锌铝镀层热轧板的耐蚀性
Corrosion Resistance of Hot Rolled Plates with Al-Zn Coating
摘 要
采用扫描电子显微镜观察锌铝镀层热轧板表面形貌，并通过中性盐雾试验，研究了锌铝镀层热轧板耐蚀性。结果表明：镀锌铝工艺可以填补热轧板表面凹坑，使热轧板的耐蚀性显著提高；随着腐蚀时间的延长，锌铝镀层热轧板的腐蚀速率先增大后减小；5%白锈和5%红锈出现的时间约为第15天和第54天；结合试验数据建立的镀锌铝热轧板腐蚀动力学模型，与试验数据拟合程度较好，可以为锌铝镀层热轧板的腐蚀动力学定量分析提供理论依据。
镀锌铝
热轧板
耐蚀性
neutral salt spray test
galvanizing Al-Zn
hot rolled plate
corrosion resistance
Abstract
Surface morphology of hot rolled plates with Al-Zn coating was observed by scanning electron microscopy (SEM). Neutral salt spray tests were applied to study the corrosion resistance of the hot rolled plates with Al-Zn coating. The results show that the corrosion resistance of the hot rolled plates was improved significantly as the galvanizing Al-Zn technology might fill up the pits on the surface of hot rolled plates. The corrosion rate of the hot rolled plates with Al-Zn coating first increased and then decreased with corrosion time. The white rust on the surface of Al-Zn coating was formed after 15 days, and the red rust occurred after 54 days. In addition, the corrosion kinetics model based on abundant experimental data was established, which had good fitting degree with experimental data and could provide theoretical basis for quantitative analysis of corrosion kinetics for hot rolled plates with Al-Zn coating.
中图分类号 TG174 DOI 10.11973/fsyfh-201802002
所属栏目 试验研究
基金项目 国家高技术研究发展计划（863计划）项目（2012AA03A504）
收稿日期 2016/7/26
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: HOU Rong,XU Guang,DAI Fangqin,MA Guohe,KE Jiangjun. Corrosion Resistance of Hot Rolled Plates with Al-Zn Coating[J]. Corrosion & Protection, 2018, 39(2): 90
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王静,伍林,易德莲,等. 镀锌层无铬钝化膜耐腐蚀性能的研究[J]. 材料保护,2006,4(11):28-30.
【2】李宇鹏,伍林,易德莲,等. 镀锌板复合钝化工艺的研究[J]. 化学与生物工程,2010(1):75-78.
【3】张益明,马荣贵,符寒光. 耐蚀热镀锌钢板在汽车工业中应用的进展[J]. 腐蚀与防护,1999,20(11):483.
【4】顾国成,刘邦津. 热浸镀[M]. 北京:化学工业出版社,1988.
【5】陈新. 热镀锌中主要合金元素的作用及机理研究[J]. 云南冶金,2009,38(4):45-47.
【6】李正明,张伟,张德晶,等. 热镀锌镀层合金最新研究进展和发展趋势[J]. 湖南有色金属,2011,27(2):35-37.
【7】熊自柳,张雲飞,姜涛. 锌铝合金镀层的性能与发展现状[J]. 河北冶金,2012(4):8-11.
【8】石焕荣,魏元际,丁毅,等. 热镀锌和锌铝合金镀层的微观组织及盐雾腐蚀行为[J]. 材料保护,2002,35(3):35-36.
【9】PEREZ A,BILLARD A,RÉBÉRÉ C,et al. Influence of metallurgical states on the corrosion behaviour of Al-Zn PVD coatings in saline solution[J]. Corrosion Science,2013,74(4):240-249.
【10】董梅,丰慧,施国兰. 热镀锌板腐蚀及盐雾试验研究[C]//2006年全国轧钢生产技术会议集. 宜昌:[出版者不详],2006.
【11】董梅,丰慧,施国兰. 热镀锌板盐雾试验研究[J]. 钢铁研究,2008,36(3):32-35.
【12】TACHIBANA K,MORINAGA Y,MAYUZUMI M. Hot dip fine Zn and Zn-Al alloy double coating for corrosion resistance at coastal area[J]. Corrosion Science,2007,49(1):149-157.
【13】孔纲,卢锦堂,车淳山,等. 热镀锌钢白锈产生原因分析及预防[J]. 腐蚀与防护,2005,26(10):450-452.
