Heat Treatment of DT345 Pre-hardened Plastic Die Steel
摘 要
研究了新型预硬化塑料模具钢DT345经不同工艺热处理后的显微组织及性能。结果表明:通过控制该钢的在线预硬入口温度在850~880℃,出口温度 ≤ 200℃,再经500~530℃回火处理,可使预硬化后的硬度达到40~43 HRC,抗拉强度达到1 140~1 270 MPa,冲击功达到260~270 J,具有适宜的综合性能指标,可满足用户高硬度模具的使用要求。
Abstract
The microstructure and property of the newly-developed DT345 pre-hardening plastic die steel after different heat treatment processes was studied. The result shows that if on-line pre-hardening inlet temperature is at 850℃ to 880℃, and make outlet temperature is less or equal 200℃ and tempersthrough 500℃ to 530℃, which can make the pre-hardening hardness reaches at 40 HRC to 43 HRC,strengh value achieve 1 140 MPa to1 270 MPa and impact value reach 260 J to 270 J. The new product can meet the user's requirement with high-hardness and all-round performance objective.
中图分类号 TG142.45
所属栏目
基金项目
收稿日期
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: YU Hong,GUO Libo. Heat Treatment of DT345 Pre-hardened Plastic Die Steel[J]. Materials for mechancial engineering, 2017, 41(Z2): 77~80
于红,郭立. 预硬化塑料模具钢DT345的热处理工艺[J]. 机械工程材料, 2017, 41(Z2): 77~80
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈再枝,蓝德年.模具钢手册[M].北京:冶金工业出版社,2002.
【2】中华人民共和国国家质量监督检验检疫总局中国标准化管理委员会.GB/T230.1-2009金属材料洛氏硬度试验第1部分:试验方法[S].北京:中国标准出版社,2009.
【3】中华人民共和国国家质量监督检验检疫总局中国标准化管理委员会.GB/T229.1-2009金属材料夏比摆锤冲击试验方法[S].北京:中国标准出版社,2009.
【4】王健安.金属学与热处理[M].北京:机械工业出版社,1988.
【5】李炯辉.金属材料金相图谱[M].北京:机械工业出版社,2006.
【2】中华人民共和国国家质量监督检验检疫总局中国标准化管理委员会.GB/T230.1-2009金属材料洛氏硬度试验第1部分:试验方法[S].北京:中国标准出版社,2009.
【3】中华人民共和国国家质量监督检验检疫总局中国标准化管理委员会.GB/T229.1-2009金属材料夏比摆锤冲击试验方法[S].北京:中国标准出版社,2009.
【4】王健安.金属学与热处理[M].北京:机械工业出版社,1988.
【5】李炯辉.金属材料金相图谱[M].北京:机械工业出版社,2006.
相关信息