碳化钨颗粒增强金属基复合涂层制备工艺研究及发展现状
Research and Development Status of Preparation Processes of WC Particle Reinforced Metal Matrix Composite Coatings
摘 要
综述了近年来国内外常用的碳化钨颗粒增强金属基复合涂层制备工艺的研究现状，包括真空熔覆、激光熔覆以及热喷涂等，着重介绍了不同工艺的特点以及所制备涂层性能的差异，并对未来的发展方向进行了展望。分析表明：碳化钨颗粒增强金属基复合涂层可以提高工件表面的硬度，改善工件的耐磨和耐蚀性能；不同的制备工艺对最终产品的性能有较大的影响，采用真空熔覆法制备的涂层在涂层结合强度、均匀性等方面相比于激光熔覆、热喷涂等方法制备的具有较大优势；对传统工艺如激光熔覆、热喷涂等的升级与改造也是一个值得关注的方向。
颗粒增强金属基复合涂层
真空熔覆
激光熔覆
热喷涂
WC
particle reinforced metal matrix composite coating
vacuum cladding
laser cladding
thermal spraying
Abstract
The research situations of the preparation processes of WC particle reinforced metal matrix composite coatings at home and abroad were reviewed, such as vacuum cladding, laser cladding, thermal spraying and so on. The characteristics of different processes and product performances were described mainly, and the developing tendency in the future was also prospected. The analysis presents that WC particle reinforced metal matrix composite coatings could improve the surface hardness and enhance the wear resistance and corrosion resistance. The effects of various processes on the final products were different. Compared with laser cladding method and thermal spraying method, vacuum cladding method had great advantages on the aspects of bonding strength, coating uniformity, etc. Finally, it was pointed out that the improvement in traditional techniques such as laser cladding and thermal spraying was also an attractive topic.
中图分类号 TG174.44 DOI 10.11973/lhjy-wl201710006
所属栏目 综述
基金项目
收稿日期 2016/7/13
修改稿日期
网络出版日期
作者单位点击查看
备注巴发海(1966-),男,教授级高工,博士,主要从事材料检测、失效分析与安全评估等方面的研究,bafahai@163.com
引用该论文: BA Fahai,LI Kai,WANG Fei,ZHANG Chao. Research and Development Status of Preparation Processes of WC Particle Reinforced Metal Matrix Composite Coatings[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2017, 53(10): 720～724
巴发海,李凯,王飞,张超. 碳化钨颗粒增强金属基复合涂层制备工艺研究及发展现状[J]. 理化检验－物理分册, 2017, 53(10): 720～724
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘娴,周夏凉,陈小明,等.超音速等离子喷涂WC-10Co4Cr涂层的力学性能及冲蚀磨损失效分析[J].理化检验-物理分册,2014,50(11):785-788.
【2】刘晓静,陈春焕,赵志强.表面处理对5083铝合金板胶接性能的影响[J].理化检验-物理分册,2013,49(2):75-78.
【3】FARAHMAND P, LIU S, ZHANG Z, et al. Laser cladding assisted by induction heating of Ni-WC composite enhanced by nano-WC and La2O3[J]. Ceramics International, 2014, 40(10):15421-15438.
【4】蒋业华,李祖来,叶小梅,等.碳化钨颗粒在WC/Fe基复合材料基体中的断裂和熔解[J].铸造,2007,56(5):491-494.
【5】YANG J, MIAO X, WANG X, et al. Microstructure, magnetic properties and empirical electron theory calculations of laser cladding FeNiCr/60%WC composite coatings with Mo additions[J]. International Journal of Refractory Metals and Hard Materials, 2016, 54:216-222.
【6】李健,夏建飞,孔德军.等离子喷涂WC/Co-Fe基涂层摩擦与磨损性能[J].润滑与密封,2012,37(8):74-80.
【7】BARTKOWSKI D, KINAL G. Microstructure and wear resistance of Stellite-6/WC MMC coatings produced by laser cladding using Yb:YAG disk laser[J]. International Journal of Refractory Metals and Hard Materials, 2016, 58:157-164.
【8】BAO J, NEWKIRK J W, BAO S. Wear-resistant WC composite hard coatings by brazing[J]. Journal of Materials Engineering and Performance, 2004, 13(4):385-388.
【9】YANG G R, HUANG C P, SONG W M, et al. Microstructure characteristics of Ni/WC composite cladding coatings[J]. 矿物冶金与材料学报(英文版), 2016, 23(2):184-192.
