Influence of Sintering Temperature on Microstructure and Mechanical Properties of Powder Metallurgy Low-Alloy Steel
摘 要
采用行程限制法将1300WB低合金钢粉压制成型并在不同温度下烧结制备了低合金钢,研究了烧结温度对其显微组织、微观形貌、密度、压溃强度和硬度的影响。结果表明:随着烧结温度升高,试样中孔隙的数量减少、尺寸减小,孔隙由连通状变得独立封闭,且孔形状由不规则形向球形转变;较低温度烧结试样的显微组织由珠光体、铁素体和渗碳体组成,随烧结温度升高,珠光体数量增多,试样的显微组织变均匀;试样的密度、压溃强度和硬度均随烧结温度升高而增大。
Abstract
1300WB low-alloy steel powder was compression formed by a route limitation method and then was sintered to a low-alloy steel at different temperatures. The effects of sintering temperature on the microstructure, micromorphology, density, compressive strength and hardness were studied. The results show that with the increase of sintering temperature, the pore quantity in the sample decreased and the size was reduced; the connected pores became independent; the pore shape changed from irregular to spherical. The microstructure of the low-temperature sintered sample was composed of pearlite, ferrite and cementite. With the increase of sintering temperature, the amount of pearlite increased and the microstructure became uniform.The density, compressive strength and hardness of samples also increased with increasing sintering temperature.
中图分类号 TF123 DOI 10.11973/jxgccl201710011
所属栏目 新材料 新工艺
基金项目 安徽省科技攻关项目(1501021006)
收稿日期 2016/9/14
修改稿日期 2017/8/29
网络出版日期
作者单位点击查看
备注孙芳芳(1990-),女,河南虞城人,硕士研究生
引用该论文: SUN Fangfang,MA Shaobo,BI Gang,LI Qilong,WANG Feng. Influence of Sintering Temperature on Microstructure and Mechanical Properties of Powder Metallurgy Low-Alloy Steel[J]. Materials for mechancial engineering, 2017, 41(10): 48~51
孙芳芳,马少波,毕岗,李其龙,王峰. 烧结温度对粉末冶金低合金钢显微组织和力学性能的影响[J]. 机械工程材料, 2017, 41(10): 48~51
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】夏春智,李亚江,王娟. Cu/Al异种金属连接的研究现状[J]. 焊接,2008(1):17-20.
【2】BRANDES E A, BROOK G B. Smithells metals reference book[M]. 7th ed. Oxford:Butterworth-Heinemann, 1992.
【3】马志鹏,闫久春,张旭昀,等. 铝钎焊用锌基合金钎料的制备及钎焊接头的组织和抗剪强度[J].机械工程材料,2015,39(2):85-89.
【4】徐维普,吴毅雄,刘秀忠,等. 锌铝合金的钎焊研究[J].机械工程材料,2004,28(7):32-34.
【5】张满,薛松柏,戴玮,等. Ag元素对Zn-Al钎料性能的影响[J].焊接学报,2010,31(10):73-76.
【6】杨金龙,薛松柏,姬峰,等. Ti元素对Zn-22Al钎料组织和性能的影响[J].焊接学报,2012,33(11):93-96.
【7】张亮,韩继光,何成文,等. 稀土元素对无铅钎料组织和性能的影响[J].中国有色金属学报,2012,22(6):1680-1696.
【2】BRANDES E A, BROOK G B. Smithells metals reference book[M]. 7th ed. Oxford:Butterworth-Heinemann, 1992.
【3】马志鹏,闫久春,张旭昀,等. 铝钎焊用锌基合金钎料的制备及钎焊接头的组织和抗剪强度[J].机械工程材料,2015,39(2):85-89.
【4】徐维普,吴毅雄,刘秀忠,等. 锌铝合金的钎焊研究[J].机械工程材料,2004,28(7):32-34.
【5】张满,薛松柏,戴玮,等. Ag元素对Zn-Al钎料性能的影响[J].焊接学报,2010,31(10):73-76.
【6】杨金龙,薛松柏,姬峰,等. Ti元素对Zn-22Al钎料组织和性能的影响[J].焊接学报,2012,33(11):93-96.
【7】张亮,韩继光,何成文,等. 稀土元素对无铅钎料组织和性能的影响[J].中国有色金属学报,2012,22(6):1680-1696.
相关信息