AZ31B镁合金/6061铝合金异质金属连接件整体微弧氧化膜的制备及其结构
Preparation and Structure of Overall Micro-Arc Oxidation Film on AZ31B Magnesium Alloy/6061 Aluminum Alloy Dissimilar Metal Connected Part
摘 要
对AZ31B镁合金和6061铝合金异质金属铆接件进行了微弧氧化，研究了不同时间微弧氧化膜的微观形貌、物相组成、电化学性能、硬度等，对比分析了微弧氧化过程中镁合金、铝合金表面氧化膜的形成过程。结果表明：经过10 min的微弧氧化后，该连接件整体被氧化膜包裹，氧化膜与2种合金基体均紧密连接，且均由致密层和疏松层组成；镁合金表面氧化膜主要由MgO、少量硅酸盐和氟化物组成，而铝合金表面氧化膜主要由Al2O3及少量硅酸盐组成；微弧氧化提高了连接件中镁合金、铝合金的腐蚀电位，降低了二者的腐蚀电位差，有效缓解了电偶腐蚀的发生。
异质金属连接件
镁合金
铝合金
氧化膜
micro-arc oxidation
dissimilar metal connected part
magnesium alloy
aluminum alloy
oxidation film
Abstract
AZ31B magnesium alloy and 6061 aluminum alloy dissimilar metal riveted part was micro-arc oxidized. The microscopic morphology, phase composition, electrochemical property and hardness of the oxidation film after micro-arc oxidation for different times were studied. The formation process of the oxidation film on the surface of magnesium alloy and aluminum alloy was comparatively analyzed during micro-arc oxidation. The results show that the connected part was integrally wrapped by the oxidation film after micro-arc oxidation for 10 min. The oxidation film connected with the two alloy substrates tightly and consisted of a compact layer and a loose layer. The oxidation film on the surface of magnesium alloy was composed of MgO and a small amount of silicates and fluoride. The oxidation film on the surface of aluminum alloy consisted of Al2O3 and a small amount of silicates. The micro-arc oxidation improved the corrosion potential of the magnesium alloy and aluminum alloy, reduced the corrosion potential difference between them and effectively alleviated the occurrence of galvanic corrosion.
中图分类号 TG174.453 DOI 10.11973/jxgccl201805004
所属栏目 试验研究
基金项目 国家重点研发计划项目（2017YFB0103904），山东省重点研发计划项目（2017CXGC0404）
收稿日期 2017/2/27
修改稿日期 2018/2/14
网络出版日期
作者单位点击查看
备注周吉学(1982-),男,山东潍坊人,副研究员,博士
引用该论文: ZHOU Jixue,CHEN Yanfei,SONG Xiaocun,LIU Hongtao,YANG Yuansheng. Preparation and Structure of Overall Micro-Arc Oxidation Film on AZ31B Magnesium Alloy/6061 Aluminum Alloy Dissimilar Metal Connected Part[J]. Materials for mechancial engineering, 2018, 42(5): 20～26
周吉学,陈燕飞,宋晓村,刘洪涛,杨院生. AZ31B镁合金/6061铝合金异质金属连接件整体微弧氧化膜的制备及其结构[J]. 机械工程材料, 2018, 42(5): 20～26
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】唐仕光, 陈泉志, 李少波, 等. 金属复合材料微弧氧化研究进展[J]. 表面技术, 2016, 45(11):23-31.
【2】WANG S, LIU P. The technology of preparing green coating by conducting micro-arc oxidation on AZ91D magnesium alloy[J]. Polish Journal of Chemical Technology, 2016, 18(4):36-40.
【3】张波, 方志刚, 李向阳, 等. 铝合金船舶的腐蚀防护技术现状与展望[J]. 中国材料进展, 2014(7):414-417.
【4】郭惠霞. 镁合金微弧氧化膜电化学腐蚀行为及机理研究[D]. 兰州:兰州理工大学, 2014.
【5】CUI X, YANG R, LIU C,et al. Structure and corrosion resistance of modified micro-arc oxidation coating on AZ31B magnesium alloy[J]. Transactions of Nonferrous Metals Society of China, 2016, 26(3):814-821.