【10】周腾,刘涛,高立新,等.钎焊WC-Ni复合涂层脱落原因分析[C]//第十七届全国表面保护技术交流会论文集.嘉兴:[出版者不详],2013:179-182.
【11】黄柳仙,曹玉鹏,林晨,等.真空熔覆镍基合金-碳化钨复合涂层的研究[J].表面技术,2009,38(3):25-27.
【12】黄新波.真空熔覆碳化钨/钴基合金复合涂层抗疲劳性能的研究[J].粉末冶金技术,2008,26(3):192-195.
【13】马世博,邵明杰,侯瑞东,等.碳化钨对真空熔覆铁基复合涂层结构和性能的影响[J].燕山大学学报,2016,40(2):116-122.
【14】林晨.热处理对镍基合金碳化钨硬面涂层疲劳强度的影响[J].金属热处理,2006,31(2):37-40.
【15】甄睿,薛亚军,方信贤,等.非真空熔覆Ni60A+WC复合涂层的组织和性能[J].金属热处理,2011,36(11):93-95.
【16】张生欣,狄平,徐梦廓,等.感应重熔-热处理对镍基碳化钨涂层的影响[J].中国表面工程,2016,29(1):46-50.
【17】孙焕,林晨,陶洪伟,等.真空高频感应熔覆Ni60-WC复合涂层的耐蚀性[J].中国表面工程,2013,26(6):35-41.
【18】WULIN S, ECHIGOYA J, BEIDI Z, et al. Vacuum laser cladding and effect of Hf on the cracking susceptibility and the microstructure of Fe-Cr-Ni laser-clad layer[J]. Surface and Coatings Technology, 2000, 126(1):76-80.
【19】宋建丽,李永堂,邓琦林,等.激光熔覆成形技术的研究进展[J].机械工程学报,2010,46(14):29-39.
【20】崔爱永,胡芳友,张忠文,等.钛合金表面激光熔覆修复技术[J].中国表面工程,2011,24(2):61-64.
【21】张光钧,吴培桂,许佳宁,等.激光熔覆的应用基础研究进展[J].金属热处理,2011,36(1):5-13.
【22】潘浒,赵剑峰,刘云雷,等.激光熔覆修复镍基高温合金稀释率的可控性研究[J].中国激光,2013,40(4):109-115.
【23】刘建弟,张述泉,王华明.激光熔覆WC颗粒增强复合涂层的组织及耐磨性[J].中国有色金属学报,2012,22(9):2600-2607.
【24】姚成武,徐滨士,黄坚,等.铁基合金激光熔覆层裂纹控制的组织设计[J].中国表面工程,2010,23(3):74-79,83.
【25】余本海,胡雪惠,吴玉娥,等.电磁搅拌对激光熔覆WC-Co基合金涂层的组织结构和硬度的影响及机理研究[J].中国激光,2010,37(10):2672-2677.
【26】倪立斌,刘继常,伍耀庭,等.基于神经网络和粒子群算法的激光熔覆工艺优化[J].中国激光,2011,38(2):99-104.
【27】朱刚贤,张安峰,李涤尘.激光熔覆工艺参数对熔覆层表面平整度的影响[J].中国激光,2010,37(1):296-301.
【28】王志坚,董世运,徐滨士,等.激光熔覆工艺参数对金属成形效率和形状的影响[J].红外与激光工程,2010,39(2):315-319.
【29】杨震晓,刘敏,邓春明,等.热喷涂基体表面前处理技术的研究进展[J].中国表面工程,2012,25(2):8-14.
【30】BOLELLI G, HULKA I, KOIVULUOTO H, et al. Properties of WC-FeCrAl coatings manufactured by different high velocity thermal spray processes[J]. Surface and Coatings Technology, 2014, 247:74-89.
【31】王东生,田宗军,沈理达,等.等离子喷涂常规和纳米ZrO2-7%/Y2O3热障涂层的热腐蚀性能[J].热加工工艺,2014(8):156-160.
【32】白智辉,高峰,王大峰,等.不同颗粒度碳化钨的WC-17Co等离子涂层组织及摩擦学特性研究[J].热喷涂技术,2015,7(3):48-53.
【33】田玉亮,刘海飞,刘邦武,等.等离子熔覆镍基合金及复合材料涂层的组织与性能研究[J].热喷涂技术,2010,2(1):30-34,48.
