达克罗涂层中六价铬在不同介质中的析出规律
Precipitation Law of Hexavalent Chromium of Dacromet Coating in Different Mediums
摘 要
采用可见分光光度法研究了含铬达克罗涂层分别在NaCl、蒸馏水、Na2SO4、NH4Cl溶液中析出六价铬的规律。结果表明：达克罗涂层在40℃的不同浓度NaCl和Na2SO4溶液中浸泡13 d时，六价铬仅有微量析出，其最大析出量分别为2.25 μg·cm-2和8.56 μg·cm-2；在40℃的蒸馏水和不同浓度NH4Cl溶液中浸泡13 d时，六价铬析出量几乎为0，涂层显示出了良好的稳定性。
达克罗涂层
六价铬
析出规律
visible spectrophotometer
dacromet coating
hexavalent chromium
precipitation law
Abstract
Precipitation law of hexavalent chromium from dacromet coating containing Cr in NaCl, distilled water, Na2SO4 and NH4Cl solutions, respectively, were studied by visible spectrophotometry. The results show that when the dacromet coating was immersed in the different-concentration NaCl or Na2SO4 solutions at 40℃ for 13 d, the hexavalent chromium precipitated slightly, with the maximum precipitated mass of 2.25 μg·cm-2 and 8.56 μg·cm-2, respectively. When immersed in distilled water and different-concentration NH4Cl solution at 40℃ for 13 d, the precipitated mass of the hexavalent chromium was nearly zero, indicating an excellent stability of the coating.
中图分类号 TG178 DOI 10.11973/jxgccl201712019
所属栏目 材料性能及应用
基金项目
收稿日期 2016/9/11
修改稿日期 2017/11/10
网络出版日期
作者单位点击查看
备注朱孝培(1993-),男,陕西安康人,硕士研究生
引用该论文: ZHU Xiaopei,ZHAO Maiqun,GAO Hui,ZHANG Jinfeng. Precipitation Law of Hexavalent Chromium of Dacromet Coating in Different Mediums[J]. Materials for mechancial engineering, 2017, 41(12): 90～93
朱孝培,赵麦群,高辉,张金凤. 达克罗涂层中六价铬在不同介质中的析出规律[J]. 机械工程材料, 2017, 41(12): 90～93
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】马壮,黄圣玲,李志超. 达克罗技术近期研究进展[J]. 现代涂料与涂装,2008, 11(6):16-18.
【2】陈锦虹, 卢锦堂, 许乔瑜, 等.镀锌层上有机物无铬钝化涂层的耐蚀性[J].材料保护,2002, 35(8):29-31.
【3】LIU J G, YAN C W. Electrochemical characteristics of corrosion behavior of organic/Dacromet composite systems pretreated with gamma-aminopropyltriethoxysilane[J]. Surface and Coatings Technology, 2006, 200(16):4976-4986.
【4】黄珊,吴明,谢飞,等.X80钢焊接接头在抚顺地区三种典型介质中的腐蚀行为[J].机械工程材料,2016,40(8):67-71.
【5】季利亚,姚正军. 无铬达克罗涂层的工艺研究[J]. 电镀与环保,2011, 31(3):22-24.
【6】王威,任呈强,曾德智,等.316L不锈钢在溶有不同气体NaCl溶液中的点蚀敏感性[J].机械工程材料,2015,39(7):95-98.
【7】王旭东,周伟峰,孙冬柏,等. Al2O3纳米粒子增强锌铝基耐蚀涂层的制备及性能研究[J]. 材料保护,2006, 39(8):3-7.
【8】蔡晓兰,郑淑萍,夏书标, 等. 达克罗膜层微观结构和成分研究[C]//中国表面工程协会第二届达克罗技术产业化论坛.[出版地不详]:中国表面工程协会, 2005:19-26.
【9】陈玲,李宁,周德瑞,等.达克罗涂层的组织结构及电化学特性研究[J].高技术通讯,2000(10):74-76.
