Effect of Temperature on Pitting Corrosion Behavior of the 904L Stainless Steel
摘 要
采用FeCl3溶液浸泡试验、动电位极化、电化学阻抗谱及体式显微镜研究了904L超级奥氏体不锈钢在不同温度下的点蚀行为。结果表明:溶液温度为25℃时,904L不锈钢具有优异的耐点蚀性能,随着溶液温度的升高,其耐点蚀性能下降,在65℃ FeCl3溶液中基体表面产生严重的点蚀坑。在不同温度模拟海水溶液中的电化学测试结果同样表明:随着试验温度的提高,自腐蚀电流密度增大,点蚀电位下降,点蚀敏感性提高;EIS均为单一的容抗弧,温度升高,容抗弧半径减小,材料腐蚀速率增大,耐蚀性降低。
Abstract
The pitting corrosion behavior of 904L super austenitic stainless steel at different temperatures was studied by pitting test of FeCl3 solution, potentiodynamic polarization and stereo microscopy. The results showed that 904L stainless steel had excellent pitting corrosion resistance at room temperature, with the increase of test temperature, the pitting corrosion resistance of 904L stainless steel decreased. In the FeCl3 solution at 65℃, serious pitting corrosion holes were found on the surface of tested 904L matrix. The results of the electrochemical test also showed that as the temperature increased, the pitting potential decreased, EIS presented as single capacitive arc, and the radius of the arc also decreased, which indicated the corrosion rate increased and the corrosion resistance decreased.
中图分类号 TG174 DOI 10.11973/fsyfh-201709006
所属栏目 试验研究
基金项目
收稿日期 2017/6/6
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: WANG Shaowei,HUANG Dejun,LI Chengtao,DONG Shuai,LUO Yue,FANG Kewei. Effect of Temperature on Pitting Corrosion Behavior of the 904L Stainless Steel[J]. Corrosion & Protection, 2017, 38(9): 689
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】向嵩,曾洪涛,杨阳,等. 浓硫酸中904L不锈钢焊接接头的耐蚀性能[J]. 北京科技大学学报,2014,36(1):69-73.
【2】顾伟,杨明. 904L和CD4MCu不锈钢在硫酸中的腐蚀行为[J]. 贵州化工,2012,37(6):7-9.
【3】曾洪涛,向嵩,刘松林,等. 904L不锈钢在氢氟酸和浓硫酸混合液中的腐蚀行为[J]. 中国腐蚀与防护学报,2013,33(3):182-187.
【4】曹楚南. 腐蚀电化学[M]. 北京:化学工业出版社,2002.
【5】曹楚南,张鉴清. 电化学阻抗谱导论[M]. 北京:科学出版社,2002.
【2】顾伟,杨明. 904L和CD4MCu不锈钢在硫酸中的腐蚀行为[J]. 贵州化工,2012,37(6):7-9.
【3】曾洪涛,向嵩,刘松林,等. 904L不锈钢在氢氟酸和浓硫酸混合液中的腐蚀行为[J]. 中国腐蚀与防护学报,2013,33(3):182-187.
【4】曹楚南. 腐蚀电化学[M]. 北京:化学工业出版社,2002.
【5】曹楚南,张鉴清. 电化学阻抗谱导论[M]. 北京:科学出版社,2002.
相关信息