Corrosion Behavior of Copper in the Country Atmospheric Environment of Qingyuan
摘 要
通过金相显微镜、扫描电镜、X射线衍射仪(XRD)、能量色散谱(EDS)和电化学阻抗谱(EIS),研究了紫铜在清远乡村大气环境中暴露不同时间后的腐蚀行为。结果表明:紫铜在清远乡村大气环境暴露后,有局部腐蚀发生。随着时间的延长,腐蚀产物增多,并逐渐覆盖了铜表面形成较为致密的膜层,导致腐蚀速率下降。在暴露的前6个月,紫铜的腐蚀产物主要是Cu2O,随着时间的延长,大气中其他污染物对铜腐蚀的影响增加,12个月后腐蚀产物中出现了CuOHCl和CuS。
Abstract
The corrosion behavior of copper exposed to the country atmosphere of Qingyuan for different times was studied by metallographic microscopy, scanning electron microscopy, X-ray diffraction, energy dispersive spectra and electrochemical impedance spectroscopy. The results showed that localized corrosion occurred after copper was exposed to the country atmospheric environment of Qingyuan. When the exposure time was prolonged, the corrosion products increased and gradually covered the copper surface to form a relatively dense film, leading to a decrease of corrosion rate. The main corrosion products were Cu2O in the first 6 months of exposure. With the extension of exposure time, the effect of other pollutants in the atmosphere on the corrosion of copper increased. CuS and CuOHCl also appeared in the corrosion products after 12 months of exposure.
中图分类号 TG174 DOI 10.11973/fsyfh-201711007
所属栏目 试验研究
基金项目 广东电网公司科技开发项目(K-GD2013-0498002-002)
收稿日期 2016/5/2
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: KUANG Yinjie,LIANG Yongchun,YANG Fan. Corrosion Behavior of Copper in the Country Atmospheric Environment of Qingyuan[J]. Corrosion & Protection, 2017, 38(11): 852
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王振尧,于国才. 铜在污染环境中的大气腐蚀[J]. 腐蚀与防护,2000,21(8):339-341.
【2】ZHANG X,INGER O W,CHRISTOFER L. Mechanistic studies of corrosion product flaking on copper and copper-based alloys in marine environments[J]. Corrosion Science,2014,85(4):15-25.
【3】ROSA V,DIANA D,BLANCA M R. Effect of atmospheric pollutants on the corrosion of high power electrical conductors-Part 2. Pure coppoer[J]. Corrosion Science,2007,49(6):2329-2350.
【4】吴军,李晓刚,董超芳,等. 紫铜T2和黄铜H62在热带海洋大气环境中早期腐蚀行为[J]. 中国腐蚀与防护学报,2012,32(1):70-74.
【5】杨敏,王振尧. 铜的大气腐蚀研究[J]. 装备环境工程,2006,3(4):38-44.
【6】FITZGERALD K P,NAIRN J,SKENNERTON G,et al. Atmospheric corrosion of copper and the colour,structure and composition of natural patinas on copper[J]. Corrosion Science,2006,48(9):2480-2509.
【7】SANDBERG J,WALLINDER I O,LEYGRAF C. Corrosion-induced copper runoff from naturally and pre-patinated copper in a marine environment[J]. Corrosion Science,2006,48(12):4316-4338.
【8】安百刚,张学元,韩恩厚. 沈阳大气环境下纯铜的初期腐蚀行为[J]. 金属学报,2007,43(1):77-81.
【2】ZHANG X,INGER O W,CHRISTOFER L. Mechanistic studies of corrosion product flaking on copper and copper-based alloys in marine environments[J]. Corrosion Science,2014,85(4):15-25.
【3】ROSA V,DIANA D,BLANCA M R. Effect of atmospheric pollutants on the corrosion of high power electrical conductors-Part 2. Pure coppoer[J]. Corrosion Science,2007,49(6):2329-2350.
【4】吴军,李晓刚,董超芳,等. 紫铜T2和黄铜H62在热带海洋大气环境中早期腐蚀行为[J]. 中国腐蚀与防护学报,2012,32(1):70-74.
【5】杨敏,王振尧. 铜的大气腐蚀研究[J]. 装备环境工程,2006,3(4):38-44.
【6】FITZGERALD K P,NAIRN J,SKENNERTON G,et al. Atmospheric corrosion of copper and the colour,structure and composition of natural patinas on copper[J]. Corrosion Science,2006,48(9):2480-2509.
【7】SANDBERG J,WALLINDER I O,LEYGRAF C. Corrosion-induced copper runoff from naturally and pre-patinated copper in a marine environment[J]. Corrosion Science,2006,48(12):4316-4338.
【8】安百刚,张学元,韩恩厚. 沈阳大气环境下纯铜的初期腐蚀行为[J]. 金属学报,2007,43(1):77-81.
相关信息