油气长输管道裂纹缺陷产生原因

油气长输管道裂纹缺陷产生原因

The Causes of Crack Defects in Long Distance Oil and Gas Pipeline

张辉宇

张瑞轩

摘要

介绍了油气长输管道检测中发现的多种类型裂纹，通过冶炼过程分析、定量光谱分析及金相分析，查出了裂纹的产生原因，为长输管道质量提供了有力保障。

标签冷裂纹

热裂纹

延迟裂纹

定量光谱分析

非金属夹渣物

焊接工艺评定

cold crack

hot crack

delay crack

quantitative spectral analysis

nonmetal slag inclusion

welding procedure of specification

Abstract

The detection of various types of cracks in long distance pipeline is introduced, through the analysis of smelting process, quantative spectral analysis and metallographic analysis, the causes resulting in the cracks are analyzed, and the corresponding treatment is carried out. It provides a strong guarantee of quality for the long distance pipeline.

中图分类号 TG115.28 DOI 10.11973/wsjc201707017

所属栏目实践经验

基金项目

收稿日期 2016/9/12

修改稿日期

网络出版日期

作者单位点击查看

联系人作者张辉宇(zhanghuiyu1970@163.com)

备注张辉宇(1970-),男,高级工程师,主要从事无损检测工作

引用该论文: ZHANG Huiyu,ZHANG Ruixuan. The Causes of Crack Defects in Long Distance Oil and Gas Pipeline[J]. Nondestructive Testing, 2017, 39(7): 73～75
张辉宇,张瑞轩. 油气长输管道裂纹缺陷产生原因[J]. 无损检测, 2017, 39(7): 73～75

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

参考文献

【1】王晓雷.承压类特种设备无损检测相关知识[M]. 北京:中国劳动社会保障出版社,2007.

【2】ASME V 2013 Nondestructive testing[S].

相关信息

	标题	相关频次
	15CrMoR钢焊接冷裂纹的磁记忆特性	2
	16MnD5钢板焊接件热影响区开裂原因分析	2
	CR检测技术在长输管道上的应用	2
	X80钢输气管道带缺陷环焊缝的力学性能及两类裂纹形成原因	2
	不同焊丝MAG焊接新型超高强度钢接头的显微组织及性能	2
	集箱管接座角焊缝缺陷浅析及返修处理	2
	炉底辊堆焊修复用不锈钢药芯焊丝的研制	2
	汽车变速操纵杆焊接接头冷裂纹产生原因分析	2
	汽车用U型螺栓断裂分析	2
	游梁式抽油机悬绳器焊接裂纹的探讨	2
	主蒸汽压力取样管焊接接头开裂原因	2
	06Ni9DR钢焊接对接接头的超声检测	1
	06Ni9DR钢焊接对接接头的射线底片评定	1
	1.25Cr0.5MoSi钢的焊接工艺评定	1
	2101双相不锈钢的焊接性能和焊接技术	1
	300 MW机组回转式空气预热器仓格板开裂原因分析	1
	变速箱悬置支臂断裂原因	1
	不锈钢管道对接焊缝焊接热裂纹超声波检测技术	1
	超声场对半连续铸造铝合金铸锭热裂纹形成的影响机理	1
	给水管座开裂原因分析	1
	焊接工艺评定试验国内外标准对比解析	1
	焊接冷裂纹起裂及扩展过程的声发射特性	1
	机车轮箍崩裂原因分析	1
	偏析对S690高强度无缝钢管性能的影响	1
	热裂纹的主要产生原因及预防措施	1
	支撑轴断裂原因分析	1
	注水井口卡箍的断裂分析	1
	铸钢件摇臂裂纹原因分析及改进	1