【34】梁文军,张宏,沈承金,等.粘结剂对超音速火焰喷涂碳化钨涂层磨粒磨损性能的影响[J].电镀与涂饰,2012,31(2):67-71.
【35】李长久,王豫跃,大森明.粉末结构对超音速火焰喷涂WC系金属陶瓷涂层结合强度的影响[J].中国表面工程,2000,13(2):1-4.
【36】JAFARI M, ENAYATI M H, SALEHI M, et al. High temperature oxidation behavior of micro/nanostructured WC-Co coatings deposited from Ni-coated powders using high velocity oxygen fuel spraying[J]. Surface and Coatings Technology, 2016, 302:426-437.
【37】GISARIO A, PUOPOLO M, VENETTACCI S, et al. Improvement of thermally sprayed WC-Co/NiCr coatings by surface laser processing[J]. International Journal of Refractory Metals and Hard Materials, 2015, 52:123-130.
【38】郭孟秋,唐斌,范鑫,等.钛合金零件表面爆炸喷涂修复[J].航空维修与工程,2015(9):121-122,123.
【39】吴旭,郭志猛.铝合金表面爆炸喷涂WC-17Co涂层性能的研究[J].粉末冶金工业,2013,23(5):22-25.
【40】张素芬,杨文娟,宋建蓬.金属材料表面爆炸喷涂WC-Co涂层的均匀性性能分析及数学描述[J].铸造技术,2014,35(10):2310-2312.
【2】刘晓静,陈春焕,赵志强.表面处理对5083铝合金板胶接性能的影响[J].理化检验-物理分册,2013,49(2):75-78.
【3】FARAHMAND P, LIU S, ZHANG Z, et al. Laser cladding assisted by induction heating of Ni-WC composite enhanced by nano-WC and La2O3[J]. Ceramics International, 2014, 40(10):15421-15438.
【4】蒋业华,李祖来,叶小梅,等.碳化钨颗粒在WC/Fe基复合材料基体中的断裂和熔解[J].铸造,2007,56(5):491-494.
【5】YANG J, MIAO X, WANG X, et al. Microstructure, magnetic properties and empirical electron theory calculations of laser cladding FeNiCr/60%WC composite coatings with Mo additions[J]. International Journal of Refractory Metals and Hard Materials, 2016, 54:216-222.
【6】李健,夏建飞,孔德军.等离子喷涂WC/Co-Fe基涂层摩擦与磨损性能[J].润滑与密封,2012,37(8):74-80.
【7】BARTKOWSKI D, KINAL G. Microstructure and wear resistance of Stellite-6/WC MMC coatings produced by laser cladding using Yb:YAG disk laser[J]. International Journal of Refractory Metals and Hard Materials, 2016, 58:157-164.
【8】BAO J, NEWKIRK J W, BAO S. Wear-resistant WC composite hard coatings by brazing[J]. Journal of Materials Engineering and Performance, 2004, 13(4):385-388.
【9】YANG G R, HUANG C P, SONG W M, et al. Microstructure characteristics of Ni/WC composite cladding coatings[J]. 矿物冶金与材料学报(英文版), 2016, 23(2):184-192.
【10】周腾,刘涛,高立新,等.钎焊WC-Ni复合涂层脱落原因分析[C]//第十七届全国表面保护技术交流会论文集.嘉兴:[出版者不详],2013:179-182.
【11】黄柳仙,曹玉鹏,林晨,等.真空熔覆镍基合金-碳化钨复合涂层的研究[J].表面技术,2009,38(3):25-27.
【12】黄新波.真空熔覆碳化钨/钴基合金复合涂层抗疲劳性能的研究[J].粉末冶金技术,2008,26(3):192-195.
【13】马世博,邵明杰,侯瑞东,等.碳化钨对真空熔覆铁基复合涂层结构和性能的影响[J].燕山大学学报,2016,40(2):116-122.
【14】林晨.热处理对镍基合金碳化钨硬面涂层疲劳强度的影响[J].金属热处理,2006,31(2):37-40.
【15】甄睿,薛亚军,方信贤,等.非真空熔覆Ni60A+WC复合涂层的组织和性能[J].金属热处理,2011,36(11):93-95.
【16】张生欣,狄平,徐梦廓,等.感应重熔-热处理对镍基碳化钨涂层的影响[J].中国表面工程,2016,29(1):46-50.
【17】孙焕,林晨,陶洪伟,等.真空高频感应熔覆Ni60-WC复合涂层的耐蚀性[J].中国表面工程,2013,26(6):35-41.