【6】帅刚, 邱骥, 王红美, 等. 铝合金TIG焊接接头喷射式微弧氧化腐蚀疲劳性能研究[J]. 表面技术, 2015, 44(12):110-115.
【7】王绍明, 陈立庄, 赵勇. TA2钛合金与5083铝合金电偶腐蚀行为和连接工艺的研究[J]. 江苏科技大学学报(自然科学版), 2012, 26(2):133-136.
【8】帅刚, 马世宁, 邱骥, 等. 大型铝合金件焊接区微弧氧化技术研究进展[J]. 特种铸造及有色合金, 2015, 35(7):709-713.
【9】DONG K, SONG Y, SHAN D, et al. Corrosion behavior of a self-sealing pore micro-arc oxidation film on AM60 magnesium alloy[J]. Corrosion Science, 2015, 100:275-283.
【10】惠记庄. 不同电参数条件下铝-镁合金微弧氧化陶瓷研究[D]. 西安:长安大学, 2006.
【11】薛文斌, 陈廷芳, 李永良, 等. AZ31镁合金搅拌摩擦焊接头微弧氧化表面防护研究[J]. 材料工程, 2013(12):1-6.
【12】鲁亮, 薛文斌, 金小越, 等. 5083铝合金搅拌摩擦焊接头微弧氧化膜电化学腐蚀行为[J]. 稀有金属材料与工程, 2012,41(9):1597-1601.
【13】鲁亮, 薛文斌, 金小越, 等. 5083铝合金搅拌摩擦焊接头微弧氧化表面防护[J].材料热处理学报,2011,32(11):140-144.
【14】马颖, 李伟荣. 微弧氧化处理提高AZ31B镁合金搅拌摩擦焊焊缝的耐蚀性[J].兰州理工大学学报, 2012, 38(4):5-9.
【15】李伟荣. AZ31B镁合金搅拌摩擦焊焊缝微弧氧化处理的研究[D].兰州:兰州理工大学, 2012.
【16】刘靖. 微弧氧化对7075铝合金搅拌摩擦焊接头腐蚀行为影响[D].秦皇岛:燕山大学, 2010.
【17】TANG H, GAO Y. Preparation and characterization of hydroxyapatite containing coating on AZ31 magnesium alloy by micro-arc oxidation[J]. Journal of Alloys and Compounds, 2016, 688:699-708.
【18】YANG S, ZHOU L, CHENG X. Magnesium Technology 2016[M].[S.l.]:Springer International Publishing,2016:291-295.
【19】KRISHNA L R, POSHAL G, JYOTHIRMAYI A,et al. Relative hardness and corrosion behavior of micro arc oxidation coatings deposited on binary and ternary magnesium alloys[J]. Materials & Design, 2015, 77:6-14.
【20】FAZEL M, SALIMIJAZI H R, GOLOZAR M A. A comparison of corrosion, tribocorrosion and electrochemical impedance properties of pure Ti and Ti6Al4V alloy treated by micro-arc oxidation process[J]. Applied Surface Science, 2015, 324:751-756.
【21】DURDU S, USTA M. Characterization and mechanical properties of coatings on magnesium by micro arc oxidation[J]. Applied Surface Science, 2012, 261:774-782.
【22】蒋百灵, 张先锋, 朱静. 铝合金镁合金微弧氧化陶瓷层的形成机理及性能[J]. 西安理工大学学报, 2003, 19(4):297-302.
【23】蒋百灵, 张先锋. 镁合金微弧氧化陶瓷层的生长过程及其耐蚀性[J]. 中国腐蚀与防护学报, 2009, 25(2):97-101. 24] 于松楠. 5754铝镁合金微弧氧化膜的制备及其理化特性研究[D]. 长春:吉林大学, 2011.
【2】WANG S, LIU P. The technology of preparing green coating by conducting micro-arc oxidation on AZ91D magnesium alloy[J]. Polish Journal of Chemical Technology, 2016, 18(4):36-40.
【3】张波, 方志刚, 李向阳, 等. 铝合金船舶的腐蚀防护技术现状与展望[J]. 中国材料进展, 2014(7):414-417.
