X80管线钢用自保护药芯焊丝的研制及焊接接头性能
Development of Self-shielded Flux Cored Wire for X80 Pipeline Steel and Properties of Welded Joint
摘 要
为满足X80管线钢的焊接需要，开发了以BaF2为主的低碱性渣系Mn-Ni-Mo-Ti-B合金系自保护药芯焊丝，并对采用该焊丝焊接后此钢接头的显微组织及力学性能进行了分析。结果表明：X80管线钢接头焊缝显微组织为针状铁素体、粒状贝氏体以及少量的M-A岛，热影响区的组织主要为粒状贝氏体、贝氏体铁素体；焊接接头的抗拉强度为711 MPa，屈服强度为565.7 MPa，室温冲击功为155 J，-20℃冲击功为144.7 J，完全能满足石油管道建设的标准要求。
药芯焊丝
显微组织
力学性能
X80 pipeline steel
flux cored wire
microstructure
mechanical property
Abstract
In order to meet the requirement of welding of X80 pipeline steel, a low alkali slag system of Mn-Ni-Mo-Ti-B alloy self-shielded flux cored wire based on BaF2 was developed and the microstructure and mechanical properties of joint welded by the welding wire were analyzed. The results show that the microstructure of weld included acicular ferrite, granular bainite and a small amount of M-A island and the microstructure of heat affected zone mainly included granular bainite and bainite ferrite. The tensile strength of the welded joint was 711 MPa and yield strength was 565.7 MPa. The impact energy was 155 J at room temperature and 144.7 J at -20℃. The properties of the weld joint could fully meet the standard requirement of oil pipeline construction project.
中图分类号 TG422.3 DOI 10.11973/jxgccl201710017
所属栏目 材料性能及应用
基金项目 国家自然科学基金资助项目（51274162）；陕西省协同创新计划项目（2015XT-39）；陕西省教育厅重点实验室科研计划项目（15JS082）；陕西省教育厅服务地方专项项目（16JF021）
收稿日期 2016/9/7
修改稿日期 2017/8/10
网络出版日期
作者单位点击查看
备注张敏(1967-),男,陕西西安人,教授,博士
引用该论文: ZHANG Min,LI Le,SHU Shaoyan,LU Xiaokang,LI Jihong. Development of Self-shielded Flux Cored Wire for X80 Pipeline Steel and Properties of Welded Joint[J]. Materials for mechancial engineering, 2017, 41(10): 77～81
张敏,李乐,舒绍燕,芦晓康,李继红. X80管线钢用自保护药芯焊丝的研制及焊接接头性能[J]. 机械工程材料, 2017, 41(10): 77～81
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李铁龙,杨新岐,王振山.焊速对AZ80镁合金搅拌摩擦焊接头成形及组织的影响[J].机械工程材料,2013,37(5):26-29.
【2】初雅杰,李晓泉,吴申庆.镁合金焊接方法的研究进展[J].机械工程材料,2010,34(6):10-12.
【3】WRIGHT I G,PINT B A.An assessment of the high temperature oxidation behavior of Fe-Cr steels in water vapor and steam[C]//Corrosion 2002.[S.l.]:NACE International, 2002:NACE-02377.
【4】王玉华,高霖,王辉.AZ31B镁合金的数控热渐进成型工艺[J].机械工程材料,2009,33(9):95-97.
【5】JIY H,PARK J J.Formability of magnesium AZ31 sheet in the increment forming at warm temperature[J].Journal of Materials Process Technology,2008,201(1):354-358.
【6】AMBROGIO G,FILICE L,MANCO G L.Warm incremental forming of magnesium alloy AZ31[J].CIRP Annals-Manufacturing Technology, 2008,57(1):257-260.
【7】OTSU M, KAI Y, TAKASHIMA K.Simultaneous control of shape and properties of AZ31 magnesium alloy sheets by incremental forming[J].Materials Transactions,2008,49(5):1124-1128.
【8】DUFLOU J R,CALLEBAUT B,VERBERT J, et al.Laser assisted incremental forming:Formability and accuracy improvement[J].CIRP Annals-Manufacturing Technology,2007,56(1):273-276.
【2】初雅杰,李晓泉,吴申庆.镁合金焊接方法的研究进展[J].机械工程材料,2010,34(6):10-12.
【3】WRIGHT I G,PINT B A.An assessment of the high temperature oxidation behavior of Fe-Cr steels in water vapor and steam[C]//Corrosion 2002.[S.l.]:NACE International, 2002:NACE-02377.
【4】王玉华,高霖,王辉.AZ31B镁合金的数控热渐进成型工艺[J].机械工程材料,2009,33(9):95-97.
【5】JIY H,PARK J J.Formability of magnesium AZ31 sheet in the increment forming at warm temperature[J].Journal of Materials Process Technology,2008,201(1):354-358.
【6】AMBROGIO G,FILICE L,MANCO G L.Warm incremental forming of magnesium alloy AZ31[J].CIRP Annals-Manufacturing Technology, 2008,57(1):257-260.
【7】OTSU M, KAI Y, TAKASHIMA K.Simultaneous control of shape and properties of AZ31 magnesium alloy sheets by incremental forming[J].Materials Transactions,2008,49(5):1124-1128.
【8】DUFLOU J R,CALLEBAUT B,VERBERT J, et al.Laser assisted incremental forming:Formability and accuracy improvement[J].CIRP Annals-Manufacturing Technology,2007,56(1):273-276.
相关信息