改性环氧树脂无铬达克罗涂层的制备及其性能
Preparation and Property of Modified Epoxy Resin Chrome-free Docromet Coating
摘 要
实施了用聚氨酯改性环氧树脂替代铬酐制备无铬达克罗涂层的工艺，运用扫描电子显微镜（SEM）和X射线衍射（XRD）手段分析了所制备涂层的形貌和成分，通过动电位极化曲线，电化学阻抗（EIS），耐硝酸铵快速腐蚀试验，盐水浸泡试验等方法对涂层的耐蚀性进行了评价和研究。结果表明：树脂固化交联形成致密、均一、连续的膜层，有效阻止腐蚀介质的侵入，提高了涂层的耐蚀性；涂层主要成分为Zn和Al，当腐蚀介质侵入时，锌铝粉钝化生成氧化物，其防腐蚀机理主要是屏蔽作用、电化学作用及钝化作用。
改性环氧树脂
耐蚀性
碳钢
chromate-free Dacromet coating
modified epoxy resin
corrosion resistance
carbon steel
Abstract
The technology of preparing a chrome-free Dacromet coating with polyurethane modified epoxy resin instead of chromic anhydride was performed. The morphology and composition of the prepared coating were analysed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The corrosion resistance of the coating was evaluated by potentiodynamic polarization curve, electrochemical impedance spectroscopy (EIS), ammonium nitrate fast corrosion resistance test and salt water immersion test. The results showed that a dense, uniform and continuous film was formed through curing and cross-linking of resin, which effectively prevented the invasion of corrosive media and improved the corrosion resistance of the coating. The main components of the coating were Zn and Al, when the corrosive medium invaded, the zinc-aluminum powder was passivated to form oxide. The corrosion protection mechanism was mainly the shielding effect, electrochemical action and passivation effect.
中图分类号 TG174 DOI 10.11973/fsyfh-201803013
所属栏目 应用技术
基金项目
收稿日期 2016/9/19
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHANG Mingming,ZHANG Kebing,ZHANG Shenglin. Preparation and Property of Modified Epoxy Resin Chrome-free Docromet Coating[J]. Corrosion & Protection, 2018, 39(3): 227
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】PIETROWSKI M,ZIELINSKIL M,WOJCIECHOWS-KA M. Selective reduction of chloronitrobebzene to chloroaniline on Ru/MgF2 catalysts[J]. Catal Lett,2009,128:31-35.
【2】HERINGER H K. Dacromet-a new protection for fasteners[J]. Product Finshing,1997(5):29.
【3】胡会利,李宁,韩家军,等. 达克罗的研究现状[J]. 电镀与涂饰,2005,24(3):31-33.
【4】马壮,黄圣玲,李智超,等. 达克罗技术近期研究进展[J]. 现代涂料与涂装,2008,11(6):16-18.
【5】陈丽娇. 无铬达克罗工艺及耐蚀性研究[D]. 威海:哈尔滨工业大学,2007.
【6】王再德,陈玲,焦明泉,等. 无铬达克罗钝化剂的选择[J]. 材料保护,2008,41(9):58-60.
【7】江曼,毕渭滨,毛钢红,等. 新型无铬达克罗防腐材料[J]. 西北大学学报,2010,40(2):215-218.
【8】鲁俊,梁英,汤尚文,等. 无铬达克罗涂料工艺及耐蚀性能研究[J]. 应用化工,2011,40(4):612-613,617.
【9】张旭明,刘春明,王建军,等. 无铬达克罗成膜物质的研究进展[J]. 材料与冶金学报,2012(1).
【10】张圣麟,乔静飞,张明明,等. 一种无铬达克罗涂液的制备方法:CN105348870A[P].2016-02-24.
【11】乔静飞,张明明,李文超,等. 一种低铬达克罗涂层的制备工艺及性能[J]. 腐蚀与防护,2016,37(3):241-244.
【12】蔡元兴. 环保型富锌涂层工艺与性能研究[D]. 济南:山东大学,2006.
【13】孙天鹤,王宏波,王枝光,等. 聚氨酯改性环氧树脂的粘接性能研究[J]. 中国科技投资,2013(2):152-179.
【14】安恩朋,李相波,程旭东,等. 达克罗涂层研究现状[J]. 腐蚀科学与防护技术,2014,26(1):73-76.
