Hardness and Residual Stress of Near Surface of Bearing Rings with Different Treatment Processes
摘 要
对M50钢轴承套圈、M50NiL钢渗碳轴承套圈及M50NiL钢渗碳+渗氮复合化学热处理轴承套圈的显微组织、硬度及残余应力进行了测试及分析,并对M50钢轴承套圈和M50NiL钢渗碳轴承套圈进行了硬度、应力和寿命耐久性试验。结果表明:复合化学热处理后,M50NiL钢轴承套圈的表面及心部硬度比M50NiL钢渗碳轴承套圈的有所提高,其表面应力尤其是次表层应力有了极大提高,因此耐磨性和抗疲劳性能也得到极大的改善;M50NiL钢渗碳轴承套圈的抗疲劳性能及使用寿命比M50钢轴承套圈的提高了3~5倍。
Abstract
The microstructure, hardness and residual stress of M50 steel bearing rings, carburized M50NiL steel bearing rings and M50NiL steel bearing rings after compound chemical heat treatment of carburization and nitridation were tested and analyzed. The hardness tests, stress tests and life durability tests were carried out on M50 steel bearing rings and carburized M50NiL steel bearing rings. The results show that:after compound chemical heat treatment, the hardness of surface and core of M50NiL steel bearing rings was improved compared with that of carburized M50NiL steel bearing rings, and the surface stress especially the subsurface stress was greatly improved, as a result, the abrasion resistance and fatigue properties were also greatly improved; the fatigue resistance and service life of carburized M50NiL steel bearing rings were enhanced by 3 to 5 times compared with those of M50 steel bearing rings.
中图分类号 TH133.3 DOI 10.11973/lhjy-wl201707005
所属栏目 专题报道(残余应力)
基金项目
收稿日期 2016/6/13
修改稿日期
网络出版日期
作者单位点击查看
备注罗燕(1965-),女,高级工程师,工学学士,主要从事残余应力和残余奥氏体检测工作,luoyan2286@126.com
引用该论文: LUO Yan,LIU Yixiang,BAN Jun,LIU Xiulian. Hardness and Residual Stress of Near Surface of Bearing Rings with Different Treatment Processes[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2017, 53(7): 477~481
罗燕,刘义翔,班君,刘秀莲. 不同处理工艺轴承套圈的近表层硬度及残余应力[J]. 理化检验-物理分册, 2017, 53(7): 477~481
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】SADEGHI F, ARAKERE N K, JALALAHMADI B, et al. A review of rolling contact fatigue[J]. Journal of Tribology, 2009,131(4):220.
【2】于芸,朱光辉.Cr4Mo4V钢制轴承套圈磨削变质层深度的测定[J].理化检验-物理分册,2011,47(5):270-273.
【3】张亦良,张振海,刘金艳.不同喷丸工艺下残余应力沿深度的分布规律[J].北京工业大学学报,2009,35(12):1585-1590.
【4】王炳方,赵振业,贺自强,等.声学法评定M50NiL/M50轴承钢的弹性模量[J].金属热处理,2013,38(6):54-57.
【5】王冠.M50NiL钢氮碳共渗与渗碳加渗氮复合改性层的组织与性能[D].哈尔滨:哈尔滨工业大学,2014.
【6】孙湛.M50NiL钢等离子体稀土渗氮/氮碳共渗层组织结构与性能研究[D].哈尔滨:哈尔滨工业大学,2013.
【2】于芸,朱光辉.Cr4Mo4V钢制轴承套圈磨削变质层深度的测定[J].理化检验-物理分册,2011,47(5):270-273.
【3】张亦良,张振海,刘金艳.不同喷丸工艺下残余应力沿深度的分布规律[J].北京工业大学学报,2009,35(12):1585-1590.
【4】王炳方,赵振业,贺自强,等.声学法评定M50NiL/M50轴承钢的弹性模量[J].金属热处理,2013,38(6):54-57.
【5】王冠.M50NiL钢氮碳共渗与渗碳加渗氮复合改性层的组织与性能[D].哈尔滨:哈尔滨工业大学,2014.
【6】孙湛.M50NiL钢等离子体稀土渗氮/氮碳共渗层组织结构与性能研究[D].哈尔滨:哈尔滨工业大学,2013.
相关信息