【14】吕家舜,李锋,杨洪刚,等. 热浸镀锌铝镁钢板镀层组织及腐蚀性能研究[J]. 材料工程,2012(10):89-93.
【15】SERE P R,ZAPPONI M,ELSNER C I,et al. Comparative corrosion behaviour of 55 aluminium-zinc alloy and zinc hot-dip coatings deposited on low carbon steel substrates[J]. Corrosion Science,1998,40(10):1711-1723.
【16】LIN K L,YANG C F,LEE J T. Correlation of microstructure with corrosion and electrochemical behavior of the batch-type hot-dip Al-Zn coatings:partⅡ. Zn and 55% Al-Zn Coating[J]. Corrosion,1991,47(1):9-17.
【17】谯赵辉,张清廉,李静,等. 钢基表面Zn-Mg合金镀层抗腐蚀机理的研究进展[C]//第五届全国腐蚀大会论文集. 北京:中国腐蚀与防护学会,2009.
【18】马海涛. SS400钢板红锈成因分析[J]. 辽宁专师学报(自然科学版),2005,7(3):72.
【19】RUDMAN P S. Hydriding and dehydriding kinetics[J]. Journal of the Less Common Metals,1983,89(1):93-110.
【2】李宇鹏,伍林,易德莲,等. 镀锌板复合钝化工艺的研究[J]. 化学与生物工程,2010(1):75-78.
【3】张益明,马荣贵,符寒光. 耐蚀热镀锌钢板在汽车工业中应用的进展[J]. 腐蚀与防护,1999,20(11):483.
【4】顾国成,刘邦津. 热浸镀[M]. 北京:化学工业出版社,1988.
【5】陈新. 热镀锌中主要合金元素的作用及机理研究[J]. 云南冶金,2009,38(4):45-47.
【6】李正明,张伟,张德晶,等. 热镀锌镀层合金最新研究进展和发展趋势[J]. 湖南有色金属,2011,27(2):35-37.
【7】熊自柳,张雲飞,姜涛. 锌铝合金镀层的性能与发展现状[J]. 河北冶金,2012(4):8-11.
【8】石焕荣,魏元际,丁毅,等. 热镀锌和锌铝合金镀层的微观组织及盐雾腐蚀行为[J]. 材料保护,2002,35(3):35-36.
【9】PEREZ A,BILLARD A,RÉBÉRÉ C,et al. Influence of metallurgical states on the corrosion behaviour of Al-Zn PVD coatings in saline solution[J]. Corrosion Science,2013,74(4):240-249.
【10】董梅,丰慧,施国兰. 热镀锌板腐蚀及盐雾试验研究[C]//2006年全国轧钢生产技术会议集. 宜昌:[出版者不详],2006.
【11】董梅,丰慧,施国兰. 热镀锌板盐雾试验研究[J]. 钢铁研究,2008,36(3):32-35.
【12】TACHIBANA K,MORINAGA Y,MAYUZUMI M. Hot dip fine Zn and Zn-Al alloy double coating for corrosion resistance at coastal area[J]. Corrosion Science,2007,49(1):149-157.
【13】孔纲,卢锦堂,车淳山,等. 热镀锌钢白锈产生原因分析及预防[J]. 腐蚀与防护,2005,26(10):450-452.
【14】吕家舜,李锋,杨洪刚,等. 热浸镀锌铝镁钢板镀层组织及腐蚀性能研究[J]. 材料工程,2012(10):89-93.
【15】SERE P R,ZAPPONI M,ELSNER C I,et al. Comparative corrosion behaviour of 55 aluminium-zinc alloy and zinc hot-dip coatings deposited on low carbon steel substrates[J]. Corrosion Science,1998,40(10):1711-1723.
【16】LIN K L,YANG C F,LEE J T. Correlation of microstructure with corrosion and electrochemical behavior of the batch-type hot-dip Al-Zn coatings:partⅡ. Zn and 55% Al-Zn Coating[J]. Corrosion,1991,47(1):9-17.
【17】谯赵辉,张清廉,李静,等. 钢基表面Zn-Mg合金镀层抗腐蚀机理的研究进展[C]//第五届全国腐蚀大会论文集. 北京:中国腐蚀与防护学会,2009.
【18】马海涛. SS400钢板红锈成因分析[J]. 辽宁专师学报(自然科学版),2005,7(3):72.
【19】RUDMAN P S. Hydriding and dehydriding kinetics[J]. Journal of the Less Common Metals,1983,89(1):93-110.
相关信息