Microstructure and Mechanical Properties of Bobbin Friction Stir Welded Joint of 5 mm Thick 6082-T6 Aluminum Alloy
摘 要
采用双轴肩搅拌摩擦焊技术对5 mm厚6082-T6铝合金板进行了对接焊,研究了接头的显微组织与力学性能。结果表明:在主轴转速为500 r·min-1、焊接速度为400 mm·min-1条件下焊接后,接头的组织致密,焊核区晶粒细小均匀,热机影响区的晶粒变得狭长,热影响区晶粒粗化;接头的抗拉强度和屈服强度分别为232.75,161.04 MPa,均略低于母材的(272,229 MPa),其弯曲性能合格;显微硬度呈W形分布,硬度最小值出现在前进侧热影响区,为67 HV,焊核区的硬度为77.6 HV。
Abstract
5 mm thick 6082-T6 aluminum alloy plates were butt-welded using the bobbin friction stir welding technique and the microstructure and mechanical properties of the joint were studied. The results show that after welding at the spindle speed of 500 r·min-1 and welding speed of 400 mm·min-1, the microstructure of the joint was dense. The grains in weld nugget zone was fine and even, while in the thermo-mechanical affected zone became long and narrow and in the heat affected zone became coarse. The tensile strength and yield strength of the joint was 232.75, 161.04 MPa, respectively, which were slightly lower than those (272,229 MPa, respectively) of base metal. The bending performance of the joint was qualified. The microhardness showed the W-shape distribution and the lowest value of the hardness appeared in the heat affected zone at the forward side, which was 67 HV. The hardness of the weld nugget zone was 77.6 HV.
中图分类号 TG453 DOI 10.11973/jxgccl201708015
所属栏目 材料性能及应用
基金项目 北京航空制造工程研究所新技术开发项目(2015-RE01)
收稿日期 2016/7/18
修改稿日期 2017/6/13
网络出版日期
作者单位点击查看
备注林松(1987-),男,河北廊坊人,工程师,硕士
引用该论文: LIN Song,ZHANG Kun,WANG Weibing,LUAN Guohong. Microstructure and Mechanical Properties of Bobbin Friction Stir Welded Joint of 5 mm Thick 6082-T6 Aluminum Alloy[J]. Materials for mechancial engineering, 2017, 41(8): 67~69
林松,张坤,王卫兵,栾国红. 5 mm厚6082-T6铝合金双轴肩搅拌摩擦焊接头的组织与性能[J]. 机械工程材料, 2017, 41(8): 67~69
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘杰, 邓钢, 韩凤武, 等.双轴肩搅拌摩擦焊技术在铝合金车体制造中的应用发展[J]. 焊接, 2015(1):17-20.
【2】董继红,董春林,孟强,等.铝合金浮动式双轴肩FSW接头组织性能分析[J]. 焊接学报, 2013, 34(10):43-46.
【3】苏斌,贺地求,杨坤玉,等.3 mm厚6061铝合金板固定双轴肩搅拌摩擦焊接头的显微组织与拉伸性能[J].机械工程材料, 2013, 37(9):41-44.
【4】北京赛福斯特技术有限公司.世界级先进焊接技术创新突破——北京赛福斯特公司全面实现"浮动式"双轴肩搅拌摩擦焊接[J]. 现代焊接, 2011(2):32-33.
【5】张会杰,王敏, 张骁, 等.铝合金双轴肩搅拌摩擦焊特征及接头组织性能分析[J].焊接学报, 2015, 36(12):65-68.
【6】张健, 李光, 李从卿,等. 2219-T4铝合金双轴肩FSW与常规FSW接头性能对比研究[J].焊接,2008(11):50-52.
【7】董春林,董继红, 赵华夏,等. 6082铝合金双轴肩FSW接头组织及腐蚀性能[J]. 焊接学报, 2012, 33(10):5-9.
【2】董继红,董春林,孟强,等.铝合金浮动式双轴肩FSW接头组织性能分析[J]. 焊接学报, 2013, 34(10):43-46.
【3】苏斌,贺地求,杨坤玉,等.3 mm厚6061铝合金板固定双轴肩搅拌摩擦焊接头的显微组织与拉伸性能[J].机械工程材料, 2013, 37(9):41-44.
【4】北京赛福斯特技术有限公司.世界级先进焊接技术创新突破——北京赛福斯特公司全面实现"浮动式"双轴肩搅拌摩擦焊接[J]. 现代焊接, 2011(2):32-33.
【5】张会杰,王敏, 张骁, 等.铝合金双轴肩搅拌摩擦焊特征及接头组织性能分析[J].焊接学报, 2015, 36(12):65-68.
【6】张健, 李光, 李从卿,等. 2219-T4铝合金双轴肩FSW与常规FSW接头性能对比研究[J].焊接,2008(11):50-52.
【7】董春林,董继红, 赵华夏,等. 6082铝合金双轴肩FSW接头组织及腐蚀性能[J]. 焊接学报, 2012, 33(10):5-9.
相关信息