【18】WULIN S, ECHIGOYA J, BEIDI Z, et al. Vacuum laser cladding and effect of Hf on the cracking susceptibility and the microstructure of Fe-Cr-Ni laser-clad layer[J]. Surface and Coatings Technology, 2000, 126(1):76-80.
【19】宋建丽,李永堂,邓琦林,等.激光熔覆成形技术的研究进展[J].机械工程学报,2010,46(14):29-39.
【20】崔爱永,胡芳友,张忠文,等.钛合金表面激光熔覆修复技术[J].中国表面工程,2011,24(2):61-64.
【21】张光钧,吴培桂,许佳宁,等.激光熔覆的应用基础研究进展[J].金属热处理,2011,36(1):5-13.
【22】潘浒,赵剑峰,刘云雷,等.激光熔覆修复镍基高温合金稀释率的可控性研究[J].中国激光,2013,40(4):109-115.
【23】刘建弟,张述泉,王华明.激光熔覆WC颗粒增强复合涂层的组织及耐磨性[J].中国有色金属学报,2012,22(9):2600-2607.
【24】姚成武,徐滨士,黄坚,等.铁基合金激光熔覆层裂纹控制的组织设计[J].中国表面工程,2010,23(3):74-79,83.
【25】余本海,胡雪惠,吴玉娥,等.电磁搅拌对激光熔覆WC-Co基合金涂层的组织结构和硬度的影响及机理研究[J].中国激光,2010,37(10):2672-2677.
【26】倪立斌,刘继常,伍耀庭,等.基于神经网络和粒子群算法的激光熔覆工艺优化[J].中国激光,2011,38(2):99-104.
【27】朱刚贤,张安峰,李涤尘.激光熔覆工艺参数对熔覆层表面平整度的影响[J].中国激光,2010,37(1):296-301.
【28】王志坚,董世运,徐滨士,等.激光熔覆工艺参数对金属成形效率和形状的影响[J].红外与激光工程,2010,39(2):315-319.
【29】杨震晓,刘敏,邓春明,等.热喷涂基体表面前处理技术的研究进展[J].中国表面工程,2012,25(2):8-14.
【30】BOLELLI G, HULKA I, KOIVULUOTO H, et al. Properties of WC-FeCrAl coatings manufactured by different high velocity thermal spray processes[J]. Surface and Coatings Technology, 2014, 247:74-89.
【31】王东生,田宗军,沈理达,等.等离子喷涂常规和纳米ZrO2-7%/Y2O3热障涂层的热腐蚀性能[J].热加工工艺,2014(8):156-160.
【32】白智辉,高峰,王大峰,等.不同颗粒度碳化钨的WC-17Co等离子涂层组织及摩擦学特性研究[J].热喷涂技术,2015,7(3):48-53.
【33】田玉亮,刘海飞,刘邦武,等.等离子熔覆镍基合金及复合材料涂层的组织与性能研究[J].热喷涂技术,2010,2(1):30-34,48.
【34】梁文军,张宏,沈承金,等.粘结剂对超音速火焰喷涂碳化钨涂层磨粒磨损性能的影响[J].电镀与涂饰,2012,31(2):67-71.
【35】李长久,王豫跃,大森明.粉末结构对超音速火焰喷涂WC系金属陶瓷涂层结合强度的影响[J].中国表面工程,2000,13(2):1-4.
【36】JAFARI M, ENAYATI M H, SALEHI M, et al. High temperature oxidation behavior of micro/nanostructured WC-Co coatings deposited from Ni-coated powders using high velocity oxygen fuel spraying[J]. Surface and Coatings Technology, 2016, 302:426-437.
【37】GISARIO A, PUOPOLO M, VENETTACCI S, et al. Improvement of thermally sprayed WC-Co/NiCr coatings by surface laser processing[J]. International Journal of Refractory Metals and Hard Materials, 2015, 52:123-130.
【38】郭孟秋,唐斌,范鑫,等.钛合金零件表面爆炸喷涂修复[J].航空维修与工程,2015(9):121-122,123.
【39】吴旭,郭志猛.铝合金表面爆炸喷涂WC-17Co涂层性能的研究[J].粉末冶金工业,2013,23(5):22-25.
【40】张素芬,杨文娟,宋建蓬.金属材料表面爆炸喷涂WC-Co涂层的均匀性性能分析及数学描述[J].铸造技术,2014,35(10):2310-2312.
相关信息