【15】季利亚,姚正军. 无铬达克罗涂层的工艺研究[J]. 电镀与环保,2011,31(3):3-24.
【16】李狄. 电化学原理[M]. 北京:北京航空航天大学出版社,1999:406.
【17】杨丽霞,张三平,林安,等. 有机涂层渗水率及金属界面腐蚀的研究进展[J]. 材料保护,2001,34(10):28-30.
【18】刘斌,李瑛,林海潮,等. 用EIS研究H2O在环氧涂层中的传输行为[J]. 中国腐蚀与防护学报,2002,22(3):172-175.
【19】曹楚南,张鉴清. 电化学阻抗谱导论[M]. 北京:科学出版社,2002.
【20】AMIRUDIN A,THIERRY D. Application of electrochemical impedance spectroscopy to study the degradation of polylmer-coated metals[J]. Progress of Organic Coatings,1995,26:1-28.
【21】GRAY G S,BER ARD R A. EIS:electrochemical impedance spectroscope-a tool that can measure remaining life in protective coatings[C]//The Industrial Protective Coatings Conference and Exhibit. Floride:[s.n.]. 2003:209-227.
【2】HERINGER H K. Dacromet-a new protection for fasteners[J]. Product Finshing,1997(5):29.
【3】胡会利,李宁,韩家军,等. 达克罗的研究现状[J]. 电镀与涂饰,2005,24(3):31-33.
【4】马壮,黄圣玲,李智超,等. 达克罗技术近期研究进展[J]. 现代涂料与涂装,2008,11(6):16-18.
【5】陈丽娇. 无铬达克罗工艺及耐蚀性研究[D]. 威海:哈尔滨工业大学,2007.
【6】王再德,陈玲,焦明泉,等. 无铬达克罗钝化剂的选择[J]. 材料保护,2008,41(9):58-60.
【7】江曼,毕渭滨,毛钢红,等. 新型无铬达克罗防腐材料[J]. 西北大学学报,2010,40(2):215-218.
【8】鲁俊,梁英,汤尚文,等. 无铬达克罗涂料工艺及耐蚀性能研究[J]. 应用化工,2011,40(4):612-613,617.
【9】张旭明,刘春明,王建军,等. 无铬达克罗成膜物质的研究进展[J]. 材料与冶金学报,2012(1).
【10】张圣麟,乔静飞,张明明,等. 一种无铬达克罗涂液的制备方法:CN105348870A[P].2016-02-24.
【11】乔静飞,张明明,李文超,等. 一种低铬达克罗涂层的制备工艺及性能[J]. 腐蚀与防护,2016,37(3):241-244.
【12】蔡元兴. 环保型富锌涂层工艺与性能研究[D]. 济南:山东大学,2006.
【13】孙天鹤,王宏波,王枝光,等. 聚氨酯改性环氧树脂的粘接性能研究[J]. 中国科技投资,2013(2):152-179.
【14】安恩朋,李相波,程旭东,等. 达克罗涂层研究现状[J]. 腐蚀科学与防护技术,2014,26(1):73-76.
【15】季利亚,姚正军. 无铬达克罗涂层的工艺研究[J]. 电镀与环保,2011,31(3):3-24.
【16】李狄. 电化学原理[M]. 北京:北京航空航天大学出版社,1999:406.
【17】杨丽霞,张三平,林安,等. 有机涂层渗水率及金属界面腐蚀的研究进展[J]. 材料保护,2001,34(10):28-30.
【18】刘斌,李瑛,林海潮,等. 用EIS研究H2O在环氧涂层中的传输行为[J]. 中国腐蚀与防护学报,2002,22(3):172-175.
【19】曹楚南,张鉴清. 电化学阻抗谱导论[M]. 北京:科学出版社,2002.
【20】AMIRUDIN A,THIERRY D. Application of electrochemical impedance spectroscopy to study the degradation of polylmer-coated metals[J]. Progress of Organic Coatings,1995,26:1-28.
【21】GRAY G S,BER ARD R A. EIS:electrochemical impedance spectroscope-a tool that can measure remaining life in protective coatings[C]//The Industrial Protective Coatings Conference and Exhibit. Floride:[s.n.]. 2003:209-227.
相关信息