【4】郭惠霞. 镁合金微弧氧化膜电化学腐蚀行为及机理研究[D]. 兰州:兰州理工大学, 2014.
【5】CUI X, YANG R, LIU C,et al. Structure and corrosion resistance of modified micro-arc oxidation coating on AZ31B magnesium alloy[J]. Transactions of Nonferrous Metals Society of China, 2016, 26(3):814-821.
【6】帅刚, 邱骥, 王红美, 等. 铝合金TIG焊接接头喷射式微弧氧化腐蚀疲劳性能研究[J]. 表面技术, 2015, 44(12):110-115.
【7】王绍明, 陈立庄, 赵勇. TA2钛合金与5083铝合金电偶腐蚀行为和连接工艺的研究[J]. 江苏科技大学学报(自然科学版), 2012, 26(2):133-136.
【8】帅刚, 马世宁, 邱骥, 等. 大型铝合金件焊接区微弧氧化技术研究进展[J]. 特种铸造及有色合金, 2015, 35(7):709-713.
【9】DONG K, SONG Y, SHAN D, et al. Corrosion behavior of a self-sealing pore micro-arc oxidation film on AM60 magnesium alloy[J]. Corrosion Science, 2015, 100:275-283.
【10】惠记庄. 不同电参数条件下铝-镁合金微弧氧化陶瓷研究[D]. 西安:长安大学, 2006.
【11】薛文斌, 陈廷芳, 李永良, 等. AZ31镁合金搅拌摩擦焊接头微弧氧化表面防护研究[J]. 材料工程, 2013(12):1-6.
【12】鲁亮, 薛文斌, 金小越, 等. 5083铝合金搅拌摩擦焊接头微弧氧化膜电化学腐蚀行为[J]. 稀有金属材料与工程, 2012,41(9):1597-1601.
【13】鲁亮, 薛文斌, 金小越, 等. 5083铝合金搅拌摩擦焊接头微弧氧化表面防护[J].材料热处理学报,2011,32(11):140-144.
【14】马颖, 李伟荣. 微弧氧化处理提高AZ31B镁合金搅拌摩擦焊焊缝的耐蚀性[J].兰州理工大学学报, 2012, 38(4):5-9.
【15】李伟荣. AZ31B镁合金搅拌摩擦焊焊缝微弧氧化处理的研究[D].兰州:兰州理工大学, 2012.
【16】刘靖. 微弧氧化对7075铝合金搅拌摩擦焊接头腐蚀行为影响[D].秦皇岛:燕山大学, 2010.
【17】TANG H, GAO Y. Preparation and characterization of hydroxyapatite containing coating on AZ31 magnesium alloy by micro-arc oxidation[J]. Journal of Alloys and Compounds, 2016, 688:699-708.
【18】YANG S, ZHOU L, CHENG X. Magnesium Technology 2016[M].[S.l.]:Springer International Publishing,2016:291-295.
【19】KRISHNA L R, POSHAL G, JYOTHIRMAYI A,et al. Relative hardness and corrosion behavior of micro arc oxidation coatings deposited on binary and ternary magnesium alloys[J]. Materials & Design, 2015, 77:6-14.
【20】FAZEL M, SALIMIJAZI H R, GOLOZAR M A. A comparison of corrosion, tribocorrosion and electrochemical impedance properties of pure Ti and Ti6Al4V alloy treated by micro-arc oxidation process[J]. Applied Surface Science, 2015, 324:751-756.
【21】DURDU S, USTA M. Characterization and mechanical properties of coatings on magnesium by micro arc oxidation[J]. Applied Surface Science, 2012, 261:774-782.
【22】蒋百灵, 张先锋, 朱静. 铝合金镁合金微弧氧化陶瓷层的形成机理及性能[J]. 西安理工大学学报, 2003, 19(4):297-302.
【23】蒋百灵, 张先锋. 镁合金微弧氧化陶瓷层的生长过程及其耐蚀性[J]. 中国腐蚀与防护学报, 2009, 25(2):97-101. 24] 于松楠. 5754铝镁合金微弧氧化膜的制备及其理化特性研究[D]. 长春:吉林大学, 2011.
相关信息