Uncertainty Evaluation on Measurement of Cross-Sectional Area of Irregular Brass Specimens through Weighing Method
摘 要
对使用称重法测量不规则黄铜试样横截面积的不确定度来源进行了分析,并对黄铜试样的横截面积的测量不确定度进行了评定。结果表明:使用称重法测量不规则黄铜试样的横截面积时,其不确定度来源主要包括试样长度的测量不确定度、试样质量的测量不确定度、测量试样密度时水温的测量不确定度等方面。试验用不规则黄铜试样横截面积的测量不确定度报告为:试样横截面积S0=63.14 mm2,扩展不确定度U=2.25 mm2,包含因子k=2。
Abstract
The sources of uncertainty in measuring the cross-sectional area of irregular brass specimens through weight method were analyzed, and the measurement uncertainty of the cross-sectional area of the irregular brass specimens was evaluated. The results show that:the uncertainty sources of measuring the cross-sectional area of irregular brass specimens through weight method mainly included measurement uncertainty of the specimen length, measurement uncertainty of the specimen quality, measurement uncertainty of the water temperature when measuring the specimen density and so on. The uncertainty report of measuring cross-sectional area of irregular brass specimens for the test was:the cross-sectional area S0 of the specimen for the test was 63.14 mm2, the expanded uncertainty U was 2.25 mm2, and the coverage factor k was 2.
中图分类号 TB302.1 DOI 10.11973/lhjy-wl201711006
所属栏目 试验技术与方法
基金项目
收稿日期 2016/12/16
修改稿日期
网络出版日期
作者单位点击查看
备注郑程(1988-),男,工程师,学士,主要从事材料力学性能检测方面的工作,373888368@qq.com
引用该论文: ZHENG Cheng. Uncertainty Evaluation on Measurement of Cross-Sectional Area of Irregular Brass Specimens through Weighing Method[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2017, 53(11): 795~798
郑程. 称重法测量不规则黄铜试样横截面积的不确定度评定[J]. 理化检验-物理分册, 2017, 53(11): 795~798
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴伟. IF热轧钢板拉伸试验结果的测量不确定度评定[J].理化检验-物理分册,2016,52(6):392-396.
【2】GB/T 3850-2015 致密烧结金属材料与硬质合金 密度测定方法[S].
【3】中国合格评定国家认可中心,宝山钢铁股份有限公司研究院.材料理化检验测量不确定度评估指南及实例(CNAS-GL10:2006)[M].北京:中国计量出版社,2007.
【4】安刚,邵晶,刘辉.游标卡尺示值误差测量结果的不确定度分析[J].品牌与标准化,2010(6):61.
【5】黄旭东.H96黄铜棒导电率测试结果的不确定度评定[J].理化检验-物理分册,2016,52(7):450-453.
【6】萧铜,杨惠敏,刘强.电子天平测量结果不确定度的研究[J].中国测试技术,2007,33(5):82-84.
【7】邱萍,王玉兰,瞿咏梅,等.一等标准铂电阻温度计在(0~419.527)℃温区检定的不确定度评定[J].现代测量与实验室管理,2000(1):47-49.
【8】沈正宇.数字多用表在标准铂电阻温度计测量中的不确定度分析[J].计量技术,2002(2):18-20.
【2】GB/T 3850-2015 致密烧结金属材料与硬质合金 密度测定方法[S].
【3】中国合格评定国家认可中心,宝山钢铁股份有限公司研究院.材料理化检验测量不确定度评估指南及实例(CNAS-GL10:2006)[M].北京:中国计量出版社,2007.
【4】安刚,邵晶,刘辉.游标卡尺示值误差测量结果的不确定度分析[J].品牌与标准化,2010(6):61.
【5】黄旭东.H96黄铜棒导电率测试结果的不确定度评定[J].理化检验-物理分册,2016,52(7):450-453.
【6】萧铜,杨惠敏,刘强.电子天平测量结果不确定度的研究[J].中国测试技术,2007,33(5):82-84.
【7】邱萍,王玉兰,瞿咏梅,等.一等标准铂电阻温度计在(0~419.527)℃温区检定的不确定度评定[J].现代测量与实验室管理,2000(1):47-49.
【8】沈正宇.数字多用表在标准铂电阻温度计测量中的不确定度分析[J].计量技术,2002(2):18-20.
相关信息