Preparation and Property of Aramid Fiber Reinforced Nylon-6 Composite
摘 要
采用毛细管流变仪和差示扫描量热仪研究了尼龙6的热性能和流变特性,确定了芳纶纤维增强尼龙6复合材料的热压成型温度;制备了芳纶纤维增强尼龙6复合材料,研究了其微观结构和力学性能,并采用相控阵超声检测技术进行了无损检测。结果表明:芳纶纤维增强尼龙6复合材料的热压成型温度为245 ℃;尼龙6对芳纶纤维的浸渍效果较好,无损检测均未发现复合材料内部存在缺陷;复合材料的静态抗拉强度为279.7 MPa,其动态压缩强度和压缩模量均随应变速率的增加而增大,在高应变速率下呈脆性破坏。
Abstract
The thermal property and rheological behavior of nylon-6 were studied using capillary rheometer and differential scanning calorimeter and the hot-press forming temperature of aramid fiber reinforced nylon-6 composite was determined. Then the aramid fiber reinforced nylon-6 composite was prepared and the microstructure and mechanical properties were studied. Nondestructive testing of the composite was also conducted using ultrasonic phased array technology. The results show that the hot-press forming temperature of the aramid fiber reinforced nylon-6 composite was 245℃. The impregnating effect of nylon-6 on aramid fiber was relatively good. No defects were found in the composite by the nondestructive testing. The static tensile strength of the composite was 279.7 MPa and both the dynamic compressive strength and compression modulus increased with the increase of strain rate. The composite showed a brittle failure at a high strain rate.
中图分类号 TB324 DOI 10.11973/jxgccl201709012
所属栏目 新材料 新工艺
基金项目 国家杰出青年科学基金资助项目(11225212)
收稿日期 2016/8/1
修改稿日期 2017/7/5
网络出版日期
作者单位点击查看
备注张达适(1993-),男,黑龙江大庆人,硕士研究生导师:文桂林教授
引用该论文: ZHANG Dashi,QIAN Xiuyang,WANG Hongxin,WEN Guilin. Preparation and Property of Aramid Fiber Reinforced Nylon-6 Composite[J]. Materials for mechancial engineering, 2017, 41(9): 68~72
张达适,钱秀洋,王洪鑫,文桂林. 芳纶纤维增强尼龙6复合材料的制备与性能[J]. 机械工程材料, 2017, 41(9): 68~72
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张小伟,刘淑鹏.芳纶纤维/云母复合绝缘纸制备技术研究[J].中国造纸学报,2014,29(4):19-22.
【2】SINGH T J, SAMANTA S. Characterization of Kevlar fiber and its composites:A review[J]. Materials Today:Proceedings,2015,2(4/5):1381-1387.
【3】孙文丹,李波,李刚,等.芳纶纤维/环氧树脂预浸料界面相容性的方法探究[J].玻璃钢/复合材料,2015(2):75-80.
【4】KMETTY À,BÁRÁNY T,KARGER-KOCSIS J. Self-reinforced polymeric materials:A review[J]. Progress in Polymer Science, 2010,35(10):1288-1310.
【5】GAO C C,YU L,LIU H S,et al. Development of self-reinforced polymer composites[J]. Progress in Polymer Science,2012,37(6):767-780.
【6】KARGER-KOCSIS J, BÁRÁNY T. Single-polymer composites (SPCs):Status and future trends[J]. Composites Science and Technology,2014,92:77-94.
【7】何春霞.三维Kevlar/尼龙复合材料力学性能的研究[J].宇航材料工艺,1996(4):20-22.
【8】王灿耀,郑玉婴.Kevlar纤维增强尼龙6复合材料的力学性能[J].应用化学,2006,23(12):1373-1376.
【9】陈小成,丁国民,陈佳,等. 芳纶纤维增强PET/PA6复合材料力学性能的研究[C]//第二十届玻璃钢/复合材料学术交流会.武汉:中国硅酸盐学会玻璃钢分会,2014:87-102.
【10】ZHAO S F,CHENG L,GUO Y,et al.PA6 and Kevlar fiber reinforced isotactic polypropylene:Structure,mechanical properties and crystallization and melting behavior[J]. Materials and Design,2012,35:749-753.
