地铁道岔滑床板断裂失效分析
Failure Analysis on Fracture of the Slide Plate of a Metro Turnout
摘 要
采用断口宏微观分析、化学成分分析、金相检验、硬度测试等方法对某地铁道岔滑床板断裂的原因进行了分析。结果表明：滑床板失效模式属于疲劳断裂，焊接工艺不当导致焊缝位置晶粒粗大、硬度偏低以及存在应力集中等是其发生疲劳断裂的主要原因，并由此提出了改进措施。
焊缝
疲劳断裂
焊接工艺
应力集中
slide plate
weld seam
fatigue fracture
welding procedure
stress concentration
Abstract
By means of macro and micro fracture analysis, chemical composition analysis, metallographic examination and hardness test, the fracture reasons of the slide plate of a metro turnout were analyzed. The results show that the failure mode of the slide plate was fatigue fracture. The coarse grain and lower hardness of the weld seam caused by the improper welding procedure, as well as the stress concentration at root of the weld seam, were main reasons for the fatigue fracture. Finally, the corresponding improvement measures were put forward.
中图分类号 U214.8+1 DOI 10.11973/lhjy-wl201708013
所属栏目 质量控制与失效分析
基金项目
收稿日期 2016/5/11
修改稿日期
网络出版日期
作者单位点击查看
备注李二勇(1977-),男,工程师,硕士,主要从事机电产品失效分析工作,legent@yeah.net
引用该论文: LI Eryong,WANG Jian,ZHANG Yiliang. Failure Analysis on Fracture of the Slide Plate of a Metro Turnout[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2017, 53(8): 595～598
李二勇,王建,张奕梁. 地铁道岔滑床板断裂失效分析[J]. 理化检验－物理分册, 2017, 53(8): 595～598
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张建国.铁路道岔滑床板断裂分析[J].理化检验-物理分册,2011,47(9):583-585,588.
【2】陈海田.50 kg/m武钢U71Mn钢轨闪光焊接性能探讨[J].山东工业技术,2016(13):30.
【3】李大东,龚利军,余腾义,等.PG4钢轨闪光焊接头落锤断裂原因分析[C]//第九届中国钢铁年会论文集.北京:[出版者不详],2013:1-7.
【4】鲍磊,韩自力,张银花,等.高速铁路钢轨质量评估[J].中国冶金,2014,24(11):9-13.
【2】陈海田.50 kg/m武钢U71Mn钢轨闪光焊接性能探讨[J].山东工业技术,2016(13):30.
【3】李大东,龚利军,余腾义,等.PG4钢轨闪光焊接头落锤断裂原因分析[C]//第九届中国钢铁年会论文集.北京:[出版者不详],2013:1-7.
【4】鲍磊,韩自力,张银花,等.高速铁路钢轨质量评估[J].中国冶金,2014,24(11):9-13.
相关信息