磷元素的非平衡晶界偏聚对A690M海洋环境用钢耐海水腐蚀性能的影响
Influence of Non-Equilibrium Grain Boundary Segregation of Phosphorus on Corrosion Resistance of Marine Steel A690M in Seawater
摘 要
采用俄歇能谱分析了A690M海洋环境用钢在600℃回火过程中磷元素的晶界偏聚行为，结合极化曲线和腐蚀锈层的微观分析探讨了P元素晶界偏聚对A690M钢耐海水腐蚀性能的影响。研究表明：A690M钢中P元素的晶界偏聚符合空位-溶质原子复合扩散导致的非平衡偏聚机制；P的晶界偏聚含量越高，锈层内部越易形成层状磷疤坑，使板坯耐海水腐蚀性能降低。
非平衡晶界偏聚
腐蚀
锈层
phosphorus
non-equilibrium segregation
corrosion
rust layer
Abstract
The grain boundary segregation behavior of phosphorus in marine steel A690M during tempering treatment at 600℃ was analyzed by Auger electron spectroscopy. The influence of grain boundary segregation of phosphorus on corrosion resistance of A690M steel in seawater was studied by microscopic observation of corrosion rust layer and polarization curve. The results show that the phosphorus segregation at grain boundary is consistent with non-equilibrium segregation behavior caused by vacancy-solute complex diffusion. The higher the concentration of phosphorus at grain boundary, the easier the formation of lamellar corrosion pit in the rust layer, which decreases the corrosion resistance of marine steel.
中图分类号 TG172 DOI 10.11973/fsyfh-201710002
所属栏目 试验研究
基金项目
收稿日期 2016/3/16
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: WAN Lanfeng,MA Zhizhen. Influence of Non-Equilibrium Grain Boundary Segregation of Phosphorus on Corrosion Resistance of Marine Steel A690M in Seawater[J]. Corrosion & Protection, 2017, 38(10): 747
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李铸铁. 09CuPCrNi耐腐蚀钢板生产工艺模拟研究[J]. 热加工工艺,2014,43(22):94-97.
【2】万兰凤,张晖,何宜柱. 成分调整对09CuPCrNi耐候钢耐腐蚀性能的影响[J]. 热加工工艺,2009,38(14):17-19.
【3】周国平,刘振宇,陈俊,等. 磷的表面逆偏析对铸轧薄带钢耐候性能的影响[J]. 腐蚀科学与防护技术,2010,22(3):157-161.
【4】MAIER P,FAULKNER R G. Effects of thermal history and microstructure on phosphorus and manganese segregation at grain boundaries in C-Mn welds[J]. Materials Characterization,2013,51:49-62.
【5】张灶利,刘键,清英,等. 磷在钢回火脆性发展时的非平衡偏聚及钼的影响[J]. 钢铁研究学报,1999,11(5):26-29.
【6】王凯,王民庆,徐庭栋. 磷的非平衡晶界偏聚现象及对回火脆性的影响[J]. 材料科学与工艺,2009,17(6):882-888.
【7】FAULKNER R G. Non-equilibrium grain-boundary segregation in austenitic alloys[J]. Journal of Materials Science,1981,16:373-383.
【8】徐庭栋. 非平衡晶界偏聚和晶间脆性断裂的研究[J]. 自然科学进展,2006,16(2):160-168.
【2】万兰凤,张晖,何宜柱. 成分调整对09CuPCrNi耐候钢耐腐蚀性能的影响[J]. 热加工工艺,2009,38(14):17-19.
【3】周国平,刘振宇,陈俊,等. 磷的表面逆偏析对铸轧薄带钢耐候性能的影响[J]. 腐蚀科学与防护技术,2010,22(3):157-161.
【4】MAIER P,FAULKNER R G. Effects of thermal history and microstructure on phosphorus and manganese segregation at grain boundaries in C-Mn welds[J]. Materials Characterization,2013,51:49-62.
【5】张灶利,刘键,清英,等. 磷在钢回火脆性发展时的非平衡偏聚及钼的影响[J]. 钢铁研究学报,1999,11(5):26-29.
【6】王凯,王民庆,徐庭栋. 磷的非平衡晶界偏聚现象及对回火脆性的影响[J]. 材料科学与工艺,2009,17(6):882-888.
【7】FAULKNER R G. Non-equilibrium grain-boundary segregation in austenitic alloys[J]. Journal of Materials Science,1981,16:373-383.
【8】徐庭栋. 非平衡晶界偏聚和晶间脆性断裂的研究[J]. 自然科学进展,2006,16(2):160-168.
相关信息