【10】周次心,周雅. 达克罗涂层的现状及发展[J]. 南昌航空大学学报(自然科学版),2014, 28(2):43-49.
【11】王再德,陈玲,焦明泉,等. 无铬达克罗钝化剂的选择[J]. 材料保护,2008, 41(9):58-60.
【12】韩树民, 郑炀曾, 于升学,等.锌铝铬膜的防腐性能与机理[J].中国有色金属学报,2002,12(3):619-623.
【13】于兴文,李自松, 曹楚南.锌铬膜成膜过程及耐腐蚀机理的研究[J].中国有色金属学报,2000(9):12-14.
【14】HU H L, LI N, ZHU Y M. Effect of chromate on the electrochemical behavior of sintered Zn-Al coating in seawater[J]. Surface and Coatings Technology, 2008, 202(24):5649-5852.
【15】李志萍, 屈吉鸿, 沈照理,等.不同含水介质对污染河流中六价铬去除的对比模拟实验研究[J].工程勘察,2005(4):19-22.
【16】徐慧,仵彦卿.六价铬在具有渗透性反应墙的渗流槽中迁移实验研究[J].生态环境学报,2010,19(8):1941-1946.
【2】陈锦虹, 卢锦堂, 许乔瑜, 等.镀锌层上有机物无铬钝化涂层的耐蚀性[J].材料保护,2002, 35(8):29-31.
【3】LIU J G, YAN C W. Electrochemical characteristics of corrosion behavior of organic/Dacromet composite systems pretreated with gamma-aminopropyltriethoxysilane[J]. Surface and Coatings Technology, 2006, 200(16):4976-4986.
【4】黄珊,吴明,谢飞,等.X80钢焊接接头在抚顺地区三种典型介质中的腐蚀行为[J].机械工程材料,2016,40(8):67-71.
【5】季利亚,姚正军. 无铬达克罗涂层的工艺研究[J]. 电镀与环保,2011, 31(3):22-24.
【6】王威,任呈强,曾德智,等.316L不锈钢在溶有不同气体NaCl溶液中的点蚀敏感性[J].机械工程材料,2015,39(7):95-98.
【7】王旭东,周伟峰,孙冬柏,等. Al2O3纳米粒子增强锌铝基耐蚀涂层的制备及性能研究[J]. 材料保护,2006, 39(8):3-7.
【8】蔡晓兰,郑淑萍,夏书标, 等. 达克罗膜层微观结构和成分研究[C]//中国表面工程协会第二届达克罗技术产业化论坛.[出版地不详]:中国表面工程协会, 2005:19-26.
【9】陈玲,李宁,周德瑞,等.达克罗涂层的组织结构及电化学特性研究[J].高技术通讯,2000(10):74-76.
【10】周次心,周雅. 达克罗涂层的现状及发展[J]. 南昌航空大学学报(自然科学版),2014, 28(2):43-49.
【11】王再德,陈玲,焦明泉,等. 无铬达克罗钝化剂的选择[J]. 材料保护,2008, 41(9):58-60.
【12】韩树民, 郑炀曾, 于升学,等.锌铝铬膜的防腐性能与机理[J].中国有色金属学报,2002,12(3):619-623.
【13】于兴文,李自松, 曹楚南.锌铬膜成膜过程及耐腐蚀机理的研究[J].中国有色金属学报,2000(9):12-14.
【14】HU H L, LI N, ZHU Y M. Effect of chromate on the electrochemical behavior of sintered Zn-Al coating in seawater[J]. Surface and Coatings Technology, 2008, 202(24):5649-5852.
【15】李志萍, 屈吉鸿, 沈照理,等.不同含水介质对污染河流中六价铬去除的对比模拟实验研究[J].工程勘察,2005(4):19-22.
【16】徐慧,仵彦卿.六价铬在具有渗透性反应墙的渗流槽中迁移实验研究[J].生态环境学报,2010,19(8):1941-1946.
相关信息