【11】WARD I M, HINE P J. The science and technology of hot compaction[J]. Polymer, 2004, 45(5):1413-1427.
【12】张立功,张佐光.先进复合材料中主要缺陷分析[J].玻璃钢/复合材料, 2001(2):42-45.
【13】COSTA M L,ALMEIDA S F M,REZENDE M C.The influence of porosity on the interlaminar shear strength of carbon/epoxy and carbon/bismaleimide fabric laminates[J]. Composites Science and Technology,2001,61(14):2101-2108.
【14】钟德煌.便携式相控阵探伤仪在复合材料检测中的应用[J].航空制造技术,2008(15):53-54.
【15】靳世久,杨晓霞,陈世利,等.超声相控阵检测技术的发展及应用[J].电子测量与仪器学报,2014,28(9):925-934.
【16】KHONDKER O A, FUKUI T, INODA M,et al. Fabrication and mechanical properties of aramid/nylon plain knitted composites[J].Composite Part A,2004,35(10):1195-1205.
【17】ISHAK Z A M, LEONG Y W,STEEG M,et al. Mechanical properties of woven glass fabric reinforced in situ polymerized poly(butylene terephthalate) composites[J]. Composites Science and Technology,2007,67(3):390-398.
【2】SINGH T J, SAMANTA S. Characterization of Kevlar fiber and its composites:A review[J]. Materials Today:Proceedings,2015,2(4/5):1381-1387.
【3】孙文丹,李波,李刚,等.芳纶纤维/环氧树脂预浸料界面相容性的方法探究[J].玻璃钢/复合材料,2015(2):75-80.
【4】KMETTY À,BÁRÁNY T,KARGER-KOCSIS J. Self-reinforced polymeric materials:A review[J]. Progress in Polymer Science, 2010,35(10):1288-1310.
【5】GAO C C,YU L,LIU H S,et al. Development of self-reinforced polymer composites[J]. Progress in Polymer Science,2012,37(6):767-780.
【6】KARGER-KOCSIS J, BÁRÁNY T. Single-polymer composites (SPCs):Status and future trends[J]. Composites Science and Technology,2014,92:77-94.
【7】何春霞.三维Kevlar/尼龙复合材料力学性能的研究[J].宇航材料工艺,1996(4):20-22.
【8】王灿耀,郑玉婴.Kevlar纤维增强尼龙6复合材料的力学性能[J].应用化学,2006,23(12):1373-1376.
【9】陈小成,丁国民,陈佳,等. 芳纶纤维增强PET/PA6复合材料力学性能的研究[C]//第二十届玻璃钢/复合材料学术交流会.武汉:中国硅酸盐学会玻璃钢分会,2014:87-102.
【10】ZHAO S F,CHENG L,GUO Y,et al.PA6 and Kevlar fiber reinforced isotactic polypropylene:Structure,mechanical properties and crystallization and melting behavior[J]. Materials and Design,2012,35:749-753.
【11】WARD I M, HINE P J. The science and technology of hot compaction[J]. Polymer, 2004, 45(5):1413-1427.
【12】张立功,张佐光.先进复合材料中主要缺陷分析[J].玻璃钢/复合材料, 2001(2):42-45.
【13】COSTA M L,ALMEIDA S F M,REZENDE M C.The influence of porosity on the interlaminar shear strength of carbon/epoxy and carbon/bismaleimide fabric laminates[J]. Composites Science and Technology,2001,61(14):2101-2108.
【14】钟德煌.便携式相控阵探伤仪在复合材料检测中的应用[J].航空制造技术,2008(15):53-54.
【15】靳世久,杨晓霞,陈世利,等.超声相控阵检测技术的发展及应用[J].电子测量与仪器学报,2014,28(9):925-934.
【16】KHONDKER O A, FUKUI T, INODA M,et al. Fabrication and mechanical properties of aramid/nylon plain knitted composites[J].Composite Part A,2004,35(10):1195-1205.
【17】ISHAK Z A M, LEONG Y W,STEEG M,et al. Mechanical properties of woven glass fabric reinforced in situ polymerized poly(butylene terephthalate) composites[J]. Composites Science and Technology,2007,67(3):390-398.
相关信息