Analysis on Cracking Reasons of a Blanking Die of YG8 Cemented Carbide
摘 要
某YG8硬质合金冲裁模具在使用过程中发生早期开裂失效。通过宏观观察、硬度测试、扫描电镜及能谱分析、金相检验等方法,对冲裁模具的开裂原因进行了分析。结果表明:由于冲裁模具原材料保存不良,钨粉接触空气发生氧化,材料中产生大量脆性η相及网状裂纹,使材料的强、韧性指标急剧下降,导致冲裁模具在服役过程中无法承受工作应力,从而产生早期开裂失效。
Abstract
The early cracking failure occurred to a blanking die of YG8 cemented carbide in the course of use. The cracking reasons of the blanking die were analyzed by macroscopic observation, hardness testing, scanning electron microscope and energy spectrum analysis, metallographic inspection and so on. The results show that:due to the poor preservation of the blanking die material, the tungsten powder contacted with the air and oxidized; as a result of that, there were a lot of brittle η phase and reticular cracks in the structure, and the indexes of the strength and toughness of the material drastically reduced; the blanking die couldn't bear the working stress during use, and the early cracking failure occurred.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl201711019
所属栏目 质量控制与失效分析
基金项目
收稿日期 2017/3/12
修改稿日期
网络出版日期
作者单位点击查看
备注金林奎(1966-),男,高级工程师,学士,主要从事金属材料失效分析工作,jinlinkui@foxmail.com
引用该论文: JIN Linkui,OU Hailong,ZOU Wenqi,YANG Yufei,FANG Manting. Analysis on Cracking Reasons of a Blanking Die of YG8 Cemented Carbide[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2017, 53(11): 844~847
金林奎,欧海龙,邹文奇,杨宇飞,方曼婷. YG8硬质合金冲裁模具开裂原因分析[J]. 理化检验-物理分册, 2017, 53(11): 844~847
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】徐进, 陈再枝,陈景榕,等.特殊钢丛书 模具钢[M].北京:冶金工业出版社,1998:354-357.
【2】程培源,詹武,常志梁,等.模具寿命与材料[M].北京:机械工业出版社,1999:102-105.
【3】蔡美良,丁惠麟,孟沪龙.新编工模具钢金相热处理[M].北京:机械工业出版社,1998:132-133.
【4】李炯辉,林德成.金属材料金相图谱[M].北京:机械工业出版社,2006:1264-1267.
【5】樊东黎,徐跃明,佟晓辉.热处理工程师手册[M].北京:机械工业出版社,2005:264-277.
【6】许文博,王艳龙,孙福来,等.粉末冶金金相图谱[M].北京:冶金工业出版社,1998:47-50.
【7】吴振海.常用模具钢热处理性能[M].上海:上海科学技术出版社,1984:175-178.
【2】程培源,詹武,常志梁,等.模具寿命与材料[M].北京:机械工业出版社,1999:102-105.
【3】蔡美良,丁惠麟,孟沪龙.新编工模具钢金相热处理[M].北京:机械工业出版社,1998:132-133.
【4】李炯辉,林德成.金属材料金相图谱[M].北京:机械工业出版社,2006:1264-1267.
【5】樊东黎,徐跃明,佟晓辉.热处理工程师手册[M].北京:机械工业出版社,2005:264-277.
【6】许文博,王艳龙,孙福来,等.粉末冶金金相图谱[M].北京:冶金工业出版社,1998:47-50.
【7】吴振海.常用模具钢热处理性能[M].上海:上海科学技术出版社,1984:175-178.
相关信息