优化工艺可有效地缓解铸铁管网的腐蚀。
Abstract
Based on the existing treatment process of a recycling plant, the flocculation and disinfection processes were optimized. The effects of two kinds of reclaimed water treatment processes on the corrosion of pipe network were analyzed by weight-loss method, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results show that the Larson index and microbial activity of the effluent from the optimization process were significantly reduced in comparison with the old process, and the corrosion surface was smooth and crystalline. The CaCO3 layer alleviating the corrosion of cast iron pipe network formed from the beginning of corrosion to the whole corrosion process.Therefore the optimization process can effectively alleviate the corrosion of cast iron pipe network.
中图分类号 TG174 DOI 10.11973/fsyfh-201706001
所属栏目 试验研究
基金项目 国家自然科学基金(51678026)
收稿日期 2016/10/31
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: FENG Cuimin,JIN Jiyue,WANG Changzheng,ZHANG Jiong,ZHANG Xinrui,LIU Dandan,LIU Yongjun. Effects of Two Water Treatment Processes on Corrosion of Recycled Water Pipeline[J]. Corrosion & Protection, 2017, 38(6): 411
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李昆,刘艳飞,彭东明,等. 再生水回用的标准比较与技术经济分析[J]. 环境科学学报,2014,34(7):1635-1653.
【2】康为民,时厉杰,赵有璟,等. 水处理中膜分离技术的应用[J]. 无机盐工业,2014,46(5):6-9.
【3】孟瑞明,梁小田,吕志成,等. 微滤-反渗透双膜工艺在再生水工程中的应用研究[J]. 给水排水,2012,38(S2):83-86.
【4】冯运玲,戴前进,李艺,等. 几种典型再生水处理工艺出水水质对比分析[J]. 给水排水,2011,37(2):47-49.
【5】刘星飞,田一梅,郭浩,等. 球墨铸铁给水管道内腐蚀实验研究[J]. 腐蚀科学与防护技术,2015,27(5):459-462.
【6】吴卿,李云,李亚男,等. 再生水用于循环冷却水中铁细菌对碳钢腐蚀的影响[J]. 天津工业大学学报,2014,33(4):40-44.
【7】崔勇,于康华,张子潇,等. 铸铁管输配再生水铁溶出颗粒物特征研究[J]. 环境科学学报,2016,38(8):2932-2940.
【8】方伟,许仕荣,徐洪福,等. 城市供水管网水质化学稳定性研究进展[J]. 中国给水排水,2006,22(14):10-13.
【9】SAREMI M,DEHGHANIAN C,SABET M M. The effect of molybdate concentration and hydrodynamic effect on mild steel corrosion inhibition in simulated cooling water[J]. Corrosion Science,2006,48(6):1404-1409.
【10】应一梅,周瑞云,杨崇豪,等. 循环冷却水输水管壁生物膜生长发育及微生物腐蚀问题研究[J]. 给水排水,2008,34(6):117-121.
【11】冯萃敏,刘丹丹,米楠,等. 基于降低拉森指数的再生水混凝处理工艺优化研究[J]. 工业水处理,2015,35(12):48-52.
【12】甘庆午,吴珊,厉智成. 再生水对钢管与球墨铸铁管的腐蚀研究[J]. 南水北调与水利科技,2014,12(2):181-184.
【13】潘一,孙林,杨双春,等. 国内外管道腐蚀与防护研究进展[J]. 腐蚀科学与防护技术,2014,26(1):77-80.
【14】PENG C Y,JOHN F,FERGUSON,et al. Effects of chloride,sulfate and natural organic matter (NOM) on the accumulation and release of trace-level inorganic contaminants from corroding iron[J]. Water Research,2013,47(14):5257-5269.
【15】王洋,张晓健,陈超,等. 水源切换引起给水管网黄水问题原因分析[J]. 环境科学,2009,30(12):3555-3561.
【2】康为民,时厉杰,赵有璟,等. 水处理中膜分离技术的应用[J]. 无机盐工业,2014,46(5):6-9.
【3】孟瑞明,梁小田,吕志成,等. 微滤-反渗透双膜工艺在再生水工程中的应用研究[J]. 给水排水,2012,38(S2):83-86.
【4】冯运玲,戴前进,李艺,等. 几种典型再生水处理工艺出水水质对比分析[J]. 给水排水,2011,37(2):47-49.
【5】刘星飞,田一梅,郭浩,等. 球墨铸铁给水管道内腐蚀实验研究[J]. 腐蚀科学与防护技术,2015,27(5):459-462.
【6】吴卿,李云,李亚男,等. 再生水用于循环冷却水中铁细菌对碳钢腐蚀的影响[J]. 天津工业大学学报,2014,33(4):40-44.
【7】崔勇,于康华,张子潇,等. 铸铁管输配再生水铁溶出颗粒物特征研究[J]. 环境科学学报,2016,38(8):2932-2940.
【8】方伟,许仕荣,徐洪福,等. 城市供水管网水质化学稳定性研究进展[J]. 中国给水排水,2006,22(14):10-13.
【9】SAREMI M,DEHGHANIAN C,SABET M M. The effect of molybdate concentration and hydrodynamic effect on mild steel corrosion inhibition in simulated cooling water[J]. Corrosion Science,2006,48(6):1404-1409.
【10】应一梅,周瑞云,杨崇豪,等. 循环冷却水输水管壁生物膜生长发育及微生物腐蚀问题研究[J]. 给水排水,2008,34(6):117-121.
【11】冯萃敏,刘丹丹,米楠,等. 基于降低拉森指数的再生水混凝处理工艺优化研究[J]. 工业水处理,2015,35(12):48-52.
【12】甘庆午,吴珊,厉智成. 再生水对钢管与球墨铸铁管的腐蚀研究[J]. 南水北调与水利科技,2014,12(2):181-184.
【13】潘一,孙林,杨双春,等. 国内外管道腐蚀与防护研究进展[J]. 腐蚀科学与防护技术,2014,26(1):77-80.
【14】PENG C Y,JOHN F,FERGUSON,et al. Effects of chloride,sulfate and natural organic matter (NOM) on the accumulation and release of trace-level inorganic contaminants from corroding iron[J]. Water Research,2013,47(14):5257-5269.
【15】王洋,张晓健,陈超,等. 水源切换引起给水管网黄水问题原因分析[J]. 环境科学,2009,30(12):3555-3561.
相关信息