Effect of AC Interference on the Corrosion Behavior of Pipeline Steel under Disbonded Coatings
摘 要
采用电化学试验和腐蚀形貌观察研究了交流干扰对剥离涂层下X80钢腐蚀行为的影响。结果表明:无交流干扰时,随着试验时间的延长,只有涂层破损点处及距离破损点4 cm处试样的自腐蚀电位出现了小幅波动,而远离破损点处试样的自腐蚀电位变化很小,基本处于稳定状态;腐蚀电流密度均有逐渐增大的趋势,且破损点处试样的腐蚀电流密度远远高于其他位置的。施加交流干扰后,随着交流干扰电压的增大,缝隙内金属的自腐蚀电位均有负移的趋势,且离破损点越近,试样的自腐蚀电位受交流干扰的影响越大,缝隙内各点试样的腐蚀电流密度均先减小后增大,破损点处试样的腐蚀电流密度变化较大。交流干扰增加了剥离涂层下试样的腐蚀倾向性及腐蚀速率,且破损点处试样的腐蚀速率受其影响较大,腐蚀形态为局部腐蚀。
Abstract
The effects of AC interference on the corrosion behavior of X80 steel under disbonded coatings were investigated using electrochemical tests and corrosion morphology observation. The results showed that when there was no AC interference, with the prolongation of test time, only the self-corrosion potentials (Ecorr) of the samples at the damaged point and 4 cm away from the damaged point fluctuated slightly, and Ecorr of the samples far away from the damaged point had no change, and were basically in a stable state. After AC interference was applied, Ecorr of the samples shifted negatively with the increase of the AC interference voltage. The closer to the damaged point, the greater the influence of AC interference on the Ecorr of the samples. The corrosion current density (Jcorr) of the sample at each point first decreased and then increased, and the Jcorr of the sample at the damaged point changed greatly. AC interference increased the corrosion tendency and corrosion rate of the samples under the disbonded coating, and the corrosion rate of the sample at the damaged point was affected greatly, and the corrosion morphology was localized corrosion.
中图分类号 TG174 DOI 10.11973/fsyfh-201805006
所属栏目 试验研究
基金项目 广西高校北部湾石油天然气资源有效利用重点实验室开放课题基金(2016KLOG21);中央高校基本科研业务费项目中国民航大学专项(3122017038)
收稿日期 2017/5/23
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: DING Qingmiao,WANG Yujun,CUI Yanyu,FANG Liping. Effect of AC Interference on the Corrosion Behavior of Pipeline Steel under Disbonded Coatings[J]. Corrosion & Protection, 2018, 39(5): 349
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李自力,丁清苗,张迎芳,等. 用电化学方法建立交流干扰下X70钢的最佳阴极保护电位[J]. 腐蚀与防护,2010,31(6):436-439.
【2】唐德志,杜艳霞,路民旭,等.埋地管道交流干扰与阴极保护相互作用研究进展[J]. 中国腐蚀与防护学报,2013,33(5):351-356.
【3】李自力,孙云峰,刘静,等. 埋地油气管道交流干扰腐蚀及防护研究进展[J]. 腐蝕科学与防护技术,2011,23(5):376-380.
【4】DU Y,TANG D,LU M,et al. Researches on the effects of AC interference on CP parameters and AC corrosion risk assessment for cathodic protected carbon steel[C]//Corrosion 2017. NACE International,[S.l.]:[s.n.],2017.
【5】李勋,张宏钊,张欣,等. 高压交流输电线路对埋地金属油气管道的电磁干扰腐蚀及其防护措施[J]. 山东理工大学学报(自然科学版),2017,4:65-70.
【6】封琼,张亚萍,汪洋,等. 基于埋地金属管道杂散电流的腐蚀与防护[J]. 腐蚀与防护,2017,38(2):91-93.
【7】任春霞,王晨,李佳威. 3PE防腐管道防腐层剥离因素及控制措施[J]. 焊管,2017,40(2):58-62.
【8】李瑞超,梁成浩,黄乃宝. 土壤中氯离子对无溶剂环氧石油沥青涂层的腐蚀影响[J]. 大连海事大学学报,2016,42(2):124-128.
【9】崔艳雨,范玥铭,危金卓,等. 埋地钢质管道防腐蚀层阴极剥离作用的研究进展[J]. 材料保护,2016,49(8):62-68.
【2】唐德志,杜艳霞,路民旭,等.埋地管道交流干扰与阴极保护相互作用研究进展[J]. 中国腐蚀与防护学报,2013,33(5):351-356.
【3】李自力,孙云峰,刘静,等. 埋地油气管道交流干扰腐蚀及防护研究进展[J]. 腐蝕科学与防护技术,2011,23(5):376-380.
【4】DU Y,TANG D,LU M,et al. Researches on the effects of AC interference on CP parameters and AC corrosion risk assessment for cathodic protected carbon steel[C]//Corrosion 2017. NACE International,[S.l.]:[s.n.],2017.
【5】李勋,张宏钊,张欣,等. 高压交流输电线路对埋地金属油气管道的电磁干扰腐蚀及其防护措施[J]. 山东理工大学学报(自然科学版),2017,4:65-70.
【6】封琼,张亚萍,汪洋,等. 基于埋地金属管道杂散电流的腐蚀与防护[J]. 腐蚀与防护,2017,38(2):91-93.
【7】任春霞,王晨,李佳威. 3PE防腐管道防腐层剥离因素及控制措施[J]. 焊管,2017,40(2):58-62.
【8】李瑞超,梁成浩,黄乃宝. 土壤中氯离子对无溶剂环氧石油沥青涂层的腐蚀影响[J]. 大连海事大学学报,2016,42(2):124-128.
【9】崔艳雨,范玥铭,危金卓,等. 埋地钢质管道防腐蚀层阴极剥离作用的研究进展[J]. 材料保护,2016,49(8):62-68.
相关信息