某塔吊钢丝绳断裂失效分析
Analysis on Fracture Failure of Wire Rope of a Tower Crane
摘 要
某工地塔吊起重机钢丝绳在施工过程中突然发生断裂失效，采用宏观检测、化学成分分析、金相检验、硬度测试、扫描电镜断口分析等方法，对钢丝绳断裂原因进行了分析。结果表明：由于内层钢丝表面润滑剂和锌系磷化膜遭到破坏，在微动磨损和腐蚀的作用下钢丝绳的力学性能严重下降，在拉力的作用下钢丝绳发生了一次性断裂。
断裂
微动磨损
腐蚀
失效分析
wire rope
fracture
fretting wear
corrosion
failure analysis
Abstract
The wire rope of a tower crane in a construction site suddenly fractured in the course of service. Causes for fracture of the wire rope were analyzed by methods of macro inspection, chemical composition analysis, metallographic examination, hardness test, scanning electron microscope fracture analysis. The results show that the surface lubricant and the phosphating film of zinc system of the inner layer steel wires were destroyed. The mechanical properties of the wire rope decreased severely under the effect of fretting wear and corrosion. The wire rope fractured once under the action of pulling force.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl201803013
所属栏目 质量控制与失效分析
基金项目
收稿日期 2017/5/24
修改稿日期
网络出版日期
作者单位点击查看
备注邱康勇(1987-),男,工程师,主要从事金属材料理化检验及机械零部件失效分析工作,295717869@qq.com
引用该论文: QIU Kangyong,ZHANG Jie,WU Jiquan. Analysis on Fracture Failure of Wire Rope of a Tower Crane[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(3): 218～221
邱康勇,张杰,吴继权. 某塔吊钢丝绳断裂失效分析[J]. 理化检验－物理分册, 2018, 54(3): 218～221
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】马惠珠,李宗奇,蔡磊,等. 起重机钢丝绳断裂失效分析[J]. 金属世界,2014,(2):24-27.
【2】张栋,钟培道,陶春虎,等. 失效分析[M]. 北京:国防工业出版社,2004.
【3】李娟,吴剑勇,田华,等. 港口门机用钢丝绳断裂原因分析[J]. 金属热处理,2015,4(10):31-32.
【4】倪忠进. 钢丝绳力学特性及失效机理研究[D]. 昆明:昆明理工大学,2008.
【5】崔影. 钢丝绳失效机理分析及改进举措[J]. 港口装卸,2012,(4):1-4.
【2】张栋,钟培道,陶春虎,等. 失效分析[M]. 北京:国防工业出版社,2004.
【3】李娟,吴剑勇,田华,等. 港口门机用钢丝绳断裂原因分析[J]. 金属热处理,2015,4(10):31-32.
【4】倪忠进. 钢丝绳力学特性及失效机理研究[D]. 昆明:昆明理工大学,2008.
【5】崔影. 钢丝绳失效机理分析及改进举措[J]. 港口装卸,2012,(4):1-4.
相关信息