镁对新型合金镀层金属液抗高温氧化性能的影响
Effect of Magnesium on High Temperature Oxidation Resistance of Molten Metal of a New Type Alloy Coating
摘 要
通过对新型合金镀层金属液（以下称合金液）氧化试验后宏观状态、微观形貌观察，结合X射线衍射（XRD）及能谱分析，研究分析了镁对该合金液氧化行为的影响。结果表明：镁对该合金液的氧化行为影响显著，铝含量一定时，随着镁含量增加，合金液的抗高温氧化性能明显变差，且氧化层呈规律性增加，超过一定含量后严重影响镀层表面质量。
抗高温氧化性能
热浸镀
表面质量
表面形貌
alloy coating
high temperature oxidation resistance
hot dip galvanizing
surface quality
surface morphology
Abstract
The effect of Mg on the oxidation behavior of new alloy baths was studied by observing the macro-state and micro-morphology of molten metal of a new alloy coating (molten alloy) after oxidation test, combing with X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS) analyses. The results show that Mg had a significant effect on the oxidation behavior of the molten alloy. The high temperature oxidation resistance of the molten alloy became worse and the oxide layer increased regularly with the increase of Mg content, when the aluminum content was constant. The surface quality of the alloy coating was seriously affected when the Mg content exceeded a certain amount.
中图分类号 TG174 DOI 10.11973/fsyfh-201706006
所属栏目 试验研究
基金项目
收稿日期 2017/1/7
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: YU Wugang,LIU Xin,LIU Canlou,JIANG Sheming,ZHANG Qifu. Effect of Magnesium on High Temperature Oxidation Resistance of Molten Metal of a New Type Alloy Coating[J]. Corrosion & Protection, 2017, 38(6): 434
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】樊志彬,李辛庚. 输电杆塔钢构件腐蚀防护技术现状和发展趋势[J]. 山东电力技术,2013,191(1):30-34.
【2】陈云,徐利民,药宁娜,等. 输变电钢构件的大气腐蚀与防护[J]. 华北电力技术,2014(12):10-14.
【3】陈军君,胡加瑞,谢亿,等. 典型工业区输变电线路金具腐蚀失效分析[J]. 腐蚀科学与防护技术,2013,25(6):508-513.
【4】陈彤,谈天,洪毅成,等. 输电网镀锌金属部件的腐蚀与防护[J]. 中国电力,2013(11):1-7.
【5】胡俊鹏,李辛庚,岳增武,等. 输变电钢构件热镀锌防腐效果调查分析[J]. 腐蚀科学与防护技术,2014,26(6):567-570.
【6】马承志,杨宏仓,梁位正,等. 沿海地区输电铁塔防腐方法对比分析[J]. 机电工程技术,43(12):141-144.
【7】张启富,刘邦津,黄建中. 现代钢带连续热镀锌[M]. 北京:冶金工业出版社,2007.
【8】李铁蕃. 金属高温氧化和热腐蚀[M]. 北京:化学工业出版社,2003.
【9】樊建峰,杨根仓,周尧和,等. 纯镁的高温氧化特性[J]. 铸造技术,2006,27(6):605-608.
【10】潘娜. 镁铝合金高温氧化动力学及氧化过程研究[D]. 太原:太原理工大学,2012.
【11】章小鸽. 锌的腐蚀与电化学[M]. 北京:冶金工业出版社,2008.
【12】卢锦堂,许乔瑜,孔纲. 热浸镀技术与应用[M]. 北京:机械工业出版社,2006.
【13】黎文献. 镁及镁合金[M]. 长沙:中南工业大学出版社,2006:15-20.
【14】王雪敏. 镁合金高温氧化及表面改性研究[D]. 上海:上海交通大学,2007.
【15】SULLIVAN J,MEHRABAN S,ELVINS J. In situ monitoring of the microsturctural corrosion mechanisms of Zinc-magnesium-aluminium galvanizing alloys using time lapse microscopy[J]. Corrosion Science,2011,53(6):2208-2215.
【16】刘灿楼. 输变电钢构件新型高耐蚀热浸镀锌合金镀层的研究[D]. 北京:钢铁研究总院,2016.
【17】PROSEK T,DAN P,STOULIL J,et al. Composition of corrosion products formed on Zn-Mg,Zn-Al and Zn-Al-Mg coatings in model atmospheric conditions[J]. Corrosion Science,2014,86(8):231-238.
【18】ANGELI G,BRISBERGER R,BULTER M,et al. Zinc-magnesium-aluminium for atomotive industry[C]//Galvatech 2013.[S.l.]:[s.n.],2013:632-636.
【2】陈云,徐利民,药宁娜,等. 输变电钢构件的大气腐蚀与防护[J]. 华北电力技术,2014(12):10-14.
【3】陈军君,胡加瑞,谢亿,等. 典型工业区输变电线路金具腐蚀失效分析[J]. 腐蚀科学与防护技术,2013,25(6):508-513.
【4】陈彤,谈天,洪毅成,等. 输电网镀锌金属部件的腐蚀与防护[J]. 中国电力,2013(11):1-7.
【5】胡俊鹏,李辛庚,岳增武,等. 输变电钢构件热镀锌防腐效果调查分析[J]. 腐蚀科学与防护技术,2014,26(6):567-570.
【6】马承志,杨宏仓,梁位正,等. 沿海地区输电铁塔防腐方法对比分析[J]. 机电工程技术,43(12):141-144.
【7】张启富,刘邦津,黄建中. 现代钢带连续热镀锌[M]. 北京:冶金工业出版社,2007.
【8】李铁蕃. 金属高温氧化和热腐蚀[M]. 北京:化学工业出版社,2003.
【9】樊建峰,杨根仓,周尧和,等. 纯镁的高温氧化特性[J]. 铸造技术,2006,27(6):605-608.
【10】潘娜. 镁铝合金高温氧化动力学及氧化过程研究[D]. 太原:太原理工大学,2012.
【11】章小鸽. 锌的腐蚀与电化学[M]. 北京:冶金工业出版社,2008.
【12】卢锦堂,许乔瑜,孔纲. 热浸镀技术与应用[M]. 北京:机械工业出版社,2006.
【13】黎文献. 镁及镁合金[M]. 长沙:中南工业大学出版社,2006:15-20.
【14】王雪敏. 镁合金高温氧化及表面改性研究[D]. 上海:上海交通大学,2007.
【15】SULLIVAN J,MEHRABAN S,ELVINS J. In situ monitoring of the microsturctural corrosion mechanisms of Zinc-magnesium-aluminium galvanizing alloys using time lapse microscopy[J]. Corrosion Science,2011,53(6):2208-2215.
【16】刘灿楼. 输变电钢构件新型高耐蚀热浸镀锌合金镀层的研究[D]. 北京:钢铁研究总院,2016.
【17】PROSEK T,DAN P,STOULIL J,et al. Composition of corrosion products formed on Zn-Mg,Zn-Al and Zn-Al-Mg coatings in model atmospheric conditions[J]. Corrosion Science,2014,86(8):231-238.
【18】ANGELI G,BRISBERGER R,BULTER M,et al. Zinc-magnesium-aluminium for atomotive industry[C]//Galvatech 2013.[S.l.]:[s.n.],2013:632-636.
相关信息